HOME   Cart(0)   Quotation   About-Us Tax PDFs Standard-List Powered by Google www.ChineseStandard.net Database: 189759 (8 Dec 2024)

GB/T 37336-2019 PDF in English


GB/T 37336-2019 (GB/T37336-2019, GBT 37336-2019, GBT37336-2019)
Standard IDContents [version]USDSTEP2[PDF] delivered inName of Chinese StandardStatus
GB/T 37336-2019English150 Add to Cart 0-9 seconds. Auto-delivery. Brake drum of automobile Valid
Standards related to (historical): GB/T 37336-2019
PDF Preview

GB/T 37336-2019: PDF in English (GBT 37336-2019)

GB/T 37336-2019 NATIONAL STANDARD OF THE PEOPLE’S REPUBLIC OF CHINA ICS 43.040.40 T 24 Brake drum of automobile ISSUED ON: MARCH 25, 2019 IMPLEMENTED ON: OCTOBER 01, 2019 Issued by: State Administration for Market Regulation; Standardization Administration of the PRC. Table of Contents Foreword ... 3  1 Scope ... 4  2 Normative references ... 4  3 Terms and definitions ... 5  4 Classification ... 5  5 Technical requirements ... 6  6 Inspection methods ... 9  Appendix A (Normative) Bench test methods of brake drum ... 12  Brake drum of automobile 1 Scope This Standard specifies the terms and definitions, classification, technical requirements, and inspection methods for brake drum of automobile. This Standard is applicable to the brake drums, whose body material is gray cast iron, for service brakes of types M and N vehicles specified in GB/T 15089- 2001. 2 Normative references The following documents are indispensable for the application of this document. For the dated references, only the editions with the dates indicated are applicable to this document. For the undated references, the latest edition (including all the amendments) are applicable to this document. GB/T 223.3 Methods for chemical analysis of iron, steel and alloy - The diantipyrylmethane phosphomolybdate gravimetric method for the determination of phosphorus content GB/T 223.58 Methods for chemical analysis of iron, steel and alloy - The sodium arsenite-sodium nitrite titrimetric method for the determination of manganese content GB/T 223.59 Iron, steel and alloy - Determination of phosphorus content - Bismuth phosphomolybdate blue spectrophotometric method and antimony phosphomolybdate blue spectrophotometric method GB/T 223.60 Methods for chemical analysis of iron, steel and alloy - The perchloric acid dehydration gravimetric method for the determination of silicon content GB/T 223.62 Methods for chemical analysis of iron, steel and alloy - The butyl acetate extraction photometric method for the determination of phosphorus content GB/T 223.63 Methods for chemical analysis of iron, steel and alloy - The sodium (potassium) periodate photometric method for the determination of manganese content GB/T 228.1 Metallic materials - Tensile testing - Part 1: Method of test at room temperature GB/T 231.1 Metallic materials - Brinell hardness test - Part 1: Test method GB/T 1031 Geometrical product specifications (GPS) - Surface texture: Profile method - Surface roughness parameters and their values GB/T 1958 Geometrical Product Specifications (GPS) - Geometrical tolerance - Verification GB/T 3177 Geometrical product specifications (GPS) - Inspection of plain workpiece sizes GB/T 7216 Metallographic test for gray cast iron GB/T 9239 (all parts) Mechanical vibration - Rotor balancing GB/T 9439-2010 Grey Iron Castings GB/T 20123 Steel and iron - Determination of total carbon and sulfur content - Infrared absorption method after combustion in an induction furnace (routine method) QC/T 556 Automotive brake temperature measurement and thermocouple mounted 3 Terms and definitions The following terms and definitions apply to this document. 3.1 Mounting spigot hole A center hole which mates with the hub. 3.2 Mounting surface The surface of the brake drum which fits the hub. 3.3 Limiting wear size The maximum radial size allowed after the friction surface of brake drum is worn. 4 Classification 4.1 Classification of brake drum the thermal fatigue test in accordance with A.4.1.1, shall not fail. 5.9.1.2 Brake drum samples for type M2, M3, N2, and N3 vehicles shall be tested in accordance with A.4.1.2. It shall meet one of the following requirements: a) The number of thermal fatigue test cycles when the brake drum sample fails is greater than or equal to 300; b) When the number of thermal fatigue test cycles when the brake drum sample fails is greater than 250, but less than 300, the test is repeated using a new brake drum sample. The number of thermal fatigue test cycles of both samples is greater than 250. 5.9.2 High load test Brake drum samples, after completion of the high load test in accordance with A.4.2, shall not fail. 6 Inspection methods 6.1 Mechanical properties 6.1.1 Tensile strength Samples for tensile strength shall be taken from the middle of the friction surface of brake drum. The sampling position is shown in Figure 3. If there are special requirements, it can be agreed between the supplier and the purchaser. The testing method of tensile strength shall be in accordance with the provisions of GB/T 228.1. Figure 3 -- Schematic diagram of sampling position of sample for tensile strength In the case where the tensile strength sampling size is limited, the wedge pressure strength can be used instead of the tensile strength. The size of the wedge sample shall comply with the requirements of Table 6. For the conversion method of wedge pressure strength and tensile strength, see Appendix D of GB/T 9439-2010. The wedge pressure strength is the average Sampling position Appendix A (Normative) Bench test methods of brake drum A.1 Scope This appendix specifies the test related requirements, failure criteria, and test methods for the bench tests such as thermal fatigue test and high load test of brake drum. A.2 Test related requirements A.2.1 Moment of inertia The actual inertia setting shall be as close as possible to the theoretical inertia. The deviation shall be within the range of ±5% of the theoretical inertia. The theoretical inertia refers to the inertia distributed on the corresponding wheel of the total inertia generated when the vehicle is braked. It shall be calculated according to formula (A.1). Where: I - Moment of inertia, in kilograms of square meters (kg • m2); m - Test mass (the mass of the vehicle’s maximum design total mass distributed on the corresponding wheel when braking), in kilograms (kg); r - Tire rolling radius, in meters (m). A.2.2 Test mass A.2.2.1 For vehicles with a maximum design total mass of less than 7500 kg, the test mass shall be calculated according to formula (A.2) or formula (A.3). Where: b) The hydraulic brake is 25 MPa/s±5 MPa/s. A.2.5 Sampling rate The sampling rate of brake line pressure and braking torque shall be greater than 20 Hz. A.2.6 Temperature measurement The thermocouple mounting position is at the center radius of the friction track of brake lining contact surface. The temperature measurement shall meet the requirements of QC/T 556. A.2.7 Sample and other brake requirements The test shall use a new brake drum and a new brake lining. The friction surface of brake drum shall be clean. Brake linings and other brake parts shall be original parts. There is no grease or other foreign matter on the brake lining surface. During the test, the brake lining, when worn to the limit, is allowed to be replaced. A.3 Sample failure criteria During the bench test, when one of the following phenomena occurs on the brake drum, it is determined that the brake drum sample has failed. a) The crack length of friction surface of brake drum exceeds two-thirds of the width of the friction surface of the brake drum; b) The crack on the friction surface of brake drum reaches the outer edge of the friction surface of brake drum; c) The brake drum has a penetrative crack; d) In any area outside the friction surface, there are any types of structural damage or cracks. A.4 Test methods and test conditions A.4.1 Thermal fatigue test A.4.1.1 Brake drum for type M1 and N1 vehicles The test methods and test conditions of the brake drum for type M1 and N1 vehicles are shown in Table A.3. ......
 
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.