GB/T 37616-2019 English PDFUS$439.00 · In stock
Delivery: <= 4 days. True-PDF full-copy in English will be manually translated and delivered via email. GB/T 37616-2019: Aluminium alloys extruded profiles-axial force controlled fatigue testing method Status: Valid
Basic dataStandard ID: GB/T 37616-2019 (GB/T37616-2019)Description (Translated English): Aluminium alloys extruded profiles-axial force controlled fatigue testing method Sector / Industry: National Standard (Recommended) Classification of Chinese Standard: H61 Classification of International Standard: 77.150.10 Word Count Estimation: 22,241 Date of Issue: 2019-06-04 Date of Implementation: 2020-05-01 Issuing agency(ies): State Administration for Market Regulation, China National Standardization Administration GB/T 37616-2019: Aluminium alloys extruded profiles-axial force controlled fatigue testing method---This is a DRAFT version for illustration, not a final translation. Full copy of true-PDF in English version (including equations, symbols, images, flow-chart, tables, and figures etc.) will be manually/carefully translated upon your order.Aluminium alloys extruded profiles-axial force controlled fatigue testing method ICS 77.150.10 H61 National Standards of People's Republic of China Aluminum alloy extruded profile axial force Control fatigue test method Published on.2019-06-04 2020-05-01 implementation State market supervision and administration China National Standardization Administration issued ForewordThis standard was drafted in accordance with the rules given in GB/T 1.1-2009. This standard was proposed by the China Nonferrous Metals Industry Association. This standard is under the jurisdiction of the National Nonferrous Metals Standardization Technical Committee (SAC/TC243). This standard was drafted. Liaoning Zhongwang Group Co., Ltd., Nonferrous Metals Technology and Economic Research Institute, Guohe General Test Evaluation and Certification Shares Company, China Aviation Shenfei Civil Aircraft Co., Ltd., Guangdong Industrial Analysis and Testing Center, Shannan Nanshan Aluminum Co., Ltd., Northeast Light Alloy Co., Ltd., Southwest Aluminum (Group) Co., Ltd., Shandong Yankuang Light Alloy Co., Ltd., Guangdong Gaodeng Aluminum Co., Ltd. CZ Zhuzhou Electric Locomotive Co., Ltd., CRRC Tangshan Locomotive & Rolling Stock Co., Ltd., CRRC Qingdao Sifang Locomotive & Rolling Stock Co., Ltd., Guangdong Jianmei Aluminum Profile Factory (Group) Co., Ltd. The main drafters of this standard. Sun Wei, Xi Huan, Wu Lei, Liu Zuoyu, Shi Changliang, Li Cast Iron, Wang Jinhua, Xiao Hong, Liu Bo, He Jiajin, Yue Yixin, He Tian, Lin Huaqiang, Xu Shiguang, Jia Dazhao. Aluminum alloy extruded profile axial force Control fatigue test method1 ScopeThis standard specifies aluminum alloy extruded profiles at room temperature (10 ° C ~ 35 ° C) (no stress concentration introduced) by axial equal amplitude force control fatigue Test method. This standard is applicable to the determination of fatigue life under the specified stress level of aluminum alloy extruded profiles, and specifies the fatigue strength under the condition of cycle number. Determination of SN curve, PSN curve and Goodman curve.2 Normative referencesThe following documents are indispensable for the application of this document. For dated references, only dated versions apply to this article. Pieces. For undated references, the latest edition (including all amendments) applies to this document. GB/T 10623 Metallic material mechanical properties test terminology JJG556 axial afterburning fatigue testing machine3 Terms and definitionsThe following terms and definitions as defined in GB/T 10623 apply to this document. 3.1 Survivability probabilityofsurvival The probability that the fatigue life or fatigue strength exceeds the specified value is expressed as a percentage. 3.2 Median fatigue life medianfatiguelife N50 Fatigue life with 50% survival. 3.3 Fatigue lifeforPsurvival NP The fatigue life of the base material survival rate P at or above the specified stress level. Note. Survival rate P generally takes 97.5%, 95%, 90%, etc. 3.4 Median logarithmic fatigue life medianlogarithmfatiguelife X50 (or lgN50) Log fatigue life with 50% survival. 3.5 Logarithmic fatigue life with a specified survival rate logarithmfatiguelifeforPsurvival xP (or lgNP) The logarithmic fatigue life at which the parent metal survival rate P can reach or exceed at a specified stress level. 3.6 Fatigue strength for survival rate fatiguetengforforsursural σP When a certain fatigue life N is specified, the base material survival rate P can reach or exceed the fatigue strength. 3.7 Median fatigue strength medianfatiguestrength Σ50 Fatigue strength with 50% survival. 3.8 Median SN curve medianS-Ncurve A curve obtained by fitting the median fatigue life at each stress level and fitting the median fatigue strength at each specified life, ie Stress-life relationship curve for 50% survival. 3.9 PSN curve PS-Ncurve Fit the fatigue life of the P-survival rate at each stress level and fit the fatigue strength of the P-survival rate at each specified life The resulting curve, the stress-life curve of P survival rate. 3.10 Goodman curve Goodmancurve Under the specified fatigue life conditions (for example. specified fatigue life Nf = 1 × 107), by at least three different stress ratios R (for example. R = The fatigue stress level parameters of -1, 0.1, and 0.5), that is, the relationship between the maximum stress, the minimum stress, the stress amplitude, and the average stress.4 Method OverviewThe method is to apply a constant amplitude alternating load along the longitudinal direction of the sample (see Figure 1). The cyclic stress type is shown in Figure 2. Prescribed stress level Under the conditions, the fatigue life of the material is measured; and the fatigue strength of the material is measured under the condition of a predetermined number of cycles. Description. 1---upper fixture; 2---sample; 3--- Lower fixture. Figure 1 Schematic diagram of fatigue test Description. Σa --- stress amplitude; Σm --- average stress; Pressure---σmax≤0, σmin< 0; Pulling pressure---σmax>0, σmin< 0; Lara---σmax >0, σmin≥0. Figure 2 cyclic stress type5 test equipment5.1 Fatigue testing machine. Electromagnetic resonance fatigue testing machine, electro-hydraulic servo fatigue testing machine or other forms of axial fatigue testing machine. 5.2 The fatigue tester shall meet the requirements of JJG556.6 sample6.1 Sample classification The shape of the sample varies according to the shape and size of the cross section of the working part, and can be divided into a circular single-section sample, a circular cross-section sample, and a rectangular shape. Single-section specimens and rectangular cross-section specimens. The circular sample is divided into a cylindrical sample and a threaded sample according to the type of the clamping end. Notched specimen The shape and size are indicated on the order form (or contract) after agreement between the supplier and the buyer. 6.2 Sample shape and size 6.2.1 Round sample 6.2.1.1 Round single section specimen The shape of the circular single-section specimen is shown in Figure 3. The dimensions and deviations are in accordance with Table 1. Description. R1 --- sample arc radius; D1 --- the smallest diameter of the sample; D(M)---sample clamping part diameter or thread size; L1 --- clamping part; L --- Total length of the sample. Figure 3 Schematic diagram of a circular single-section sample Table 1 Round single-section sample size and deviation unit is mm Profile thickness a sample type Minimum diameter of sample D1 Sample arc radius R1 Sample holding part diameter or snail Grain specification D (M) >15.00~25.00 Thread sample Cylindrical sample 5.00±0.02 50.00±1.00 M14×1 12.00±1.00 >25.00 Thread sample Cylindrical sample 10.00±0.02 80.00±1.00 M22×1 20.00±1.00 6.2.1.2 Round equal section specimen The shape of the circular cross-section sample is shown in Figure 4. The dimensions and deviations are in accordance with Table 2. Description. R2 --- sample transition arc radius; D2 --- sample cross-sectional diameter; D(M)---sample clamping part diameter or thread size; L1 --- clamping part; Lc --- parallel length of the working part of the sample; L --- Total length of the sample. Figure 4 Schematic diagram of a circular cross-section sample Table 2 The dimensions and deviation units of the circular equal section specimen are in millimeters Profile thickness a sample type Specimen cross-sectional diameter D2 Sample transition arc radius R2 Specimen working part Parallel length Lc Sample holding part diameter or Thread size D (M) ≥25.00 Thread sample Cylindrical sample 10.00±0.05 60.00±1.00 35.00±1.00 M22×1 20.00±1.00 6.2.1.3 Allowable deviation For circular cross-section specimens, the allowable deviation of coaxiality and parallelism is not more than 0.05mm, and the perpendicularity between the end faces of the threaded specimen and the axis The allowable deviation is not more than 0.05mm. 6.2.2 Rectangular specimen 6.2.2.1 Rectangular single section specimen The shape of the rectangular single-section specimen is shown in Figure 5. The dimensions and deviations are in accordance with Table 3. If there are special requirements, the supply and demand double After the party has agreed, please indicate it in the order form (or contract). Description. R1---sample arc radius; a --- sample thickness; B1 --- the minimum width of the sample; B --- sample clamping part width; L1---clamping part; L --- Total length of the sample. Figure 5 Schematic diagram of a rectangular single-section sample Table 3 Rectangular single-section specimen size and deviation unit is mm Profile thickness a Sample minimum width b1 Sample arc radius R1 Sample clamping portion width B ≤15.00 15.00±0.05 120.00±1.00 40.00±1.00 6.2.2.2 Rectangular equal section specimen The shape of the rectangular cross-section sample is shown in Figure 6. The dimensions and deviations should be in accordance with Table 4. If there are special requirements, the supply and demand double After the party has agreed, please indicate it in the order form (or contract). Description. R2---sample transition arc radius; a --- sample thickness; B2 --- sample cross section width; B --- sample clamping part width; L1---clamping part; Lc---the parallel length of the working part of the sample; L --- Total length of the sample. Figure 6 Schematic diagram of a rectangular equal-section sample Table 4 Rectangular equal section sample size and deviation unit is mm Profile thickness a Specimen cross-sectional width b2 Specimen transition arc radius R2 Parallel length Lc of specimen working part Width of specimen clamping part B ≤15.00 15.00±0.05 50.00±1.00 50.00±1.00 40.00±1.00 6.2.2.3 Allowable deviation The allowable deviation of the parallelism of the parallel portion of the sample is not more than 0.15 mm, and the allowable deviation of the coaxiality of the clamping portions at both ends is not more than 0.40 mm. 6.3 Sample preparation 6.3.1 General requirements 6.3.1.1 The sampling position and direction shall comply with the requirements of relevant standards or agreements. If the sampling position and direction are not specified, it may be as specified in 6.3.2. Sampling with 6.3.3 and numbering and marking the samples. 6.3.1.2 The processing dimensions, shape tolerances and surface roughness of the specimen shall meet the requirements, and the arc and parallel length shall be smoothly connected. Single cross section test Sample size and shape tolerances should be verified and measured using a tool microscope. 6.3.1.3 During turning and milling, the depth of cut shall be reduced successively and sufficient cutting fluid shall be provided to reduce work hardening and prevent overheating. 6.3.1.4 When the sample is polished, it shall be polished along the longitudinal direction of the sample, and the force pressed against the surface of the sample shall be as small as possible to reduce the influence of surface residual stress. 6.3.1.5 The surface of the specimen shall be free from scratches, bumps and corrosion. 6.3.2 Round specimen 6.3.2.1 When the wall thickness of the profile is greater than 15.00mm and not more than 40.00mm, a circular specimen is cut at the center of the profile wall thickness; the profile wall When the thickness is greater than 40.00 mm, a circular sample having a diameter of d 5.00 mm is cut from the center of the wall thickness of the profile to the position 1/2 of the surface. 6.3.2.2 After the round sample is roughed, the diameter of the sample is d 0.50mm. It is recommended to cut through 3 times, each cutting depth is 1.25mm, 0.75mm, 0.25mm. 6.3.2.3 After the roughing of the sample is finished, the diameter of the sample is d 0.02mm. It is recommended to cut through 3 times. The degree is 0.12 mm, 0.07 mm, and 0.05 mm. 6.3.2.4 Polish the finished sample in a direction approximately perpendicular to the axis of the sample, and finally reach the nominal size of the sample, except for the sample holding end Further, the surface roughness Ra is not more than 0.32 μm. 6.3.3 Rectangular specimen 6.3.3.1 When the wall thickness of the profile is not more than 15.00mm, cut the rectangular specimen with full wall thickness. 6.3.3.2 Rectangular cross-section The surface of the specimen is generally not required to be machined. The side is generally longitudinally milled. It is recommended that after 3 passes, each The secondary milling depth is 0.50 mm, 0.20 mm, 0.10 mm. 6.3.3.3 Polish the milled specimen longitudinally until it reaches the nominal size. The side surface roughness Ra is not higher than 0.32 μm except for the sample holding end. 6.3.3.4 In order to avoid the occurrence of fatigue cracks on the edges, the edge of the working part of the specimen should have a reverse radius of 0.10 mm along the axial direction. A rounded corner of 0.20 mm and a roughness of no more than 0.32 μm.7 Test instructions7.1 Before the test, the sample shall be visually inspected. When the surface of the sample is cleaned, the sample shall not be damaged. Surface defects, cracks, chisels, nicks, circumferential scratches, unfused and corroded defects are not permitted. 7.2 Use a tool microscope to measure the width or diameter of the smallest cross section of a single-section specimen, measure the thickness of the specimen with a micrometer, and measure the fine The degree should be no less than 0.01mm. 7.3 The clamping specimen shall be such that the load applied to the specimen is axial. 7.4 The applied load shall be smooth and shall not be overloaded. The load should be kept stable during the sample process. 7.5 The test selection frequency range is generally not more than.200 Hz. 7.6 The specimen shall be tested under the specified stress until the specimen is broken or tested to the specified number of cycles. 7.7 The sample fracture occurs in the non-working part and the test result is invalid. 7.8 Record test results and abnormalities during the test.8 Test methods and data processing8.1 Passability test 8.1.1 Overview of test methods Passivity test is used for random sampling test of product production process control. 8.1.2 Number of samples Prepare at least 3 samples for each inspection lot. 8.1.3 Test conditions The test conditions are generally the specified stress level, the stress ratio R, the specified number of cycles, and the test frequency range. Stress level, stress ratio, and The number of cycles is determined by the test conditions specified by the technical standards and technical agreements. 8.1.4 Evaluation of test results Under the specified test conditions, if all the fatigue samples of the same inspection batch have reached the specified number of cycles without breaking, the test knot If the sample is broken or broken in the non-working part, the test result is unqualified. 8.2 Determination of fatigue life 8.2.1 Overview of test methods The group test method was used to determine the median fatigue life at a certain stress level in the middle life zone and the fatigue life of the specified survival rate. 8.2.2 Number of samples A set of samples of at least 3 pieces. The number of samples that need to be repeated for each level of stress depends on the degree of dispersion of the test data and should meet the requirements. The confidence level sought. 8.2.3 Determination of median fatigue life The fatigue life of a set of samples was measured at the same stress level. When the confidence level γ is required, it should be based on the variation system during the test. For the number CV=s/x and the given confidence γ, refer to Table A.1 of Appendix A to determine the minimum number of observations required. When testing data processing, first Each fatigue life is taken as a logarithmic fatigue life xi = lgNi, and then calculated. Subsample mean x. x= N∑ i=1 Xi (1) Subsample standard deviation s. s= i=1 (xi-x)2 N-1 (2) Median fatigue life N50. N50=lg-1x (3) 8.2.4 Determination of the fatigue life of the specified survival rate Specifies the logarithmic fatigue life xP of the survival rate P. xP = x ± uPs (4) In the formula, the standard normal offset uP value corresponding to the survival rate P refers to Table A.2. According to the characteristics of uP, when P≥50%, take a negative value. A positive value is obtained when P < 50%. The fatigue life NP of the prescribed survival rate P. NP = lg-1xP (5) Note. If the user or product technical conditions require sample standard deviation correction or unilateral tolerance coefficient correction, or fatigue test factor F method for fatigue assessment For the life, refer to Appendix B, Appendix C and Appendix D for data processing. 8.3 Determination of fatigue strength 8.3.1 Overview of test methods The median fatigue strength at a predetermined number of cycles in the long-life zone and the fatigue strength of the prescribed survival rate were measured by the lift test method. 8.3.2 Number of samples Generally, about 15 pieces of effective samples are required. The number of samples required for each level of stress depends on the degree of dispersion of the test data. The required confidence γ is satisfied. 8.3.3 Determination of median fatigue strength The stress increment Δσ=σi 1-σi of the two adjacent stress levels of the lifting test method shall be the expected fatigue limit or median fatigue strength. 3% to 5%. The level of stress level depends on the magnitude of the stress increment and the degree of dispersion of the test data, and is generally 3 to 5 grades. The first thing The test stress level of the sample should be slightly higher than the expected fatigue limit or median fatigue strength, and then the test stress level of the sample depends on the previous test. Sample test results. Where the previous sample does not reach the specified number of cycles, the subsequent test will be at a lower level of stress. Under the next test; if the previous sample reaches the specified number of cycles without destruction, the subsequent test is carried out at a high level of stress level until the end Until all tests are completed. The test data before the first occurrence of the opposite result can be used once in subsequent tests. Median fatigue strength σ50. Σ50= N∑ i=1 Viσi (6) In the formula. n --- the total number of effective trials; m --- stress series; Σi --- the i-th stress level; Vi --- Number of tests for the i-th stress level. If the test requires the determination of the median fatigue strength and standard deviation, the data points of adjacent stress levels should be plotted as a break point (×) and An unbreaking point (○) is paired. If the lifting diagram is closed, all test points can be paired, and the median fatigue strength The estimated amount is calculated according to equation (7), and the results calculated by equations (7) and (6) are the same. Median fatigue strength σ50. Σ50= n*∑ m* i=1 V*iσ*i (7) In the formula. n*---the total number of pairs, that is, half of the number of samples n; m*---the number of pairs of pairs, that is, the number of stress levels m minus 1, ie m*=m-1; Σi*---the stress level of the pair (σi σi 1)/2; Vi*---the number of pairs of adjacent two levels. Standard deviat......Tips & Frequently Asked Questions:Question 1: How long will the true-PDF of GB/T 37616-2019_English be delivered?Answer: Upon your order, we will start to translate GB/T 37616-2019_English as soon as possible, and keep you informed of the progress. The lead time is typically 2 ~ 4 working days. The lengthier the document the longer the lead time.Question 2: Can I share the purchased PDF of GB/T 37616-2019_English with my colleagues?Answer: Yes. The purchased PDF of GB/T 37616-2019_English will be deemed to be sold to your employer/organization who actually pays for it, including your colleagues and your employer's intranet.Question 3: Does the price include tax/VAT?Answer: Yes. Our tax invoice, downloaded/delivered in 9 seconds, includes all tax/VAT and complies with 100+ countries' tax regulations (tax exempted in 100+ countries) -- See Avoidance of Double Taxation Agreements (DTAs): List of DTAs signed between Singapore and 100+ countriesQuestion 4: Do you accept my currency other than USD?Answer: Yes. If you need your currency to be printed on the invoice, please write an email to Sales@ChineseStandard.net. In 2 working-hours, we will create a special link for you to pay in any currencies. Otherwise, follow the normal steps: Add to Cart -- Checkout -- Select your currency to pay. |
