GBZ41107.3-2021 English PDFUS$349.00 · In stock
Delivery: <= 4 days. True-PDF full-copy in English will be manually translated and delivered via email. GBZ41107.3-2021: Destructive tests on welds in metallic materials - Hot cracking tests for weldments - Arc welding processes - Part 3: Externally loaded tests Status: Valid
Basic dataStandard ID: GB/Z 41107.3-2021 (GB/Z41107.3-2021)Description (Translated English): Destructive tests on welds in metallic materials - Hot cracking tests for weldments - Arc welding processes - Part 3: Externally loaded tests Sector / Industry: National Standard Classification of Chinese Standard: J33 Word Count Estimation: 18,194 Issuing agency(ies): State Administration for Market Regulation, China National Standardization Administration GBZ41107.3-2021: Destructive tests on welds in metallic materials - Hot cracking tests for weldments - Arc welding processes - Part 3: Externally loaded tests---This is a DRAFT version for illustration, not a final translation. Full copy of true-PDF in English version (including equations, symbols, images, flow-chart, tables, and figures etc.) will be manually/carefully translated upon your order. GB /Z 41107:3-2021 Destructive tests on welds in metallic materials -- Hot cracking tests for weldments -- Arc welding processes -- Part 3: Externally loaded tests ICS 25:160:40 CCSJ33 National Standardization Guiding Technical Document of the People's Republic of China Destructive testing of welds in metallic materials Arc welding method for hot crack test of weldments Part 3: External load test (ISO /T R17641-3:2005,MOD) Published on 2021-12-31 2022-07-01 Implementation State Administration for Market Regulation Released by the National Standardization Administration directory Preface III Introduction IV 1 Scope 1 2 Normative references 1 3 Terms and Definitions 1 4 Symbols and Abbreviations 1 5 General 2 6 Trial 3 7 Test report 11 Appendix A (Informative) Adjustable Restraint Test Device and Use of Auxiliary Bending Plate Legend 12 forewordThis document is in accordance with the provisions of GB/T 1:1-2020 "Guidelines for Standardization Work Part 1: Structure and Drafting Rules of Standardization Documents" drafted: This document is part 3 of GB/T (Z) 41107 "Arc Welding Method for Destructive Testing of Welds of Metal Materials for Hot Crack Test" point: GB/T (Z)41107 has released the following parts: --- Part 1: General; --- Part 2: Self-restraint test; --- Part 3: External load test: This document uses the redrafted method to modify the use of ISO /T R17641-3:2005 "Hot cracking of weldments for destructive testing of welds in metallic materials" Pattern Test Arc Welding Methods Part 3: External Load Test: This document has technical differences compared with ISO /T R17641-3:2005, and the clauses involved in these technical differences have been adopted on the outside The vertical single line (|) at the margin position is marked, and the corresponding technical differences and their reasons are as follows: a) ISO 17641-1:2004 (see Chapter 3) is replaced by GB/T 41107:1 modified to adopt international standards; b) Added the symbol and description of the critical compression displacement "CCD" (see Chapter 4); c) Added the symbol and description of bending strain ε (see Chapter 4); d) The symbols and descriptions of SS and SV are deleted (see Chapter 4); e) Changed the description of "Vcrit" from "critical strain to produce the first thermal crack" to "critical tension to produce the first thermal crack" rate" (see Chapter 4); f) Added the symbol and description of VPVR (see Chapter 4); g) Changed the name of the test, from "flat plate tensile test" to "programmed flat plate tensile test", in accordance with the test method GB/T 41107:1- 2021 is consistent with the presentation (see Chapter 4, Chapter 5, 6:3); h) Modified the index for evaluating solidification cracks by hot tensile test in Table 2, from "BTR" to "CCD" (see Chapter 5); i) Changed the symbol of the sample length in Figure 1, from "a" to "l" (see 6:1:2); j) added a description of the result processing of Method A (see 6:1:5); k) The formula and related descriptions of bending strain are added (see 6:2:3); l) Added example Figure 4b) about crack inspection results (see 6:2:4): The following editorial changes have also been made to this document: --- Change "ductility recovery temperature (DTR)" in the description of "BTR" in Table 1 to "ductility recovery temperature (DRT)" (see Chapter 4); --- Change the welding rate symbol from "Ws" to "Vw" to be consistent with the test (see Chapter 4); --- Change the "Rm" unit in Figure 2 from "N/mm2" to "MPa" (see 6:1:5); --- Change the position of the transverse axis of 500/510 from the corresponding 0:5% bending strain to the corresponding 1% bending strain (see 6:2:4); --- Change the symbol from "Vcr" to "Vcrit" (see 6:3:3, 6:3:4); --- Added Appendix A "The Legend of Adjustable Restraint Test Device and Use of Auxiliary Bending Plates" (informative): Please note that some content of this document may be patented: The issuing agency of this document assumes no responsibility for identifying patents: This document is proposed by China Machinery Industry Federation: This document is under the jurisdiction of the National Welding Standardization Technical Committee (SAC/TC55): This document is drafted by: Harbin Welding Research Institute Co:, Ltd:, Shanghai Materials Research Institute, Suzhou Thermal Engineering Research Institute Co:, Ltd:, Tianjin University Xue, Baoji Petroleum Steel Pipe Co:, Ltd: (National Petroleum and Natural Gas Pipe Engineering Technology Research Center): The main drafters of this document: Xu Kai, Lv Xiaochun, Wang Bin, Sun Zhiqiang, Chen Mo, Yang Haoquan, An Hongliang, Zhai Lianna, Chen Zhongbing, Lu Li, Wang Dongpo, Yang Zijia, Zhang Jun, Su Jinhua, Qiao Wenyu:IntroductionHot cracks in the heat affected zone of the weld metal and base metal are one of the most common defects in arc welding: Cracks affect the safety of welded parts Use, in most codes and standards, any type of detectable cracks are not allowed, therefore, countries are working on research and development of thermal Crack-insensitive welding consumables and base metals, and welding processes designed to reduce or eliminate the risk of hot cracking: At the same time, a variety of Test methods for thermal crack susceptibility of metallic weldments (including weld consumables, base metals, and welded joints) are also being developed: GB/T (Z)41107 "Arc Welding Method for Destructive Testing of Welds of Metal Materials for Hot Crack Test" is a guide for hot cracking of weldments in my country: Basic and generic document for striae testing: GB/T (Z) 41107 aims to establish the terminology, basic principles and tests applicable to hot crack testing type, which consists of three parts: --- Part 1: General: A brief introduction to hot crack testing terminology, basic principles, test types, test overview, and test applications The regulations aim to provide the corresponding basic information for the testing personnel: --- Part 2: Self-restraint test: Specifications for specimen dimensions, specimen requirements and test procedures for self-restrained thermal crack tests are intended to Provide inspectors with relevant technical information on thermal crack self-restraint testing: --- Part 3: External load test: For thermal tensile test, adjustable restraint test and transverse adjustable restraint test, program-controlled flat plate tensile test Specifications for specimen size, specimen preparation, test procedures and evaluation methods for thermal crack testing under external load Provides technical information on thermal crack external load testing: Destructive testing of welds in metallic materials Arc welding method for hot crack test of weldments Part 3: External load test1 ScopeThis document specifies external load thermal cracks such as thermal tensile test, adjustable restraint test, transverse adjustable restraint test, and program-controlled flat plate tensile test: Test specimen dimensions, specimen preparation, test procedures and evaluation methods: This document applies to the assessment of hot crack susceptibility of austenitic stainless steels, nickel and nickel-based alloys, nickel-copper alloy base metals and welding consumables: If the contract Both parties have agreed that this document may also be used for reference to other materials such as aluminum alloys and high-strength steels:2 Normative referencesThe contents of the following documents constitute essential provisions of this document through normative references in the text: Among them, dated citations documents, only the version corresponding to that date applies to this document; for undated references, the latest edition (including all amendments) applies to this document: GB/T 41107:1 Arc Welding Method for Destructive Test Welds of Metal Materials - Part 1: General Provisions (GB/T 41107:1-2021, ISO 17641-1:2004, MOD)3 Terms and DefinitionsThe terms and definitions defined in GB/T 41107:1 apply to this document:4 Symbols and AbbreviationsThe symbols and abbreviations in Table 1 apply to this document: Table 1 Symbols and abbreviations and descriptions Symbol/Abbreviation Description Unit hot tensile test BTR Brittleness temperature range, the difference between zero strength temperature (NST) and ductile recovery temperature (DRT) °C CCD critical compression displacement, the minimum displacement required to apply controllable compression to ensure no more cracking mm DRR Ductility recovery rate, ratio of area shrinkage difference [(Z②-Z③)/(Z①-Z③)]×100 (see Figure 2) % DRT ductility recovery temperature, the temperature at which the area shrinkage Z recovers to 5% in the "cooling" tensile test ℃ NDR zero ductility temperature range, temperature difference (T④-T⑥) (see Figure 2) ℃ NST Zero strength temperature, that is, the highest temperature T⑥ of the test (see Figure 2) ℃ RDR Ductility recovery ratio, area ratio (S②-③-④/S①-③-⑤)×100 (see Figure 2) - ......Tips & Frequently Asked Questions:Question 1: How long will the true-PDF of GBZ41107.3-2021_English be delivered?Answer: Upon your order, we will start to translate GBZ41107.3-2021_English as soon as possible, and keep you informed of the progress. The lead time is typically 2 ~ 4 working days. The lengthier the document the longer the lead time.Question 2: Can I share the purchased PDF of GBZ41107.3-2021_English with my colleagues?Answer: Yes. The purchased PDF of GBZ41107.3-2021_English will be deemed to be sold to your employer/organization who actually pays for it, including your colleagues and your employer's intranet.Question 3: Does the price include tax/VAT?Answer: Yes. Our tax invoice, downloaded/delivered in 9 seconds, includes all tax/VAT and complies with 100+ countries' tax regulations (tax exempted in 100+ countries) -- See Avoidance of Double Taxation Agreements (DTAs): List of DTAs signed between Singapore and 100+ countriesQuestion 4: Do you accept my currency other than USD?Answer: Yes. If you need your currency to be printed on the invoice, please write an email to Sales@ChineseStandard.net. In 2 working-hours, we will create a special link for you to pay in any currencies. Otherwise, follow the normal steps: Add to Cart -- Checkout -- Select your currency to pay. |
