GB/T 2766-2022 (GBT2766-2022)

GB/T 2766-2022_English: PDF (GBT 2766-2022, GBT2766-2022)
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)StatusPDF
GB/T 2766-2022English170 Add to Cart 0--9 seconds. Auto-delivery Surgical instruments -- Non-cutting, articulated instruments -- General requirements and test methods Valid GB/T 2766-2022

BASIC DATA
Standard ID GB/T 2766-2022 (GB/T2766-2022)
Description (Translated English) Surgical instruments -- Non-cutting, articulated instruments -- General requirements and test methods
Sector / Industry National Standard (Recommended)
Classification of Chinese Standard C31
Classification of International Standard 11.040.30
Word Count Estimation 10,173
Date of Issue 2022-10-14
Date of Implementation 2023-11-01
Older Standard (superseded by this standard) GB/T 2766-2006
Drafting Organization Shanghai Medical Devices (Group) Co., Ltd. Surgical Instruments Factory, Shanghai Medical Devices Inspection and Research Institute, Xinhua Surgical Instruments Co., Ltd.
Administrative Organization National Surgical Instrument Standardization Technical Committee (SAC/TC 94)
Proposing organization State Drug Administration
Issuing agency(ies) State Administration for Market Regulation, National Standardization Management Committee

Standards related to: GB/T 2766-2022

GB/T 2766-2022
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 11.040.30
CCS C 31
Replacing GB/T 2766-2006
Surgical instruments - Non-cutting, articulated instruments -
General requirements and test methods
(ISO 7151:1988, MOD)
ISSUED ON: OCTOBER 12, 2022
IMPLEMENTED ON: NOVEMBER 1, 2023
Issued by: State Administration for Market Regulation;
Standardization Administration of PRC.
Table of Contents
Foreword ... 3
1 Scope ... 6
2 Normative references ... 6
3 Terms and definitions ... 7
4 Materials ... 7
5 Requirements ... 7
6 Test methods ... 10
7 Marking ... 11
Appendix A (Informative) Structural changes of this document compared with ISO
7151:1988 ... 12
Surgical instruments - Non-cutting , articulated instruments
- General requirements and test methods
1 Scope
This document specifies the materials, requirements, test methods, and marking of non-
cutting articulated instruments.
This document applies to non-cutting articulated instruments.
2 Normative references
The following documents contain the provisions which, through normative reference in
this document, constitute the essential provisions of this document. For the dated
referenced documents, only the versions with the indicated dates are applicable to this
document; for the undated referenced documents, only the latest version (including all
the amendments) is applicable to this document.
GB/T 230.1-2018 Metallic materials - Rockwell hardness test - Part 1: Test method
(ISO 6508-1:2016, MOD)
NOTE: There is no technical difference between the referenced content of GB/T 230.1-2018 and
the referenced content of ISO 6508:1986.
GB/T 4340.1-2009 Metallic materials - Vickers hardness test - Part 1: Test method
(ISO 6507-1:2005, MOD)
NOTE: There is no technical difference between the referenced content of GB/T 4340.1-2009 and
the referenced content of ISO 6507-1:1982.
YY/T 0149-2006 Medical instruments of stainless steel - Test methods of corrosion
resistance (ISO 13402:1995, MOD)
YY/T 0294.1-2016 Surgical instruments - Metallic materials - Part 1: Stainless
steel (ISO 7153-1:1991, MOD)
NOTE: There is no technical difference between the referenced content of YY/T 0294.1-2016 and
the referenced content of ISO 7153-1:1983.
The test shall be carried out according to the provisions of GB/T 230.1-2018 or GB/T
4340.1-2009. The Rockwell hardness of the finished product (except 05Cr17Ni4Cu4Nb)
shall be within the range of 40HRC~48HRC or the Vickers hardness shall be within the
range of 390HV~485HV. The Rockwell hardness of the finished product made of
05Cr17Ni4Cu4Nb material shall be within the range of 36HRC~44HRC or the Vickers
hardness shall be within the range of 330HV~410HV. The difference between the two
pieces shall not be greater than Rockwell hardness 4HRC or Vickers hardness 40HV.
NOTE: The test force is determined by the manufacturer according to the product characteristics.
5.1.3 Hardness of tungsten carbide inserts
The test shall be carried out according to the provisions of GB/T 4340.1-2009; the
Vickers hardness of tungsten carbide inserts shall not be less than 1000HV10. The
difference in hardness between the inserts of the two opposite jaws shall not exceed
50HV10.
5.2 Corrosion resistance
The test shall be carried out according to the method specified in 6.1 or 6.2, and it shall
not be lower than the requirements of level-b in 5.4 of YY/T 0149-2006.
5.3 Manufacturing process
Instruments shall be manufactured according to appropriate process requirements.
When the instruments are fully locked, the jaw teeth shall be completely matched.
The teeth of the two parts of the instrument shall be clear, full, without sharp edges, and
of the same shape. The teeth shall fit together and there shall be no resistance when
reopening the instrument.
Unless otherwise specified, there shall be no sharp edges; sharp edges shall be removed
around the sides of the jaws.
The joints of the instrument shall be able to move smoothly, with proper tightness; the
instrument shall be able to be easily opened and closed by operating the control handle
with one hand.
5.4 Surface condition
5.4.1 General rules
The surface is checked with normal vision or corrected vision; there shall be no
abscesses, cracks, or wear marks on the surface of the instrument. Instruments shall be
free from residual scale, residual acid grease, and residues of grinding additive and
polishing agent.
5.4.2 Surface finishing
Surface finishing shall be one of the following situations or a combination of them:
a) Mirror polishing;
b) Processing to reduce reflection, such as satin polishing, matting, and
blackening processing;
c) Additional coating, e.g. a coated layer for insulation purposes.
NOTE 1: A satin finish is usually achieved by appropriate processes such as grinding, polishing, and
electropolishing followed by satin polishing (glass bead rolling or satin brushing). The smooth
surface is uniform, smooth, and weak glare.
NOTE 2: Instruments with a mirror finish are usually ground sufficiently to remove all surface
imperfections and polished to remove grinding marks to achieve a mirror finish. A mirror
finish is achieved by appropriate processes such as polishing, lapping, electropolishing, and
mirror polishing.
5.4.3 Passivation and final treatment
Unless the metallurgical properties of the instrument are unsuitable (for example, with
brazed or soft-soldered welded seam), the instrument shall be passivated or other
electrochemically treated in accordance with the properties of such stainless steel.
NOTE 1: Regarding the method of passivation treatment, such as electropolishing or treatment in 10%
(volume fraction) nitric acid solution, the treatment time is not less than 30 min, and the
temperature is within 10 °C~60 °C. The instruments are then rinsed with water and dried in
hot air.
NOTE 2: If the joint is lubricated, a non-corrosive lubricant that meets the requirements of the
Pharmacopoeia of the People’s Republic of China shall be used.
5.5 Elasticity
The test shall be carried out in accordance with the provisions of 6.3, and the instrument
shall not have obvious deformation, cracks, or any other permanent deformation.
5.6 Clamping function
The test shall be carried out in accordance with the provisions of 6.4; for needle holders,
there shall be no slippage of the fiber material, whether the loading direction is
longitudinal or transverse; for other instruments, the loading direction is determined
according to the tooth profile.
6 Test methods
6.1 Corrosion resistance (boiling water test)
6.1.1 Reagents
Distilled or deionized water.
6.1.2 Apparatus
Glass or ceramic beakers or suitable corrosion-resistant stainless-steel containers.
6.1.3 Sample preparation
Wash instruments with soap and warm water, rinse thoroughly in reagent (6.1.1), and
dry.
6.1.4 Test procedures
Put the instrument into the beaker or other container containing the reagent (6.1.1) and
boil for at least 30 min. The instrument is then cooled in test water for at least 1 h.
Remove the instrument from the water and expose it to air for 2 h. Wipe the instrument
vigorously with a dry cloth and check for signs of corrosion on the instrument.
6.2 Corrosion resistance (pressure steam test)
6.2.1 Equipment
A non-vacuum autoclave operating at 134 °C~138 °C and 0.22 MN • m-2.
6.2.2 Sample preparation
Sample preparation is the same as 6.1.3.
6.2.3 Test procedures
6.2.3.1 Place the instrument in a tray and place them in the autoclave.
6.2.3.2 The amount of third-grade water shall be determined according to the pressure
steam test cycle of the instrument, and 3+0.5 0 min, 134 °C~138 °C and 0.22 MN • m-2
shall be used as a pressure steam test cycle of the instrument.
6.2.3.3 After the test, remove the tray and allow the instrument to cool to room
temperature in the air. Check for signs of corrosion on instrument surfaces.
6.3 Elasticity
...