HG/T 3660-1999 (HG/T3660-1999)

Standard IDContents [version]USDSTEP2[PDF] delivered inName of Chinese StandardStatus
HG/T 3660-1999English70 Add to Cart 0-9 seconds. Auto-delivery. Testing methods for melt viscosity of hot-melt adhesives  

Standards related to: HG/T 3660-1999

HG/T 3660-1999: PDF in English (HGT 3660-1999)

HG/T 3660-1999
Record Number. 3885-1999
Chemical Industry Standard
of the People’s Republic of China
Testing Methods for Melt Viscosity of
Hot-melt Adhesives
ISSUED ON. JUNE 16, 1999
Issued by. State Oil and Chemical Industry Authority
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Normative references ... 4
3 Principle ... 4
4 Instruments ... 5
5 Sample state adjustment, temperature and humidity of test laboratary... 5
6 Operational steps ... 5
7 Calculation ... 7
8 Test Report ... 8
This standard is formulated by equivalently adopting Japanese Industrial
Standard JIS K 6862-1984 Testing Methods for Melt Viscosity of Hot-melt
Compared with JIS K 6862, main differences of this standard are.
- The viscosity meter used in the method B of this standard is not the same
This standard was proposed by Technical Inspection Division of former Ministry
of Chemical Industry, the People's Republic of China.
This standard shall be administered by the National Adhesive Standardization
Technical Committee.
Drafting organization of this standard. Shanghai Institute of Rubber Products.
Main drafters of this standard. Lu Zhiyun, and Xin Renfen.
This standard shall be responsibly interpreted by National Adhesive
Standardization Technical Committee.
Testing Methods for Melt Viscosity of
Hot-melt Adhesives
1 Scope
This standard specifies the melt viscosity test for hot-melt adhesive at 180ºC.
It may also negotiate to use other test temperature according to needs.
According to different sample amount, this standard uses Brooke (Brookfield)
type single cylinder rotary viscometer and sleeve rotary viscometer
respectively to determine the melt viscosity of hot-melt adhesive.
The maximum melt viscosity measured by this standard is 200 Pa • s.
2 Normative references
The following standards contain provisions which, through reference in this
Standard, constitute provisions of this Standard. At time of publication, the
editions indicated are valid. All standards are subject to revision. The parties
who are using this Standard shall explore the possibility of using the latest
version of the following standards.
GB/T 2918-98 Plastics - Standard atmospheres for conditioning and testing
3 Principle
The viscosity measured by rotational viscometer is the dynamic viscosity. The
molten hot-melt adhesive is non-Newtonian fluid. The ratio of any shear rate
AND corresponding shear stress is not constant.
The specific amount of hot-melt adhesive is heated under the given
conditions. When the temperature of hot-melt adhesive reaches the test
temperature, SELECT suitable viscometer’s rotor and speed. START
viscometer. RECORD the viscosity value.
1) When sample amount is 200mL, it is not suitable to use rotor A-1.
8 Test Report
The test report shall include the following content.
a) Sample source, name, type, date of manufacture or batch number, date of
b) Temperature, humidity and time of sample state adjustment;
c) Test method (Method A, Method B);
d) Viscometer’s model, rotor, rotation speed, and rotation time;
e) The test results (viscosity and test temperature);
f) Other content required to report.
(Above excerpt was released on 2014-08-15, modified on 2021-06-07, translated/reviewed by: Wayne Zheng et al.)