QC/T 262-1999 English PDF

QC/T 262-1999_English: PDF (QC/T262-1999)
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)StatusPDF
QC/T 262-1999English170 Add to Cart 0--9 seconds. Auto-delivery Metallographic Test of Car Carburizing Gear   QC/T 262-1999


BASIC DATA
Standard ID QC/T 262-1999 (QC/T262-1999)
Description (Translated English) Metallographic Test of Car Carburizing Gear
Sector / Industry Automobile & Vehicle Industry Standard (Recommended)
Classification of Chinese Standard T04
Word Count Estimation 6,654
Date of Issue 1905/6/21
Date of Implementation 1999-03-15
Older Standard (superseded by this standard) ZB T04001-1988
Quoted Standard GB/T 9450; GB/T 8539
Drafting Organization Changchun Automobile Research Institute of Materials
Administrative Organization National Automotive Standardization Technical Committee
Summary This standard specifies the meaning and detection methods automotive gear carburizing steel microstructure, the effective depth of carburized layer. This standard applies to the effective depth of carburized hardened layer is greater than 0. 3mm car gears. This standard applies to the heat treatment process after the completion of all quality checks gear.


QC/T 262-1999 QC AUTOMOTIVE INDUSTRY STANDARD OF THE PEOPLE’S REPUBLIC OF CHINA Replacing ZB T04 001-88 Metallographic Test of Car Carburizing Gear APPROVED ON. MARCH 15, 1999 IMPLEMENTED ON. MARCH 15, 1999 Approved by. State Bureau of Machine Building Industry Table of Contents 1 Theme Contents and Applicable Scope . 3 2 Normative References . 3 3 Terms .. 3 4 Specimen Requirements . 4 5 Technical Requirements .. 4 6 Structure Levels . 4 Additional Information... 10 Metallographic Test of Car Carburizing Gear 1 Theme Contents and Applicable Scope 1.1 This Standard specifies the definitions and test methods of metallographic structure, effective layer depth of carburized case for the car steel carburizing gear. 1.2 This Standard is applicable to the car gear with effective depth of carburized and hardened case greater than 0.3mm. 1.3 This Standard is applicable to the quality inspection of gear after finishing all the heat treatment procedures. 2 Normative References GB/T 9450 Steels - Determination and Verification of the Depth of Carburized and Hardened Cases GB/T 8539 General Specification for Quality Inspection of Gear Materials and Their Heat Treatment 3 Terms 3.1 Surface hardness The surface hardness near the pitch circle in the center of tooth-width. 3.2 Center hardness The hardness, on the cross-section in the center of tooth-width, and on the intersecting position between tooth centerline and tooth root circle (see Schematic diagram). 3.3 Effective depth of carburized and hardened case From the tooth surface, the vertical distance under 9.81N (1kgf) load measured to 550HV, or under 49.03N (5kgf) load measured to 515HV. 4 Specimen Requirements 4.1 When preparing the specimen, no phenomenon such as the structure changes due to heat shall occur. 4.2 When measuring the effective depth of carburized and hardened case, the tested surface shall be parallel to the working stage of hardness machine. 5 Technical Requirements 5.1 The effective depth of carburized and hardened case shall abide by the product drawing, and be subject to the tooth root and pitch circle positions; while its test method shall conform to the provisions of GB/T 9450; the decrease to the center hardness shall conform to the provisions of GB/T 8539. 5.2 The carbon content on the surface course is recommended to be 0.8%~1.0%. 5.3 Carbide Inspect under the magnification of 400×; the inspection position shall be subject to the addendum angle and working surface; evaluate as per the carbide level diagram in this Standard. The constantly meshed gear is qualified for Level 1~Level 5; while shifting gear is qualified for Level 1~Level 4. 5.4 Residual austenite and martensite Inspect under the magnification of 400×; the inspection position shall be subject to surface near pitch circle and tooth root; separately evaluate as per the residual austenite and martensite level diagram; it is qualified for Level 1~Level 5. 5.5 Surface hardness is HRC 58~63, the center hardness shall be specified by the product drawing. 5.6 If the surface is not martensite structure; the maximum depth shall not exceed 0.02mm. 6 Structure Levels 6.1 The carbide levels shall be determined as per its shape, quantity, size, distribution ......

Similar standards: QC/T 265-2023  QC/T 267-2023  QC/T 268-2023  
Similar PDFs (Auto-delivered in 9 seconds): QC/T 268-2023  QC/T 5-2017  QC/T 4-2017  QC/T 3-2017  QC/T 2-2017