Rubber vulcanized -- Determination of abrasion resistance (Akron machine)
| Valid |
| GB/T 1689-1998 | English | 279 |
Add to Cart
|
3 days
|
Rubber vulcanized--Determination of abrasion resistance (Akron machine)
| Obsolete |
| GB 1689-1982 | English | 199 |
Add to Cart
|
2 days
|
Rubber, vulcanized--Determination of abrasion resistance (Akron machine)
| Obsolete |
BUY with any currencies (Euro, JPY, GBP, KRW etc.): GB/T 1689-2014 Related standards: GB/T 1689-2014
PDF Preview: GB/T 1689-2014
GB/T 1689-2014: PDF in English (GBT 1689-2014) GB/T 1689-2014
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 83.060
G 40
Partially replacing GB/T 1689-1998
Rubber vulcanized - Determination of abrasion
resistance (Akron machine)
ISSUED ON: SEPTEMBER 22, 2014
IMPLEMENTED ON: JUNE 01, 2015
Issued by: General Administration of Quality Supervision, Inspection and
Quarantine of PRC;
Standardization Administration of PRC.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative references ... 5
3 Principle ... 5
4 Instruments ... 5
5 Instrument calibration ... 6
6 Specimen ... 6
7 Environment conditioning ... 7
8 Procedures ... 7
9 Test results ... 7
10 Test report ... 8
Appendix A (Normative) Standard rubber formula ... 9
Foreword
This standard was drafted in accordance with the rules given in GB/T 1.1-2009.
This standard replaces GB/T 1689-1998 Rubber vulcanized - Determination of
abrasion resistance (Akron machine). As compared with GB/T 1689-1998, the
main technical changes are as follows:
- DELETE the age number of the normative references (see Chapter 2;
Chapter 2 of the 1998 edition);
- DELETE the normative reference GB/T 9865.1-1996 (see Chapter 2 of the
1998 edition);
- ADD relevant content in the principle (see Chapter 3);
- ADD Akron machine (see 4.1);
- ADD content related to the balance (see 4.2);
- ADD recommendations for regular calibration of grinding wheels (see note
in Chapter 5);
- ADD the use of different sample preparation methods (see note in Chapter
6);
- CORRECT the unit of density in the calculation formula (see 9.1; 9.1 of
1998 edition).
This standard was proposed by the China Petroleum and Chemical Industry
Federation.
This standard shall be under the jurisdiction of the National Rubber and Rubber
Product Standardization Technical Committee General Test Method
Subcommittee (SAC/TC 35/SC 2).
Drafting organizations of this standard: Zhongce Rubber Group Co., Ltd.,
Triangle Tire Co., Ltd., Fengshen Tire Co., Ltd., Qingdao Rubber Conveyor Belt
Co., Ltd., Qingdao Yikesi New Materials Co., Ltd., Shandong Bayi Tire
Manufacturing Co., Ltd., Qingdao Double Star Group Technology Development
Center, Beijing Rubber Industry Research and Design Institute, Guizhou Tire
Co., Ltd., Jiangsu Xinzhengwei Testing Machinery Co., Ltd., Jiangsu Mingzhu
Testing Machinery Co., Ltd.
The main drafters of this standard: Xiang Chan, Xu Qiuhuan, Yan Fujiang, Ren
Shaowen, Liu Yuwan, Zhang Feng, Yao Feng, Lin Qingju, Wang Daiqiang, Liu
Qiang, Zhao Jianlin, Sha Shufen, Xie Junfang, Li Jing, Feng Ping, Shen Kehui,
Rubber vulcanized - Determination of abrasion
resistance (Akron machine)
1 Scope
This standard specifies the method for determining the abrasion resistance of
vulcanized rubber.
This standard is applicable to the determination of the abrasion resistance of
vulcanized rubber by the Akron machine.
2 Normative references
The following documents are indispensable for the application of this document.
For dated references, only the dated version applies to this document. For
undated references, the latest version (including all amendments) applies to
this document.
GB/T 533 Rubber vulcanized or thermoplastic - Determination of density
(GB/T 533-2008, ISO 2781:2007, IDT)
GB/T 2941 Rubber - General procedures for preparing and conditioning test
pieces for physical test methods (GB/T 2941-2006, ISO 23529:2004, IDT)
3 Principle
In this test, the specimen and the grinding wheel are rubbed under a certain
inclination angle and a certain load, to determine the wear volume or wear index
of a certain mileage of the specimen.
4 Instruments
4.1 Akron machine
4.1.1 The rotation speed of the rubber wheel shaft is 76 r/min ± 2 r/min. The
rotation speed of the grinding wheel shaft is 34 r/min ± 1 r/min.
4.1.2 When the angle between the rubber wheel shaft and the grinding wheel
shaft is zero degrees, the two shafts shall remain parallel and horizontal.
is the circumference ratio.
6.2 The surface of the specimen shall be flat and shall be free from cracks and
impurities.
6.3 After the two sides of the specimen are polished, they are glued to the
rubber wheel. The specimen shall not be subjected to tension when bonding.
The joint shall be smoothly transitioned during binding. The bonded sample
wheel shall be conditioned for at least 16 h.
6.4 The rubber wheel has a diameter of 68 mm, a thickness of 12.7 mm ±
0.2 mm, a hardness of 75 to 80 degrees (Shore A). The diameter of the center
hole shall correspond to the diameter of the rotary shaft of the rubber wheel.
Note: The sample preparation method of vulcanizing the rubber to be tested or
directly vulcanizing the rubber to be tested on the metal mold wheel can also
be used. The test results obtained by different sample preparation methods are
not comparable and shall be noted in the test report.
7 Environment conditioning
The environment conditioning of the sample shall be carried out in accordance
with the provisions of GB/T 2941.
8 Procedures
8.1 Fix the glued specimen wheel on the rubber wheel shaft and start the motor
to rotate the specimen clockwise.
8.2 Pre-grind the specimen for 15 min ~ 20 min, remove the rubber scraps and
weigh the mass, accurate to 0.001 g.
8.3 Use pre-ground specimen for testing. After the specimen runs for 1.61 km,
turn off the motor, remove the specimen, brush off the chips, weigh it within 1
h, accurate to 0.001 g.
8.4 Determine the density of the specimen according to GB/T 533.
9 Test results
9.1 The wear volume V of specimen is calculated according to formula (1):
......
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.
|