GB/T 11206-2009: Standard test method for rubber deterioration -- Surface cracking
Status: Valid GB/T 11206: Evolution and historical versions
| Standard ID | Contents [version] | USD | STEP2 | [PDF] delivered in | Standard Title (Description) | Status | PDF |
| GB/T 11206-2009 | English | 369 |
Add to Cart
|
3 days [Need to translate]
|
Standard test method for rubber deterioration -- Surface cracking
| Valid |
GB/T 11206-2009
|
| GB/T 11206-1989 | English | 439 |
Add to Cart
|
4 days [Need to translate]
|
Rubber vulcanized--The test method of deterioration surface cracking
| Obsolete |
GB/T 11206-1989
|
PDF similar to GB/T 11206-2009
Basic data | Standard ID | GB/T 11206-2009 (GB/T11206-2009) | | Description (Translated English) | Standard test method for rubber deterioration -- Surface cracking | | Sector / Industry | National Standard (Recommended) | | Classification of Chinese Standard | G40 | | Classification of International Standard | 83.060 | | Word Count Estimation | 16,195 | | Date of Issue | 2009-04-24 | | Date of Implementation | 2009-12-01 | | Older Standard (superseded by this standard) | GB/T 11206-1989 | | Adopted Standard | ASTM D518-1999, MOD | | Regulation (derived from) | National Standard Approval Announcement 2009 No.6 (Total No.146) | | Issuing agency(ies) | General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China, Standardization Administration of the People's Republic of China | | Summary | This standard specifies test methods and evaluation methods of surface cracking occurs when static strain aging in the state of rubber samples. This standard applies to rubber placed under atmospheric or medium containing ozone aging test conducted in static stretching or bending state. This standard does not apply to the discharge exposed to high concentrations of ozone to produce an electrically insulating material environment or rubber parts, does not apply to hard rubber. | GB/T 11206-2009: Standard test method for rubber deterioration -- Surface cracking---This is a DRAFT version for illustration, not a final translation. Full copy of true-PDF in English version (including equations, symbols, images, flow-chart, tables, and figures etc.) will be manually/carefully translated upon your order.
Standard test method for rubber deterioration. Surface cracking
ICS 83.060
G40
National Standards of People's Republic of China
Replacing GB/T 11206-1989
Rubber aging test surface cracking method
Posted 2009-04-24
2009-12-01 implementation
Administration of Quality Supervision, Inspection and Quarantine of People's Republic of China
Standardization Administration of China released
Foreword
This revised standard adopts ASTMD518.1999 "Test Methods for Rubber surface cracking aging."
This standard is based on ASTMD518.1999 "Standard Test Method for Rubber Deterioration surface cracking" redrafted. For comparison, in Appendix A
The standard lists the reg number and ASTMD518.1999 reg control list numbered.
This standard replaces GB/T 11206-1989 "Standard Test Method for vulcanized rubber surface cracking aging."
This standard ASTMD518.1999 technical differences and the reasons are as follows.
--- Remove ASTMD518.1999 1.2, as are the use of legal units of measurement in the national standards;
--- With GB/T 7762 instead of ASTMD1149, since GB/T 7762 main technical content and ASTMD1149 phase
With no technical difference (Chapter 2 of this standard, 7.2,11.3,15.5.1 and 20.4);
--- Increase in GB/T 528, as shall be prepared dumbbell GB/T 528's provisions (Chapter 2 of this standard, the first
Chapter 18);
--- Increase in stretching the rectangular specimen type 2 specimens, dimensions of length 100mm, width (10 ± 0.3) mm, thickness (1.0 ± 0.1) mm
Or (2.0 ± 0.2) mm. The advantages of using this sample size is that the sample belongs to the main narrow shaped specimens, small cross-section, the internal stress
Small, easy to draw the corresponding elongation and installed in the sample holder, elongation and high precision (6.1 and 7.1 of this standard);
--- Increase its effective work dumbbell tensile test method, because the dumbbell is susceptible to various elongation tensile deformation test,
As part of a uniform stress distribution under tension, the distribution of crack crack occurred after aging surface more uniform, fracture fracture surface also
The effective work area, easy to detect and observe; dumbbell tensile properties of the sample can also be conducive to the rubber-like
Products made comprehensive evaluation (this standard Chapter 17 ~ Chapter 20);
--- Thickness of the specimen was changed from 1.9mm ~ 2.5mm (2.0 ± 0.2) mm, as in the domestic rubber samples general press (2.0 ±
0.2) mm prepared sample (this standard 6.1,10.1 and 14.1);
--- Increase detailed testing and evaluation methods, help assess test results (this standard Chapter 21 ~ Chapter 22);
--- Increase the informative Appendix B "sample cracks rating Photo", to facilitate the detection of reference rating.
This standard compared with GB/T 11206-1989 main changes are as follows.
--- Increasing the normative references ASTMD4575 (see Chapter 2);
--- Tensile test specimens with cone method instead of a triangular strip specimens bending method (1989 edition, Chapter 8; edition Chapter 13 through 16);
--- Rectangular tensile test specimens law that increase sample sizes from one of two (see 6.1);
--- Increasing the precision and bias section (see Chapter 23).
The Standard Appendix A, Appendix B are informative appendices.
The standard proposed by China Petroleum and Chemical Industry Association.
This standard by the national Common test methods for rubber and rubber goods Technical Committee of Standardization Technical Committee (SAC/TC35/SC2)
Centralized.
This standard was drafted. Guangzhou Institute of Materials Co., Ltd., Beijing Rubber Industry Research and Design Institute, Dongguan City, New Materials belite
Limited.
The main drafters of this standard. Xie Yufang, Xie Junfang, mine gold, Yang Yunong, Sushi Qiong, ZHANG Shu-dong.
This standard replaces the standards previously issued as follows.
--- GB/T 11206-1989.
Rubber aging test surface cracking method
Warning --- personnel should use this standard regular laboratory work experience. This standard does not point out all possible security asked
Questions, the user has the responsibility to take appropriate safety and health practices and to ensure compliance with the conditions relevant national regulations.
1 Scope
This standard specifies the test methods and evaluation methods of surface cracks occur in the static strain aging state rubber samples.
This standard applies to rubber placed under the atmosphere or ozone-containing medium in the aging test under static tensile or bending state.
This standard does not apply to exposure at the discharge generated by the high concentration of ozone environment of an electrically insulating material or rubber parts; not suitable
In hard rubber.
2 Normative references
The following documents contain provisions which, through reference in this standard and become the standard terms of dated references, all subsequent
Amendments (not including errata content) or revisions do not apply to this standard. However, according to the study encourages the parties to the agreement
Whether the latest versions of these documents. For undated reference documents, the latest versions apply to this standard.
GB/T 528 vulcanized rubber or thermoplastic rubber tensile stress strain properties (GB/T 528-1998, eqvISO 37.
1994)
GB/T 7762 vulcanized rubber or thermoplastic rubber resistant to ozone cracking static tensile test (GB/T 7762-2003, ISO 1431-1.
1989, MOD)
Test methods for determining the concentration of ozone test chamber ASTMD4575 rubber aging test reference and optional
3 Test Method
3.1 according to the actual state of rubber or rubber, you can select the following test methods.
a) rectangular sample drawing method;
b) rectangular specimens bending test method;
c) the sample cone drawing method;
d) dumbbell specimen stretching method.
3.2 rubber samples under static tensile or bending is fixed in the sample holder exposed to ambient atmosphere or an ozone-containing medium, after a certain
After continuous exposure time by observing the changes in appearance and surface cracking the case of the sample was evaluated.
3.3 Determination of the concentration of ozone is carried out according to the provisions ASTMD4575.
4 Test principle and application
4.1 rubber samples in a static state stretched or bent or placed under an atmosphere containing ozone aging test medium, its surface will be made
On the role that factors such as ozone cracking. This is essentially the direction of the crack and the direction of the sample by the stress perpendicular to each other. Observation test
Like surface cracking changes can be relatively resistant to evaluate the degree of aging of rubber.
4.2 As the relationship between the test results and determined the life and duplicate samples at different venues is not necessarily reproducible results
Sex, so this standard does not apply to the procurement of technical documents. There is no clear correlation between laboratory test results and the actual usage
Relations, this standard is mainly used for resistance to two or more rubber material aging cracking performance comparison.
5 A method --- rectangular specimens stretching device
5.1 sample holder plate
Rectangular sample plates fixed to the static tensile specimens. Sample plate width 1 type specimen is 140mm, a length of about 380mm, thickness
Tips & Frequently Asked Questions:Question 1: How long will the true-PDF of GB/T 11206-2009_English be delivered?Answer: Upon your order, we will start to translate GB/T 11206-2009_English as soon as possible, and keep you informed of the progress. The lead time is typically 1 ~ 3 working days. The lengthier the document the longer the lead time. Question 2: Can I share the purchased PDF of GB/T 11206-2009_English with my colleagues?Answer: Yes. The purchased PDF of GB/T 11206-2009_English will be deemed to be sold to your employer/organization who actually pays for it, including your colleagues and your employer's intranet. Question 3: Does the price include tax/VAT?Answer: Yes. Our tax invoice, downloaded/delivered in 9 seconds, includes all tax/VAT and complies with 100+ countries' tax regulations (tax exempted in 100+ countries) -- See Avoidance of Double Taxation Agreements (DTAs): List of DTAs signed between Singapore and 100+ countriesQuestion 4: Do you accept my currency other than USD?Answer: Yes. If you need your currency to be printed on the invoice, please write an email to [email protected]. In 2 working-hours, we will create a special link for you to pay in any currencies. Otherwise, follow the normal steps: Add to Cart -- Checkout -- Select your currency to pay. Question 5: Should I purchase the latest version GB/T 11206-2009?Answer: Yes. Unless special scenarios such as technical constraints or academic study, you should always prioritize to purchase the latest version GB/T 11206-2009 even if the enforcement date is in future. Complying with the latest version means that, by default, it also complies with all the earlier versions, technically.
|