Interleaving paper for cold rolled metal sheets
| Valid |
| GB/T 22869-2008 | English | 319 |
Add to Cart
|
3 days
|
Metal sheet and strip interleaving paper
| Obsolete |
BUY with any currencies (Euro, JPY, GBP, KRW etc.): GB/T 22869-2020 Related standards: GB/T 22869-2020
PDF Preview: GB/T 22869-2020
GB/T 22869-2020: PDF in English (GBT 22869-2020) GB/T 22869-2020
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 85.060
Y 32
Replacing GB/T 22869-2008
Interleaving Paper for Cold Rolled Metal Sheets
ISSUED ON: SEPTEMBER 29, 2020
IMPLEMENTED ON: APRIL 1, 2021
Issued by: State Administration for Market Regulation;
Standardization Administration of the People’s Republic of
China.
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Normative References ... 4
3 Requirements ... 5
4 Test Methods ... 6
5 Inspection Rules ... 8
6 Marking, Packaging, Transportation and Storage ... 9
Appendix A (normative) Determination of Tearing Retention Rate after Hot-
pressing ... 11
Interleaving Paper for Cold Rolled Metal Sheets
1 Scope
This Standard specifies the requirements, test methods, inspection rules, marking,
packaging, transportation and storage of interleaving paper for cold rolled metal sheets.
This Standard is applicable to protective papers for cold rolled metal sheets.
2 Normative References
The following documents are indispensable to the application of this document. In
terms of references with a specified date, only versions with a specified date are
applicable to this document. In terms of references without a specified date, the latest
version (including all the modifications) is applicable to this document.
GB/T 450 Paper and Board - Sampling for Testing and Identification of Machine and
Cross Direction Wire Side and Felt Side
GB/T 451.1 Paper and Board - Determination of Size and Deviation
GB/T 451.2 Paper and Board - Determination of Grammage
GB/T 455 Paper and Board - Determination of Tearing Resistance
GB/T 456 Paper and Board - Determination of Smoothness (Bekk method)
GB/T 462 Paper and Board - Determination of Moisture Content
GB/T 1540 Paper and Board - Determination of Water Absorption - Cobb Method
GB/T 1541 Paper and Board - Determination of Dirt
GB/T 1545-2008 Paper Board and Pulp - Determination of Acidity or Alkalinity
GB/T 2678.2-2008 Paper Board and Pulp - Determination of Water Soluble Chlorides
GB/T 2678.6 Paper, Board and Pulp - Determination of Water Soluble Sulphates
(conductimetric titration method)
GB/T 2828.1 Sampling Procedures for Inspection by Attribute - Part 1: Sampling
Schemes Indexed by Acceptance Quality Limit (AQL) for Lot-by-lot Inspection
GB/T 10342 Paper - Package and Mark
GB/T 10739 Paper, Board and Pulps - Standard Atmosphere for Conditioning and
Testing
GB/T 12914 Paper and Board - Determination of Tensile Properties - Constant Rate of
Elongation Method (20 mm/min)
GB/T 22837 Paper and Board - Determination of Surface Strength (wax method)
3 Requirements
3.1 The technical indexes of the interleaving paper for cold rolled metal sheets shall
comply with the stipulations of Table 1.
3.2 The paper surface shall be flat; the fiber structure shall be uniform. There shall be
no appearance defects, such as: folds, pulp mass, sand, oil stains and holes, etc.
3.3 The interleaving paper for cold rolled metal sheets is roll paper; the width deviation
of the roll shall not exceed 30 mm; the roll diameter and length shall comply with the
stipulations of the contract.
3.4 The end face of the paper roll shall be neat and clean; the banner shall have a
consistent degree of tightness; the paper core shall not be deformed. The deviation
between the end face of the paper core and the end face of the paper roll shall not
exceed ± 3 mm.
3.5 The joints of the interleaving paper for cold rolled metal sheets shall be firm and
flat, and there shall be no phenomenon of bonding layer. The joints shall be clearly
marked. In each batch of products, the number of rolls with joint(s) shall not exceed
10% of the total number of rolls of that batch of products, and the number of joints per
roll shall not exceed 2.
4.2 Grammage, Grammage Deviation and Banner Quantitative Difference
The grammage, grammage deviation and banner quantitative difference shall be
determined in accordance with GB/T 451.2. When determining the banner quantitative
difference, the width of 1,000 mm is used as the benchmark.
4.3 Tensile Strength and Elongation
The tensile strength and elongation shall be determined in accordance with GB/T
12914.
4.4 Tearing Resistance
The tearing resistance shall be determined in accordance with GB/T 455.
4.5 Surface Oil Absorption
The surface oil absorption shall be determined in accordance with GB/T 1540. The
medium shall adopt FX-50C rolling oil; the oil absorption time shall be 60 s.
4.6 Tearing Retention Rate after Hot-pressing
The tearing retention rate after hot-pressing shall be determined in accordance with
Appendix A.
4.7 Smoothness
The smoothness shall be determined in accordance with GB/T 456.
4.8 Surface Strength
The surface strength shall be determined in accordance with GB/T 22837.
4.9 Water Extract pH
The water extract pH shall be determined in accordance with the pH meter method in
GB/T 1545-2008; the cold extraction shall be adopted.
4.10 Water Soluble Chlorides
The water soluble chlorides shall be determined in accordance with GB/T 2678.2-2008;
the mercury nitrate method shall be adopted.
4.11 Water Soluble Sulphates
The water soluble sulphates shall be determined in accordance with GB/T 2678.6.
4.12 Moisture Index for Delivery
Appendix A
(normative)
Determination of Tearing Retention Rate after Hot-pressing
A.1 Principle
Under certain temperature and pressure, conduct hot-pressing treatment on the
specimen; test the tearing resistance of the specimen after the hot-pressing treatment
and the tearing resistance of the control specimen; calculate the tearing retention rate
of the specimen.
A.2 Instruments and Materials
A.2.1 Hot-pressing testing machine
The maximum working pressure is 16 MPa; the highest set temperature may reach
300 °C. The size (length width) of the hot-pressing plate is 400 mm 400 mm.
A.2.2 Stainless steel plate
Quantity: 7 pieces; surface processing type: 2B; designation: 304; specifications
(length width thickness): 350 mm 350 mm 0.5 mm.
A.3 Preparation of Specimens
A.3.1 Along the paper web, horizontally stack two pieces of sample with the length of
the paper roll banner width and the width of 800 mm into three layers. Then, along the
longitudinal direction, uniformly cut two stacks of 320 mm 320 mm specimen. A total
of 12 specimens are taken, in which, 6 specimens are used for the hot-pressing
resistance test, and the other 6 specimens are used as control specimens.
A.3.2 Prepare 7 clean stainless steel plates (A.2.2). Firstly, place a specimen flatwise
on the first stainless steel plate; use the second stainless steel plate to cover it. When
covering the second stainless steel plate, maintain the plate and the edge of the plate
aligned. Then, place the second specimen flatwise on the second stainless steel plate;
use the third stainless steel plate to cover it, until the 6th specimen is placed flatwise
on the 6th stainless steel plate, then, use the 7th stainless steel plate to cover it. Thus,
a combination of stainless steel plate - specimen is formed.
A.4 Test Procedures
A.4.1 Switch on the power of the hot-pressing testing machine (A.2.1); set the
temperature to 170 °C and the working pressure to 8.0 MPa.
......
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.
|