GB/T 1599-2014
ICS 77.150.30
H 62
Replacing GB/T 1599-2002
Antimony ingot
Issued by. General Administration of Quality Supervision, Inspection and
Quarantine of the People’s Republic of China;
Standardization Administration of the People’s Republic of
Table of Contents
Foreword . 3 
1 Scope .. 4 
2 Normative references .. 4 
3 Requirements.. 4 
4 Test method . 5 
5 Inspection rules .. 5 
6 Mark, packaging, transportation, storage and quality certificate .. 7 
7 Content of contract (or purchasing order) .. 8 
This Standard is drafted in accordance with the rules given in GB/T 1.1-2009.
This Standard replaces GB/T 1799-2002 "Antimony ingot". Compared with GB/T 1599-
2002, the main changes are as follows.
-- This Standard adds designation Sb99.70.
-- This Standard cancels designation Sb99.85.
For chemical composition of antimony ingot, ADD requirements for two impurities of
bismuth and cadmium.
For chemical composition of the antimony ingot, increase the requirements for impurities
such as selenium and lead.
This Standard shall be under the jurisdiction of the National Technical Committee of Non-
Ferrous Metal (SAC/TC 243).
The drafting organizations of this standard. Hsikwang Shan Twinkling Star Co., Ltd. AND
Hunan Chenzhou Mining Co., Ltd.
Main drafters of this Standard. Li Zhiqiang, Liu Xinchun, Song Yingqiu, Dai Yongjun, Wu
Shaobo, Liao Guangrong, Zeng Qingbin, Deng Weihua, Yang Zhou, Liu Fangyun, Wang
Weiguo, Ouyang Jingquan, Gong Fubao and Zhao Bo.
This Part replaces the following previous standards.
-- GB/T 1599-1979, GB/T 1599-2002.
Antimony ingot
1 Scope
This Standard specifies the antimony ingot’s requirements, test methods, inspection rules
and marks, packaging, transportation, storage, quality certificates and contracts (or
purchasing orders).
This Standard is applicable to the antimony ingot which is produced by the raw materials
such as antimony concentrate and lead-antimony concentrate. The antimony-bead
standard which is produced by the raw materials such as antimony concentrate and lead-
antimony concentrate can also be implemented with reference to this Standard.
2 Normative references
The following documents are essential to the application of this document. For the dated
documents, only the versions with the dates indicated are applicable to this document; for
the undated documents, only the latest version (including all the amendments) are
applicable to this Standard.
GB/T 8170 Numerical Modification Rules
GB/T 3253 (all parts) Methods for chemical analysis of antimony and antimony trioxide
3 Requirements
3.1 Product classification
The antimony ingot is divided into four designations -- Sb99.90, Sb99.70, Sb99.65 and
Sb99.50 according to the chemical composition.
3.2 The chemical composition of antimony ingot shall comply with the provisions in Table
to the supplier within 60 days from the date of the receipt of the product; it shall be settled
by negotiation between the supplier and the demander. If the arbitration is required, the
arbitration sampling shall be carried out jointly by the supplier and the demander at the
demander's place.
5.2 Group-batch
Antimony ingot shall be submitted in batches for inspection. Each batch shall be composed
of the products of the same designation; the weight of each batch shall not exceed 100t.
5.3 Inspection items
It shall perform the inspections of chemical composition, surface mass and weight for each
batch of the antimony ingot.
5.4 Sampling and sample preparation
5.4.1 Sampling
The sampling of antimony ingot shall be performed in the same batch of the products
whose appearance inspection is qualified; sample the one which is not less than 5% of the
total antimony ingot as the sampled antimony ingot. Then use drill of which the bit’s
specification is ϕ8mm~ϕ12mm to perform alternate drilling (if drilling the top surface of the
first one, then it shall drill the bottom surface of the second one) on the top surface or the
bottom surface of the sampled antimony ingots in turn; the drilling position is at the three
equidistance-points on any diagonal line. The drilling depth shall not be less than half the
thickness of the antimony ingot. The collected drilling cuttings shall be the sample. The
lubricating agent shall not be used during the time of the drilling, and it shall choose the
appropriate rotating speed and the feeding rate (It is preferable to prevent the oxidation
phenomenon due to the excessive heating).
5.4.2 Sample preparation
Crush the sample to the particle size of not more than 5mm; mix it uniformly; divide it to
500g-1000g by quartile method; remove the iron filings with the magnet. Then divide it into
four equal parts; use one of them in the inspection; hand over one or two of them to
demander (if required by the demander); the other one shall be retained by the supplier for
future reference. Before the analysis and testing, samples shall be milled to the particle
size of no greater than 0.125mm by mortar. The sample shall be retained for twelve months.
5.5 Determination of the test results
5.5.1 When the analysis result of the chemical composition does not comply with the
provisions in this Standard, it shall be determined as the unqualified batch.
5.5.2 When the inspection result of the surface mass does not comply with the provisions