High temperature bearing steel
| Valid |
PDF Preview: GB/T 38886-2020
GB/T 38886-2020: PDF in English (GBT 38886-2020) GB/T 38886-2020
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.140.10
H 40
High temperature bearing steel
ISSUED ON: JUNE 02, 2020
IMPLEMENTED ON: DECEMBER 01, 2020
Issued by: State Administration for Market Regulation;
Standardization Administration of PRC.
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Normative references ... 4
3 Order content ... 7
4 Dimensions, appearance and weight ... 7
5 Technical requirements ... 9
6 Test method ... 14
7 Inspection rules ... 16
8 Packaging, marking, quality certificate ... 17
High temperature bearing steel
1 Scope
This standard specifies the order content, dimensions, shape, weight, technical
requirements, test methods, inspection rules, packaging, marking and quality
certificates of high temperature bearing steel.
This standard applies to the manufacture of hot-rolled or forged round steel,
cold-drawn round steel and steel wire (hereinafter referred to as steel) for high-
temperature bearings which have a temperature resistance of 300 °C ~ 550 °C.
2 Normative references
The following documents are essential to the application of this document. For
the dated documents, only the versions with the dates indicated are applicable
to this document; for the undated documents, only the latest version (including
all the amendments) are applicable to this standard.
GB/T 222 Permissible tolerances for chemical composition of steel products
GB/T 223.5 Steel and iron - Determination of acid-soluble silicon and total
silicon content - Reduced molybdosilicate spectrophotometric method
GB/T 223.9 Iron steel and alloy - Determination of aluminum content -
Chrome azurol S photometric method
GB/T 223.11 Iron, steel and alloy - Determination of chromium content -
Visual titration or potentiometric titration method
GB/T 223.13 Methods for chemical analysis of iron, steel and alloy - The
ammonium ferrous sulfate titration method for the determination of vanadium
content
GB/T 223.20 Methods for chemical analysis of iron steel and alloy - The
Potentiometric titration method for the determination of cobalt content
GB/T 223.23 Iron, steel and alloy - Determination of nickel content - The
dimethylglyoxime spectrophotometric method
GB/T 223.26 Iron, steel and alloy - Determination of molybdenum content -
The thiocyanate spectrophotometric method
GB/T 223.28 Methods for chemical analysis of iron, steel and alloy - The α-
GB/T 224 Determination of the depth of decarburization of steels
GB/T 226 Test method for macrostructure and defect of steel by etching
GB/T 228.1 Metallic materials - Tensile testing - Part 1: Method of test at
room temperature
GB/T 230.1 Metallic materials - Rockwell hardness test - Part 1: Test
method
GB/T 231.1 Metallic materials - Brinell hardness test - Part 1: Test method
GB/T 702-2017 Hot-rolled steel bars - Dimensions, shape, weight and
tolerances
GB/T 905-1994 Dimension, shape, weight and tolerance for cold-drawn
round, square and hexagonal steels
GB/T 908-2019 Forged bars for dimensions, shape, weight and tolerances
GB/T 2101 General requirement of acceptance packaging marking and
certification for section steel
GB/T 2103 General requirements for acceptance, packing, marking and
quality certification of steel wire
GB/T 4162-2008 Forged and rolled steel bars - Method for ultrasonic testing
GB/T 4336 Carbon and low-alloy steel - Determination of multi-element
contents - Spark discharge atomic emission spectrometric method (routine
method)
GB/T 6394 Metal - Methods for estimating the average grain size
GB/T 10561-2005 Steel - Determination of content of nonmetallic inclusions
- Micrographic method using standards diagrams
GB/T 11261 Steel and iron - Determination of oxygen content - The pulse
heating inert gas fusion-infra-red absorption method
GB/T 14979-1994 Eutectic carbide of steel - Micrographic method using
Standard diagrams
GB/T 15711 Inspection of non-metallic inclusions of steel - Etching test
method of tower samples
GB/T 18579-2019 High-carbon chromium bearing steel wires
GB/T 20066 Steel and iron - Sampling and preparation of samples for the
5.11.6 The surface of peeled, polished or machine-polished steel shall not have
harmful defects that affect the use of steel.
5.12 Special requirements
According to the requirements of the buyer, as negotiated between the supplier
and the buyer and indicated in the contract, it may add the following special
inspection items:
a) It may provide steel with a sulfur content of 0.015% ~ 0.060%;
b) Tower hairline;
c) Other requirements.
6 Test method
6.1 Surface quality
The surface quality of steel shall be inspected visually or by other effective
methods.
6.2 Dimensions and shape
Steel size measurement is carried out by a caliper or template that can ensure
the necessary accuracy.
6.3 Chemical composition
6.3.1 Sampling for chemical analysis shall be carried out in accordance with
GB/T 20066.
6.3.2 The chemical analysis method shall be carried out according to the
general methods such as GB/T 4336 and GB/T 20123. The arbitration shall be
carried out according to standards GB/T 223.5, GB/T 223.9, GB/T 223.11, GB/T
223.13, GB/T 223.20, GB/T 223.23, GB/T 223.26, GB/T 223.28, GB/T 223.29,
GB/T 223.31, GB/T 223.43, GB/T 223.47, GB/T 223.50, GB/T 223.53, GB/T
223.62, GB/T 223.63, GB/T 223.65, GB/T 223.77, GB/T 223.84, GB/T 223.85,
GB/T 223.86.
6.3.3 The specimen for oxygen content shall be inspected after fully removing
the decarburized layer. Its analysis method shall be carried out according to
GB/T 11261.
6.4 Mechanical properties
6.4.1 The test method of Brinell hardness shall be carried out in accordance
Where:
D - The maximum carbide size, in micrometers (μm);
α - The maximum length of carbide in any direction (major axis size), in
micrometers (μm);
b - Indicate the maximum size of the carbide perpendicular to the α direction
(minor axis size), in micrometers (μm).
6.9 Decarburization layer
The decarburization layer is carried out in accordance with the metallographic
law in GB/T 224.
6.10 Ultrasonic testing
Ultrasonic testing is carried out in accordance with level A requirements in GB/T
4162-2008.
6.11 Tower hairline
Tower-shaped hairline is carried out according to the requirements of GB/T
15711.
7 Inspection rules
7.1 Inspection and acceptance
The inspection and acceptance of steel shall be carried out by the technical
quality supervision department of the supplier. The purchaser has the right to
carry out acceptance inspection according to the provisions of this standard.
7.2 Group-batching rules
Steel shall be inspected and accepted in batches. Each batch shall be
composed of steels of the same designation, the same sub-heat number, the
same size, the same heat treatment number.
7.3 Sampling location and sampling quantity
The sampling location and quantity of steel shall be as specified in Table 13.
7.4 Re-inspection and judgment rules
7.4.1 If any item in the inspection item is unqualified (except for white spots and
non-metallic inclusions), it may take the same number of samples for
reinspection of the unqualified item. If the re-inspection result is still unqualified,
......