Add to Cart
|
5 days [Need to translate]
|
Test methods for properties of resin casting body
| Valid |
GB/T 2567-2021
|
| GB/T 2567-2008 | English | 150 |
Add to Cart
|
0--9 seconds. Auto-delivery
|
Test methods for properties of resin casting body
| Obsolete |
GB/T 2567-2008
|
| GB/T 2567-1995 | English | 199 |
Add to Cart
|
2 days [Need to translate]
|
The generals of test methods for properties of resin casting body
| Obsolete |
GB/T 2567-1995
|
| GB 2567-1981 | English | 199 |
Add to Cart
|
2 days [Need to translate]
|
Resin-casting objects--Mechanical properties tests--General rules
| Obsolete |
GB 2567-1981
|
| Standard ID | GB/T 2567-2021 (GB/T2567-2021) | | Description (Translated English) | | | Sector / Industry | National Standard (Recommended) |
GB/T 2567-2021
Test methods for properties of resin casting body
ICS 83.120
CCSQ23
National Standards of People's Republic of China
Replace GB/T 2567-2008
Test method for performance of resin casting body
Released on 2021-08-20
2022-03-01 implementation
State Administration of Market Supervision and Administration
Issued by the National Standardization Management Committee
Preface
This document is in accordance with the provisions of GB/T 1.1-2020 "Guidelines for Standardization Work Part 1.Structure and Drafting Rules of Standardization Documents"
Drafting.
This document replaces GB/T 2567-2008 "Resin casting body performance test method", compared with GB/T 2567-2008, except for structural adjustment
In addition to the overall and editorial changes, the main technical changes are as follows.
a) The sample processing method is changed, and the one-time forming method is recommended (see 5.1.4.1, 4.1.4.1 of the.2008 edition);
b) The appearance requirements for processed samples have been added (see 5.1.4.5);
c) The regulations on internal stress inspection of resin casting bodies have been deleted (see 4.1.5 of the.2008 edition);
d) The regulations on periodic verification of testing machines have been deleted (see 4.5.4 of the.2008 edition);
e) The length of the tensile specimen is changed from ≥200mm to.200mm~220mm (see 6.1.2.1, 5.1.2 of the.2008 edition);
f) The requirements for grading loading of tensile properties (see 5.1.4.6 in the.2008 edition) and the requirements for grading loading of compression properties (see the.2008 edition) have been deleted.
5.2.4.6), grading loading regulations for bending performance (see 5.3.4.6 of the.2008 edition);
g) A calculation method for measuring the tensile modulus of elasticity using an automatic recording device has been added (see 6.1.6.3);
h) A calculation method for measuring the compressive elastic modulus using an automatic recording device has been added (see 6.2.6.3);
i) A calculation method for measuring the bending elastic modulus and bending strain using an automatic recording device has been added (see 6.3.6.3);
j) The placement of unnotched specimens for the impact toughness test of simply supported beams has been added (see 6.4.3.2);
k) The sensitivity requirement of the balance has been changed from 0.0002g to 0.0001g (see 6.6.4.1, 5.6.4.1 of the.2008 edition);
l) The equipment requirements of constant temperature bath for alkali resistance test have been added (see 6.6.4.4);
m) The procedure of the alkali resistance test is changed (see 6.6.6.1, 5.6.6.1 of the.2008 edition);
n) The test report has added information on the sample processing method [see Chapter 8 b)] and the results of the bending performance [see Chapter 8 f)].
This document was proposed by the China Building Materials Federation.
This document is under the jurisdiction of the National Fiber Reinforced Plastics Standardization Technical Committee (SAC/TC39).
This document was drafted by. Changzhou Tianma Group Co., Ltd. (formerly Building Materials 253 Plant), Beijing FRP Research and Design Institute Co., Ltd.,
Shanghai FRP Research Institute Co., Ltd., the 53rd Research Institute of China North Industries Group.
The main drafters of this document. Xuan Weidong, Zhang Haiyan, Zhang Xiaoping, Wang Xuerong.
The previous versions of this document and the documents replaced are as follows.
---First published in 1981 as GB 2567-1981, first revised in.1995;
--- In the second revision in.2008, GB/T 2568-1995 "Test Method for Tensile Properties of Resin Casting Body" was incorporated
(Previous versions of GB/T 2568-1995 are issued. GB 2568-1981), GB/T 2569-1995 "Resin Casting
Body Compression Performance Test Method" (the previous version of GB/T 2569-1995 is issued. GB 2569-1981),
GB/T 2570-1995 "Test Method for Bending Performance of Resin Casting Body" (Previous versions of GB/T 2570-1995 released
For. GB 2570-1981), GB/T 2571-1995 "Test Method for Impact Performance of Resin Casting Body" (GB/T 2571-1995
The previous releases of the version are. GB 2571-1981), GB 4726-1984 "Resin casting body torsion test method" content
And GB 7194-1987 "Determination of Alkali Resistance of Unsaturated Polyester Resin Casting Body" and GB 8238-1987 "Unsaturated
Determination of Refractive Index of Polyester Resin Liquid and Casting Body Part of Casting Body;
---This is the third revision.
Test method for performance of resin casting body
1 Scope
This document specifies the test standard environment, samples, tests, test results and test reports for determining the performance of resin castings.
This document is suitable for determining the tensile properties, compression properties, bending properties, impact toughness, torsion, and resistance of thermosetting resin castings.
Alkalinity and refractive index.
2 Normative references
The contents of the following documents constitute the indispensable clauses of this document through normative references in the text. Among them, dated quotations
Only the version corresponding to that date is applicable to this document; for undated reference documents, the latest version (including all amendments) is applicable to
This document.
The estimated confidence interval of the average value of the statistical interpretation of ISO 2602 test results (Statistical interpretation of test
results-Estimationofthemean-Confidenceinterval)
3 Terms and definitions
There are no terms and definitions that need to be defined in this document.
4 Test standard environment
Ambient temperature. (23±2)℃, relative humidity (50±10)%.
5 Sample
5.1 Sample preparation
5.1.1 Mould
5.1.1.1 Plate casting mold
5.1.1.1.1 Materials
The materials should meet the following requirements.
a) The template is a flat and smooth glass plate or steel plate, and its size is determined by the required sample area plus the area of the mold frame.
b) Release agent or release film.
c) U-shaped mold frame, consistent with the size of the template.
d) The thickness of the gasket is controlled according to the thickness of the cast plate.
e) Bow clip.
5.1.1.1.2 Mold making
Clamp the U-shaped mold frame between two pre-coated mold release agents or cover the mold release film. The U-shaped opening is the casting port, U-shaped
......
GB/T 2567-2008
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 83.120
Q 23
Replacing GB/T 2567~2571-1995, GB/T 4726-1984, GB/T 7194-1987
Partially replacing GB/T 8238-1987
Test methods for properties of resin casting body
ISSUED ON: JUNE 30, 2008
IMPLEMENTED ON: APRIL 01, 2009
Issued by: General Administration of Quality Supervision, Inspection and
Quarantine;
Standardization Administration of the People's Republic of
China.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative references ... 5
3 Standard environment for testing ... 5
4 Specimen ... 5
5 Tests... 8
6 Test results ... 29
7 Test report ... 30
Annex A (Normative) Drawing method ... 31
Test methods for properties of resin casting body
1 Scope
This Standard specifies the test standard environment, specimen, test method,
test result and test report for properties of resin casting body.
This Standard is applicable to testing the tensile, compression, bending, simply-
supported beam impact toughness, torsion, alkali resistance and refractive
index of thermosetting resin castings for fiber reinforced plastics, castings of
special casting resins.
2 Normative references
The provisions in following documents become the provisions of this Standard
through reference in this Standard. For dated references, the subsequent
amendments (excluding corrigendum) or revisions do not apply to this Standard,
however, parties who reach an agreement based on this Standard are
encouraged to study if the latest versions of these documents are applicable.
For undated references, the latest edition of the referenced document applies.
ISO 2602, Statistical interpretation of test results - Estimation of the mean -
Confidence interval
3 Standard environment for testing
Ambient temperature: (23±2)°C, relative humidity (50±5)%.
4 Specimen
4.1 Specimen preparation
4.1.1 Mold
4.1.1.1 Flat casting mold
4.1.1.1.1 Materials
a) The template is a flat and smooth glass plate or steel plate. Its size is
determined according to the required specimen area plus the area of the
mold frame;
4.1.4 Specimen processing
4.1.4.1 Use a scribing tool on the casting plate. Mark the processing line
according to the specimen size. Sampling must avoid bubbles, cracks, pits,
stress concentration areas.
4.1.4.2 Machine the specimen. During processing, the surface of the specimen
shall be prevented from damage and defects such as scratches.
4.1.4.3 The rough surface needs to be finely ground with a fine file or sandpaper.
The size of the notch is detected with a special template.
4.1.4.4 Water can be used to cool during processing. Dry in time after
processing.
4.1.5 Internal stress examination
Before the casting body is tested, use polarized light to test the internal stress.
If there is internal stress, remove it.
4.1.6 Internal stress relief method
4.1.6.1 Oil bathing method
Place the specimen steadily in a container filled with oil. Immerse the entire
specimen in the oil. Place the container immersed in the specimen in the oven.
The temperature in the box is raised from room temperature to the glass
transition temperature of resin within 1 h. Turn off the power after 3 h of constant
temperature. After the oven is naturally cooled to room temperature, take the
specimen out from the oil bath. Carry out the internal stress observation.
NOTE: The oil used in the oil bath shall not have chemical effects on the specimen, and
shall not swell, dissolve, or absorb.
4.1.6.2 Air bathing method
Place the specimen in a drying oven with an air blower. The treatment
temperature and time are the same as in the oil bath.
4.2 Specimen visual inspection and quantity
4.2.1 Before the test, the specimen must be strictly inspected. The specimen
shall be flat, smooth, free of bubbles, cracks, obvious impurities and processing
damage and other defects.
4.2.2 Each group shall have at least 5 valid specimens.
4.3 Specimen state adjustment
4.3.1 Before the test, the specimen shall be placed under the test standard
environmental conditions for at least 24 h. The specimen after state adjustment
shall be tested under the same test standard environmental conditions as the
state adjustment (if otherwise specified, according to relevant regulations).
4.3.2 If the laboratory standard environmental conditions are not available, the
specimens can be placed in a desiccator before the test for at least 24 h.
4.4 Specimen measurement accuracy
4.4.1 The measurement of the working area of the specimen is accurate to
0.01mm.
4.4.2 The measurement accuracy of other values of the specimen shall be in
accordance with the provisions of the corresponding test method.
4.5 Test equipment
4.5.1 The load error of the test equipment does not exceed ±1%. The selection
of the test equipment range shall make the failure load of the specimen within
the range of 10% to 90% of the full scale (as far as possible to fall on one side
of the full scale) and not less than 4% of the full scale of the test equipment
(electronic tensile test equipment is according to relevant regulations).
4.5.2 The error of the measuring deformation instrument shall not exceed ±1%.
4.5.3 The test equipment can obtain the constant test speed specified in the
test method standard. The speed error does not exceed 1%.
4.5.4 The test equipment shall be regularly verified by the national metrology
department and used within the valid verification period.
5 Tests
5.1 Tensile test
5.1.1 Test principle
Apply a static tensile load at a constant speed along the axial direction of the
specimen until the specimen breaks or reaches a predetermined elongation.
Throughout the process, measure the load applied to the specimen and the
elongation of the specimen, so as to determine tensile stress (tensile yield
stress, tensile stress at break or tensile strength), tensile modulus of elasticity,
elongation at break rate and plot the stress-strain curve.
5.1.2 Specimen
5.2.4.1 Specimen preparation is according to the provisions of 4.1.
5.2.4.2 The visual inspection of the specimen shall be carried out in accordance
with the provisions of 4.2.
5.2.4.3 The state of the specimen is adjusted according to the provisions of 4.3.
5.2.4.4 Number the specimens. Measure the width and thickness of the
specimen at any 3 places (the diameter of the type II sample is measured at
any 3 places). Take the arithmetic mean. The measurement accuracy shall be
as specified in 4.4.
5.2.4.5 Place the specimen. Align the center line of the specimen with the center
line of the upper and lower platens. Make sure the end face of the specimen is
parallel to the surface of the platen. Adjust the testing machine. Make the
surface of the platen just contact the end face of the specimen. Apply the initial
load (about 5% of the failure load) to the specimen to avoid the initial region of
the stress-strain curve. Check and adjust specimen and deformation
measurement system. Keep the whole system in normal working condition.
5.2.4.6 When measuring the compressive elastic modulus, install a deformation
measuring instrument between the upper and lower pressing plates and the
contact surface of the specimen or in the middle of the height of the specimen.
Check the meter. Start the testing machine. Load in levels at a specified speed.
The level difference is 5% to 10% of the failure load. Load at least five levels.
The applied load shall not exceed 50% of the failure load. Usually, the
measurement is repeated at least 3 times. Take the stable deformation
increments of 2 times. Record all levels of loads and corresponding deformation
values. When there is an automatic recording device, it can be loaded
continuously.
5.2.4.7 When measuring the compressive strength, apply a uniform continuous
load to the specimen at the specified speed until the failure load or the
maximum load. Read the failure load or maximum load.
5.2.4.8 Specimens with instability and end extrusion damage shall be discarded.
When there are less than 5 valid specimens in the same batch, the test shall
be redone.
5.2.5 Calculation
5.2.5.1 The compressive strength is calculated according to formula (4) or
formula (5):
3 - Specimen.
Figure 4 -- Schematic diagram of the three-point bending test device
5.3.3.1 The standard environment of the test shall be as specified in 3.
5.3.3.2 The test equipment shall be in accordance with the provisions of 4.5.
5.3.3.3 The schematic diagram of the three-point test equipment is shown in
Figure 4. The span L is (16±1) h. The radius R of the loading upper indenter is
(5.0±0.1) mm. When the thickness of the specimen is greater than 3mm, r is
(5.0±0.2)mm.
5.3.3.4 When testing the bending strength, the test speed is 10mm/min. The
test speed is 2mm/min when measuring the flexural modulus of elasticity. The
arbitration inspection speed is 2mm/min.
5.3.4 Test steps
5.3.4.1 Specimen preparation is according to the provisions of 4.1.
5.3.4.2 The visual inspection of the specimen shall be carried out in accordance
with the provisions of 4.2.
5.3.4.3 The state of the specimen is adjusted according to the provisions of 4.3.
5.3.4.4 Number the conforming specimens. Measure the width and thickness
of the specimen at 3 points near the center of the span. Take the arithmetic
mean. The measurement accuracy shall be as specified in 4.4.
5.3.4.5 Adjust the span L and the position of the loading indenter, accurate to
0.5mm. The upper loading indenter is located in the middle of the support and
parallel to the support.
5.3.4.6 Place the specimen in the middle of the support. The length direction of
the sample is perpendicular to the support and the upper indenter.
5.3.4.7 Adjust loading speed. Select the load range of the testing machine and
the range of the deformation instrument. Adjust the testing machine so that the
loading upper indenter is just in contact with the specimen. Apply the initial load
(approximately 5% of the failure load) to the specimen to avoid the initial region
of the stress-strain curve. Check and adjust the instrument to make the whole
system in normal state.
5.3.4.8 When measuring the bending strength or bending stress, load uniformly
and continuously at the specified speed until failure. Record the failure load or
maximum load value. For materials that do not exhibit failure at deflection equal
to 1.5 times the thickness of the specimen, record the load at this deflection.
4.4.
5.4.4.5 Select the pendulum according to the energy required to break the
specimen. Make the energy consumed within the range of 10%~85% of the
energy of the pendulum.
5.4.4.6 Use the standard span template to adjust the distance of the support.
5.4.4.7 According to the position of the hitting center of the testing machine and
the size of the specimen, it is decided whether to add a gasket on the support.
The size of the gasket shall be determined according to the conditions of the
testing machine.
5.4.4.8 Check the energy consumed by the testing machine no-load before the
test. Make the pointer point to zero after no-load impact.
5.4.4.9 Raise and lock the pendulum. Hold the entire width of the specimen
against the support. Align the impact center with the back of the specimen
center or notch center. Make smooth release of the pendulum. Read the work
consumed by breaking the specimen and the form of failure from the dial.
5.4.4.10 Specimens broken at non-notched places shall be discarded. Take
another specimen to supplement. For non-notched specimens, calculate as a
fracture. If the specimen is not broken, the value shall not be taken. When there
are less than 5 valid specimens in the same batch, the test shall be redone.
5.4.5 Calculation
The impact strength is calculated according to formula (11):
Where,
σK - Impact strength, in kilojoules per square meter (kJ/m2);
A - Work consumed by breaking the specimen, in Joules (J);
b - Width under the notch of the specimen or the width in the middle of the
unnotched specimen, in millimeters (mm);
d - Thickness under the notch of the specimen or the thickness in the middle of
the unnotched specimen, in millimeters (mm).
5.5 Torsion test
G - Shear modulus of elasticity, in megapascals (MPa);
Δτ - Stress increment on straight segment of shear stress-strain curve, in
megapascals (MPa);
Δr - Equivalent strain increment.
5.6 Alkali resistance test
5.6.1 Test principle
When the thermosetting resin casting body is soaked in the alkaline solution, it
will swell from the surface to the inside, crack and even break. The alkali
resistance of the specimens can be compared by measuring the changes in
appearance, physical or mechanical properties of the samples before and after
the test.
5.6.2 Specimen
5.6.2.1 Specimen preparation is carried out according to 4.1.
5.6.2.2 The surface size of the sample is 80mm × 15mm. The thickness is (3-
6) mm.
5.6.2.3 The visual inspection and quantity of the specimen shall be carried out
according to 4.2.
5.6.3 Reagents
5.6.3.1 Distilled or deionized water.
5.6.3.2 Sodium hydroxide: chemically pure.
5.6.4 Instruments and equipment
5.6.4.1 Analytical balance: resolution is 0.0002g.
5.6.4.2 Round bottom flask: 1000mL.
5.6.4.3 Reflux condenser.
5.6.5 Test conditions
5.6.5.1 Test medium: 10% sodium hydroxide solution; other concentrations can
also be prepared as required.
5.6.5.2 Test temperature: boiling temperature or as required.
5.6.5.3 Test period age: the period age of the boiling test is 10h, 50h, 100h or
selected as required.
5.6.6 Test steps
5.6.6.1 Put 500mL of sodium hydroxide solution and a small amount of zeolite
into the heating reflux device. Boil or maintain the desired temperature.
5.6.6.2 Put the prepared set of specimens into the flask. Keep the solution in
the bottle at a slight boil or at the desired temperature. Simultaneously record
the time.
5.6.6.3 Take out the specimens by the age of period. After cooling, use clean
water to rinse. Use gauze or filter paper to drain the surface moisture. Observe
the appearance and record.
5.6.6.4 Place the specimen in a drying oven at 100°C for 2 h. Take out. Observe
and record.
5.6.6.5 Other physical or mechanical properties of the samples before and after
the test can be determined as required.
5.6.7 Calculation
5.6.7.1 The alkali resistance of the sample is judged from the appearance of
cracks, changes in gloss, cracks, stickiness and other abnormalities.
5.6.7.2 The rate of change and retention of physical or mechanical properties
of the specimen.
5.6.7.2.1 The change rate Φ (%) of the physical or mechanical properties of the
specimen can be calculated according to formula (16):
Where,
M1 - Determined value of physical or mechanical properties before the test;
M2 - Determined value of physical or mechanical properties after the test.
5.6.7.2.2 The retention rate Ψ (%) of the physical or mechanical properties of
the specimen can be calculated according to formula (17):
5.7.2.2 White light source.
5.7.2.3 Thermostat, accurate to ±0.2°C.
5.7.2.4 Contact solution, α-bromonaphthalene.
5.7.3 Specimen
5.7.3.1 Specimen preparation is carried out according to 4.1.
5.7.3.2 The specimen size is 12mm × 6mm × 3mm.
5.7.3.3 For maximum accuracy, the surface of the specimen in contact with the
prism shall be perfectly flat and well-polished. A clear straight line appeared
through the dividing line between the light and dark halves of the eyepiece field
of view, indicates that the specimen and the prism were in good contact.
Prepare another well-polished surface, perpendicular to the first polished
surface and at one end of the specimen. The two polished surfaces shall meet
in a clear straight line rather than an oblique or arc.
5.7.4 Test steps
5.7.4.1 Calibrate the instrument. When using an Abbe refractometer, it can be
corrected with a calibration block. It can also use the secondary distilled water
to calibrate. The refractive index of water at 20 °C is 1.3330. It is 1.3320 at 30°C.
The temperature coefficient is -0.0001/°C.
5.7.4.2 Method for determination of transparent solids: No reflector and light
entrance prism are used in the measurement. Glue the solid-polished surface
to the refractive prism with α-bromonaphthalene. Make it in close contact with
the prism surface. No bubbles appear. The other polished surface faces the
light source. Turn the reading handwheel. Intersect the light-dark dividing line
in the field of view with the intersection of the crosshairs. Simultaneously rotate
the Amish prism handwheel. Eliminate foreign colors. The reading of the scale
is the refractive index of the casting. The maximum difference between readings
shall not be greater than 0.001. Take the average value as the determination
result.
5.7.4.3 Method for determination of translucent solids: When measuring, the
solid shall have a polished surface. Stick the solid polished surface on the
refractive prism with α-bromonaphthalene. Remove the protective cover as the
light entry surface. Use reflected light to measure. The specific operation steps
are the same as 5.7.4.2.
......
|