GB/T 26077-2021 English PDFUS$669.00 · In stock
Delivery: <= 6 days. True-PDF full-copy in English will be manually translated and delivered via email. GB/T 26077-2021: Metallic materials - Fatigue testing - Axial-strain-controlled method Status: Valid GB/T 26077: Historical versions
Basic dataStandard ID: GB/T 26077-2021 (GB/T26077-2021)Description (Translated English): Metallic materials - Fatigue testing - Axial-strain-controlled method Sector / Industry: National Standard (Recommended) Classification of Chinese Standard: H22 Word Count Estimation: 36,373 Issuing agency(ies): State Administration for Market Regulation, China National Standardization Administration GB/T 26077-2021: Metallic materials - Fatigue testing - Axial-strain-controlled method---This is a DRAFT version for illustration, not a final translation. Full copy of true-PDF in English version (including equations, symbols, images, flow-chart, tables, and figures etc.) will be manually/carefully translated upon your order.(Metallic materials Fatigue test Axial strain control method) ICS 77.040.10 CCSH22 National Standards of People's Republic of China Replace GB/T 26077-2010 Axial strain control method for fatigue test of metallic materials (ISO 12106.2017, MOD) Released on 2021-04-30 2021-11-01 implementation State Administration of Market Supervision and Administration Issued by the National Standardization Management Committee Table of contentsForeword Ⅲ Introduction Ⅴ 1 Scope 1 2 Normative references 1 3 Terms and definitions 1 4 Symbol 3 5 Test equipment 5 6 Sample 8 7 Test procedure 14 8 High temperature strain control creep-fatigue test 18 9 Result expression 19 10 Test report 21 Appendix A (informative) Uncertainty of measurement 25 Appendix B (Informative) Graphical representation example of test results 26 Reference 30 Axial strain control method for fatigue test of metallic materials1 ScopeThis document specifies the test equipment, specimens, test procedures, high temperature strain control creep Variable fatigue test, result expression and test report. This document is applicable to uniaxially loaded specimens with strain control and strain ratio Re=-1 under constant temperature and constant amplitude conditions. This document can also be used Instructs to conduct tests at other strain ratios Re, and to conduct tests at high temperatures where creep deformation may be active.2 Normative referencesThe contents of the following documents constitute the indispensable clauses of this document through normative references in the text. Among them, dated quotations Only the version corresponding to that date is applicable to this document; for undated reference documents, the latest version (including all amendments) is applicable to This document. GB/T 12160 Calibration of extensometer system for uniaxial testing of metallic materials (GB/T 12160-2019, ISO 9513.2012, IDT) GB/T 16825.1 Inspection of static uniaxial testing machine Part 1.Inspection and calibration of force measurement system of tensile and (or) compression testing machine Standard (GB/T 16825.1-2008, ISO 7500-1.2004, IDT) GB/T 25917.1 Uniaxial fatigue test system Part 1.Dynamic force calibration (GB/T 25917.1-2019, ISO 4965-1. 2012, IDT) GB/T 34104 Metal material testing machine loading coaxiality inspection (GB/T 34104-2017, ISO 23788.2012, MOD) JJF1637 Low-cost metal thermocouple calibration specification JJG141 Verification Regulation of Precious Metal Thermocouple for Work JJG556 Verification Regulations of Axial Force Fatigue Testing Machine JJG617 Verification Regulation of Digital Temperature Indicating Regulator3 Terms and definitionsThe following terms and definitions apply to this document. 3.1 Engineering stress The instantaneous force divided by the initial cross-sectional area within the gauge length. S=F/A0 Where. S ---Engineering stress; F --- instantaneous force; A0-the original cross-sectional area. 3.2 True stress The instantaneous force divided by the instantaneous cross-sectional area within the gauge length. σ=F/A or σ=S(1 e) Where. S---Engineering stress F/A0; e ---Engineering strain ΔL/L0. Note. When the strain is about 10%, the real stress is similar to the engineering stress F/A0.It is also important that when the strain is about 10%, the engineering strain is derived from the extension The meter actually measures and is the controlled parameter under test. 3.3 Initiallength Gaugelength L0 The initial length between the measuring points of the extensometer at the test temperature. 3.4 Parallel length Lp The length between the transition radii of the specimen. 3.5 Strain Engineering strain e= ΔL L0 = Li-L0 L0 Real total strain ε=∫ Li L0 dL Where. Li --- the instantaneous length of the gauge length part; L0---initial length or gauge length. Note. When the true strain value is about 10%, ε is approximate to engineering strain e=ΔL/L. It is also important that with a strain of about 10%, the engineering strain It is the quantity measured by the extensometer and the controlled parameter in the strain control fatigue test. 3.6 Cycle The smallest unit of cyclic repetition on the strain-time function. 3.7 Maximum The maximum algebraic value of a variable in a loop. 3.8 Minimum The smallest algebraic value of a variable in a loop. 3.9 Mean Half of the algebraic sum of the maximum and minimum values of the variable. 6.2 Preparation of test samples 6.2.1 General requirements The low-cycle fatigue test is designed to characterize the inherent characteristics of the material, and it is very important to prepare the sample in accordance with the following recommendations. If try The purpose of the test is to investigate the influence of some special factors (such as surface heat treatment, oxidation, etc.) without following the recommendations below. Under any condition, Any deviation should be noted in the test report. 6.2.2 Machining program If the test material needs heat treatment, it should be done before processing the sample. Machining may cause residual stress on the surface of the specimen, thereby Affect the test results. This stress is caused by the thermal gradient generated during the processing stage, and is related to the deformation of the material or the change of the microstructure. For high temperature tests, the effect of residual stress on the test results is not obvious, because part or all of the heat is released during the heat preservation process. Residual Stress. The selection of appropriate finishing process can reduce the residual stress of the sample. For hard materials, grinding should be given priority. Grinding. It is used within 0.1mm of the size of the finished product, and the feed amount does not exceed 0.005mm/time; Polishing. Use sandpaper with a gradually decreasing particle size to complete the polishing within 0.025mm of the finished product size. It is recommended to sample the sample in the final stage. Take longitudinal polishing. Note 1.Changes in the microstructure of the material. This phenomenon is caused by the temperature increase and strain hardening during the processing process, and it also causes phase transitions and surface recombination. The reason for the crystal. Its direct effect is to invalidate the test result, because the test material is no longer in its original state, and care should be taken to prevent it. Note 2.Pollutant intervention. certain elements or compounds may degrade the mechanical properties of a certain material, such as the presence of chlorine in steel or titanium alloys. So add The use of these elements should be avoided in the process (especially in the cutting emulsion). Attention should also be paid to the cleaning and degreasing process during the pre-storage of the sample. The problem. The processing technology used should be traceable and subsequently recorded in the test report. In addition, the position of each sample should be pointed out carefully. For placement and orientation, it is advisable to use an initial shape other than the bar or round bar as the test material. For example, forged, cast or additively manufactured products, which The above variables will affect the fatigue response. GB/T 2975 specifies the mechanical properties of steel profiles, bars, flats and pipes specified in ISO 6929 The identification, location and preparation requirements of test specimens and test pieces. In addition, GB/T 20832 specifies samples related to product characteristics Axis. 6.2.3 Sampling and marking Test materials sampled from semi-finished products or components may have a significant impact on the interpretation of the results obtained during the test. Therefore record The detailed information of the sample sampling site is necessary. A clear sampling plan should be attached to the test report. The sampling plan should include. ---The sampling location of each sample; --- Processing direction of semi-finished products (such as rolling direction, extrusion direction, etc.); ---Marking of each sample. The sample shall have a unique number during the processing of the sample. Any marking method can be used on the area that will not be processed away on the sample Marking should not affect the quality of the test. 6.2.4 Surface condition of the sample The surface condition of the sample will affect the test results. The impact is usually related to the following factors. ---The surface roughness of the sample; ---Residual Stress; --- Changes in the microstructure of the material; ---Involvement of pollutants. Follow the recommendations below to minimize the impact of the above factors. The surface quality of the sample is usually characterized by surface roughness. The importance of the surface roughness of the sample to the obtained test results is To a large extent is related to the test conditions, the surface corrosion or plastic deformation of the sample will reduce its influence. The average surface roughness of the sample should be less than 0.2μm (or the equivalent value of other parameters). Another important parameter different from the average surface roughness is the presence of local mechanical scratches. For the final work of round specimen processing The sequence is usually to remove all scratches in the circumferential direction caused by the lathe. The specimen should be polished longitudinally after grinding. At low power (approximately 20 times) check the sample, there should be no scratches along the circumferential direction and obvious processing marks. If the heat treatment is performed after the surface of the sample is processed, it is recommended to polish the surface of the sample after the heat treatment. If it can't be polished, It is advisable to conduct heat treatment in a vacuum environment or inert gas protection to avoid oxidation of the sample. It is recommended to remove the residual stress of the specimen. The heat treatment should not change the microstructure of the material being studied. The details of heat treatment and machining should be indicated in the test report. 6.2.5 Dimension check The size of the sample should be inspected after finishing finishing, and the inspection method used should not change the surface condition of the sample. 6.2.6 Storage and transportation After the sample is prepared, it should be stored to prevent any damage (contact scratches or oxidation, etc.). It is recommended to use a separate box or a tube with a cap Save the sample. In some cases, the sample should be stored in a vacuum bottle or a desiccator containing silica gel. The transportation of samples should be minimized. Special care should be taken when marking the sample. It is recommended to mark the specimen at both ends of the specimen, so that the half of the specimen can also be To be recognized.7 Test procedure7.1 Laboratory environment Low cycle fatigue and creep-fatigue test is a very complicated test. The quality of test results and selected test methods and laboratories The environment has a lot to do with it. The test should be carried out in the following suitable environment. ---Constant room temperature and relative humidity; ---Minimum air pollution (such as dust, chemical vapor, etc.); ---No external electrical signal interference that affects the control and data acquisition of the testing machine; ---Minimal external mechanical vibration. Note. When testing certain materials (such as aluminum alloy), it is extremely important to observe and record the relative humidity, because humidity has a significant impact on fatigue life. 7.2 Test machine control During the test, the peak strain of the servo control should not exceed ±1% of the set value. In the strain control test of long-life fatigue (i.e., the nominal cyclic plasticity is negligible, for example, about 106 to 107 cycles) strain control test, In order to shorten the test time, the test control mode can be switched, and the force control fatigue test can be carried out at a higher frequency. The fatigue that started in the strain control The labor test can obtain a stable stress-strain response. In this case, the cyclic plasticity is small and can be ignored. In this case, the test can be controlled The control mode is switched to the force control mode, and the test frequency should be increased cautiously, so as not to increase the sample temperature due to the hysteresis effect. Trying in conversion When testing the control mode, it is advisable to monitor the strain at any time and make adjustments in the force control mode to ensure that the strain is within the range of the maximum strain and the minimum strain. The limit deviation is within ±0.5%. When changing the test control mode, it is advisable to refer to GB/T 3075 for more information. In a creep fatigue test involving constant stress (force) in the cycle, the indicated peak value of the applied force should be kept within ±1% of the set value. 7.3 Installation of the sample When installing the specimen, try to avoid pre-strain. For the previously aligned test system, it is recommended to use displacement control to reduce the One end is clamped on the chuck, and the actuator is moved so that the other end of the sample touches the other chuck. Then keep the specimen small on the other end of the chuck Compression preload (force control) clamping. Next, set up the extensometer, when its output returns to zero, the strain control conversion can be carried out. Especially at high temperature In the test, the use of anti-adhesion compounds or pre-oxidation of the end of the sample can help remove the sample from the fixture. When the force is zero, it may The extensometer needs to be reset to zero. Set the gauge length of the extensometer and adjust it mechanically to zero. If necessary, it is recommended to use a mechanical zero adjustment device or use Adjust the gauge length with your fingers to make it as close to zero as possible (that is, within about ±0.5% of the test range). Once the “rough” zero position is obtained, build It is recommended to reset the electronic zero of the extensometer again. When handling samples that are susceptible to corrosive erosion, cotton or acrylic protective gloves should be worn. 7.4 Cycle Waveform-Strain Rate or Cycle Frequency In order to determine the trend of material properties, a strain ratio other than Re=-1 is usually used for strain control experiments. Figure 8 shows the The stress-strain hysteresis curve during the test when Re=0.As shown in Figure 8, for the average strain of this tension offset, the cycle of the average stress The ring relaxation tends to zero average stress value. In this case, it is recommended to carefully monitor and record such stress-strain and average stress information to Then carry out subsequent data analysis and determine material trends. When Re=∞, the hysteresis loop exhibits similar behavior, but under the opposite stress meaning In a sense, when the hysteresis loop moves upward in the stress-strain space, the stress relaxation tends to a smaller negative value. Note. Testing under the condition of Re=0.1 does not always prevent bifurcation buckling, because the cyclic average stress relaxation during the test may cause the hysteresis loop The lower part is compressed, as shown in the stress-strain response in Figure 8. Fig. 8 Stress-strain hysteresis loop from 0 to maximum strain test when Re=0 The waveform of the control parameter (strain) should remain unchanged during the test. The purpose of the test study is to study the effect of the cyclic waveform on the fatigue behavior of the material. Except for the impact test. The test is usually carried out with a constant total strain rate, in the range of 5×10-4s-1~5×10-2s-1 (0.05%s-1~ 5%s-1), which means a triangular loop shape. Generally, it can be used in the range of 0.01Hz~1Hz at room temperature Sine wave, but it is not recommended to perform at high temperature, because this will cause the strain rate to change. The creep-fatigue cycle usually consists of a constant total strain rate ramp, which is likely to be different in the tensile and compressive directions, and at the same time. The force and/or strain residence time ranges from a few minutes to tens of hours or even hundreds of hours. Chapter 8 explains this further. 7.5 Test procedure 7.5.1 Forecast At the beginning of the test, it is recommended to repeatedly apply cyclic force to the sample within the elastic range at room temperature to determine the elastic modulus of the material and confirm The correctness of the measurement system (force and strain). The deviation of the measured value of the elastic modulus from the expected value should not exceed ±5%. For the same test condition, it is recommended to increase the test temperature from room temperature to the test temperature by detecting the temperature (the force value is at zero in the force control mode of the testing machine) Point), the thermal strain of the extensometer measures the average thermal expansion coefficient of the material. The deviation of the measured value of this coefficient from the expected value should not exceed Over ±5%. Generally, the installation of the extensometer is carried out at room temperature, and the value of the extensometer is adjusted to zero when the test temperature is reached. In this case, at high The strain value measurement should be corrected in the temperature test, because the gauge length of the extensometer has been changed due to thermal expansion. Therefore, in the pre-test At least the thermal expansion value of the gauge length shall be recorded during the verification and correction. For automatic systems, the corrected gauge length should be used for online control and data collection. For some systems, especially when the test temperature exceeds 1000°C, the extensometer may be installed when the sample is in a hot state. In this case, Under circumstances, it is impossible to measure the coefficient of thermal expansion. At this time, the actual gauge length should be measured by a reliable method. If the fatigue test is performed at high temperature, it is recommended. a) Pre-compress the sample at room temperature, and the pre-compression is equal to the product of the metal linear expansion coefficient and the difference between the room temperature and the test temperature (that is, αΔT); b) Determine the gauge length at the test temperature; c) Set the extensometer to zero and compensate to the newly established gauge length under the test temperature in the test procedure. 7.5.2 Start test For a clear test procedure, it is necessary to choose the direction of the first quarter cycle. Tensile stress is usually selected; for induction heating In the low-cycle fatigue test, due to the effect of thermal induction, the compressive stress is the direction of the first quarter of the cycle. In the experiment of strain control, the usual procedure is to change the control mode from force value to strain after heating up and checking the elastic modulus. test The machine should complete this conversion without overshoot (that is, additional strain beyond the required strain level). Overshoot will affect subsequent test production Health impact. The difference between the actual half-width of the strain at the beginning of the t......Tips & Frequently Asked Questions:Question 1: How long will the true-PDF of GB/T 26077-2021_English be delivered?Answer: Upon your order, we will start to translate GB/T 26077-2021_English as soon as possible, and keep you informed of the progress. The lead time is typically 4 ~ 6 working days. The lengthier the document the longer the lead time.Question 2: Can I share the purchased PDF of GB/T 26077-2021_English with my colleagues?Answer: Yes. The purchased PDF of GB/T 26077-2021_English will be deemed to be sold to your employer/organization who actually pays for it, including your colleagues and your employer's intranet.Question 3: Does the price include tax/VAT?Answer: Yes. Our tax invoice, downloaded/delivered in 9 seconds, includes all tax/VAT and complies with 100+ countries' tax regulations (tax exempted in 100+ countries) -- See Avoidance of Double Taxation Agreements (DTAs): List of DTAs signed between Singapore and 100+ countriesQuestion 4: Do you accept my currency other than USD?Answer: Yes. If you need your currency to be printed on the invoice, please write an email to Sales@ChineseStandard.net. In 2 working-hours, we will create a special link for you to pay in any currencies. Otherwise, follow the normal steps: Add to Cart -- Checkout -- Select your currency to pay.Question 5: Should I purchase the latest version GB/T 26077-2021?Answer: Yes. Unless special scenarios such as technical constraints or academic study, you should always prioritize to purchase the latest version GB/T 26077-2021 even if the enforcement date is in future. Complying with the latest version means that, by default, it also complies with all the earlier versions, technically. |
