HOME   Cart(0)   Quotation   About-Us Tax PDFs Standard-List Powered by Google www.ChineseStandard.net Database: 189759 (2 Feb 2025)

GB/T 31935-2015 PDF English


Search result: GB/T 31935-2015 English: PDF (GB/T31935-2015)
Standard IDContents [version]USDSTEP2[PDF] delivered inName of Chinese StandardStatus
GB/T 31935-2015English115 Add to Cart 0-9 seconds. Auto-delivery. Corrosion of metals and alloys -- Corrosion test for intergranular corrosion susceptibility of low-Cr ferritic stainless steels Valid
BUY with any currencies (Euro, JPY, GBP, KRW etc.): GB/T 31935-2015     Related standards: GB/T 31935-2015

PDF Preview: GB/T 31935-2015


GB/T 31935-2015: PDF in English (GBT 31935-2015)

GB/T 31935-2015 GB NATIONAL STANDARD OF THE PEOPLE’S REPUBLIC OF CHINA ICS 77.060 H 25 Corrosion of Metals and Alloys – Corrosion Test for Intergranular Corrosion Susceptibility of Low-Cr Ferritic Stainless Steel ISSUED ON. SEPTEMBER 11, 2015 IMPLEMENTED ON. JUNE 1, 2016 Issued by. General Administration of Quality Supervision, Inspection and Quarantine; Standardization Administration of PRC. Table of Contents Foreword ... 3 1 Scope ... 4 2 Normative References ... 4 3 Specimen ... 4 4 Test Instrument and Test Equipment ... 9 5 Test Solution ... 9 6 Test Conditions and Procedures ... 9 7 Assessment of Test Results ... 10 8 Test Report ... 10 Foreword This Standard was drafted as per the rules specified in GB/T 1.1-2009. This Standard was proposed by China Iron and Steel Association. This Standard shall be under the jurisdiction of National Technical Committee for Standardization of Steel (SAC/TC 183). Chief Drafting organizations of this Standard. Baosteel Stainless Steel Co., Ltd., China Metallurgical Information and Standardization Institute, and National Ship Materials Quality Supervisions and Inspection Center. Chief drafting staffs of this Standard. Jiang Laizhu, Luo Suzhen, Hou Jie, Feng Chao, Luo Ming, and Feng Xiumei. Corrosion of Metals and Alloys – Corrosion Test for Intergranular Corrosion Susceptibility of Low-Cr Ferritic Stainless Steel 1 Scope This Standard specifies the specimen, test instrument and test equipment, test solution, test conditions and procedure, test result assessment and test report of corrosion test for intergranular corrosion susceptibility of low-cr ferritic stainless steel. This Standard is applicable to inspect the low-cr ferritic stainless steel (generally the chromium content is less than 16%) in the weakly oxidizing corrosive media by the sulfuric acid-copper sulfate corrosion test. 2 Normative References The following documents are essential to the application of this document. For the dated documents, only the versions with the dates indicated are applicable to this document; for the undated documents, only the latest version (including all the amendments) are applicable to this document. GB/T 5231 Designation and Chemical Composition of Wrought Copper and Copper Alloys GB/T 625 Chemical Reagent - Sulfuric Acid GB/T 665 Chemical Reagent – Copper (II) Sulfate Pentahydrate 3 Specimen 3.1 Sampling and preparation 3.1.1 The specimen of pressure-processed steel shall be taken from the steels with the same furnace number, the same specification, and the same heat-treatment batch. 3.1.2 Welded joints of plates shall be taken from the same base metal, and adopt the same welding process. solution; make it in micro boiling state; the test shall last 15h±3h. 6.6 After the test, take out the specimen to clean and dry. 7 Assessment of Test Results 7.1 For the specimen with insignificant uniform corrosion (specimen isn’t thinned or specimen surface has no obvious corrosive products covering), the metallographic method shall be used to assess the resistance to intergranular corrosion of the test materials. 7.2 Conduct the sampling analysis against the specimen section; the sampling length of section is recommended to be 15mm~20mm; observe the maximum intergranular corrosion depth of the specimen section through the metallographic method. 7.3 If the test material is weld seam specimen, when performing the section sampling to analyze its intergranular corrosion depth, the section direction of specimen shall be perpendicular to the weld seam; and cutting surface shall contain the weld seam zone and weld seam heat affected zone. 7.4 The data of specimen with the most serious corrosion shall be regarded as the standard to assess the test results. 8 Test Report Test report shall contain the following contents. a) Specimen name and test area size; b) If sensitizing treatment is performed, the sensitizing treatment system shall be recorded; c) Test solution, and test time; d) Test results. ......
 
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.