GB/T 23602-2009 English PDFUS$189.00 · In stock
Delivery: <= 3 days. True-PDF full-copy in English will be manually translated and delivered via email. GB/T 23602-2009: Methods of descaling and cleaning for titanium and titanium alloy surfaces Status: Valid
Basic dataStandard ID: GB/T 23602-2009 (GB/T23602-2009)Description (Translated English): Methods of descaling and cleaning for titanium and titanium alloy surfaces Sector / Industry: National Standard (Recommended) Classification of Chinese Standard: H14 Classification of International Standard: 77.120 Word Count Estimation: 8,80 Date of Issue: 2009-04-15 Date of Implementation: 2010-02-01 Adopted Standard: ASTM B600-1991 (2002), MOD Regulation (derived from): National Standard Approval Announcement 2009 No.5 (Total No.145) Issuing agency(ies): General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China, Standardization Administration of the People's Republic of China Summary: This standard specifies the method of descaling and cleaning the surface of titanium and titanium alloy products. This standard applies to the removal in the production of titanium and titanium alloy products, general use and thermal pollution generated in the process, oxide, dirt and surface contamination in the form of foreign matter. GB/T 23602-2009: Methods of descaling and cleaning for titanium and titanium alloy surfaces---This is a DRAFT version for illustration, not a final translation. Full copy of true-PDF in English version (including equations, symbols, images, flow-chart, tables, and figures etc.) will be manually/carefully translated upon your order.Methods of descaling and cleaning for titanium and titanium alloy surfaces ICS 77.120 H14 National Standards of People's Republic of China Titanium and titanium alloy surface descaling and cleaning methods Posted 2009-04-15 2010-02-01 implementation Administration of Quality Supervision, Inspection and Quarantine of People's Republic of China Standardization Administration of China released ForewordThis revised standard adopts ASTMB600.1991 (2002 Confirmafion) "Titanium and titanium alloy surface cleaning and descaling Standard Guide." For ease of use, this standard ASTMB600.1991 made the following changes. a) "The Guide" to the "standard"; b) delete the part of the range; c) the original standard Note 1 to Note 9 to Chapter 5, "Handling Precautions." The standard proposed by China Nonferrous Metals Industry Association. This standard Nonferrous Metals by the National Standardization Technical Committee. This standard was drafted. Baoji Titanium Group Ltd., Baoji Titanium Industry Co., Ltd. The main drafters of this standard. Huang Yongguang, Wang Yongmei, Ma Honghai, Wang Hongwu, Wang Weiqi, Fengjun Ning. Titanium and titanium alloy surface descaling and cleaning methods1 ScopeThis standard specifies the method of descaling and cleaning the surface of titanium and titanium alloy products. This standard applies to the removal of titanium and titanium alloy products are generally pollution generated in the production, use and heat treatment process, oxides, dirt and In the presence of surface contamination in the form of foreign matter.2 GeneralFor grease products titanium and titanium alloy machining, casting and pressure processing of used oils and lubricants, recommended base or milk The immersion-type alkaline cleaning agents and electrolytic cleaning system. In electrolysis, the workpiece may be an anode, a cathode may be. These should be the removal of dirt Before pickling heat treatment or prescribed conduct 4.2. When electrolysis voltage should be controlled to prevent spark discharge, resulting in products table Surface pits appear.3 Impact Cleaning3.1 mechanical descaling such as sand blasting, shot peening, steam shower and other methods to clear the surface of the titanium material and thermal processing scales skin lubricant, but then should be used Chapter 4 of the cleaning. 3.2 sand blasting should be used for high-quality, cleaned, iron-free silica sand. 3.3 If the entire surface of the product using the blast method to clean the exposed surface due to grit or sand pill roughened. To ensure the surface finish Degree should be the preferred local cleaning and pickling with appropriate cleaning. 3.4 grit or sand containing iron proceeds blast cleaning the surface of the titanium material, pickling method should be used to remove embedded surface after blast Steel particles. 3.5 abrasive blasting or are likely to cause the titanium surface residual compressive stress, and cause local deformation should be used or chemical milling wheel Profile machining processing. 3.6 Under normal circumstances, the sand and can not replace pickling. Grinding contaminated layer can not be removed by the interstitial elements (such as carbon, oxygen and nitrogen) cause. When these elements are present in excess, according to the provisions of 4.3 for the elimination of pickling.4 pickling and descaling4.1 In addition to the recommended quick sand blasting or grinding method for processing titanium material surface, for the guarantee complete removal of metallic iron, oxides, and other scaly skin table Surface contamination, 4.3.2 shall also be pickled. If chemical milling to remove the surface oxide product contaminated layer, or the product is not conducive to the overall appearance When sandblasting, salt treatment can be used to prevent surface localized corrosion. 4.2 For scaly and residual lubricant titanium rolling, casting, forging or assembly formed before pickling 4.3.2 regulations, may Using one of the following methods may be treated to completely remove surface contamination. 4.2.1 All corrosion based solution recommended by the manufacturer requirements mixed with tap water. 4.2.2 base molten salt bath according to the procedure laid carried out at 399 ℃ ~ 454 ℃. 4.2.3 base molten salt bath according to the procedure laid carried out at 204 ℃. Oxide and oxide colors 4.2.4 below 593 ℃ heat generated can be used pickling clear. Acid ratio (by volume). 10% - 20% (150g/L ~ 300g/L) of nitric acid (70%) + 1% ~ 2% (12g/L ~ 24g/L) hydrofluoric acid (60%) + water temperature of 49 ℃. 4.2.5 forging and heat-treating with graphite or titanium are usually formed by mixing glass lubricant heat scaly, scaly skin this heat can melt in the 454 ℃ The base was completely dissolved in a salt bath. Then the provisions of 4.3.2 may then be pickled. 4.2.6 can be heat-treated α + β titanium and titanium alloys β solution treatment at above 593 ℃ generated containing graphite and molybdenum disulfide lubricant ......Tips & Frequently Asked Questions:Question 1: How long will the true-PDF of GB/T 23602-2009_English be delivered?Answer: Upon your order, we will start to translate GB/T 23602-2009_English as soon as possible, and keep you informed of the progress. The lead time is typically 1 ~ 3 working days. The lengthier the document the longer the lead time.Question 2: Can I share the purchased PDF of GB/T 23602-2009_English with my colleagues?Answer: Yes. The purchased PDF of GB/T 23602-2009_English will be deemed to be sold to your employer/organization who actually pays for it, including your colleagues and your employer's intranet.Question 3: Does the price include tax/VAT?Answer: Yes. Our tax invoice, downloaded/delivered in 9 seconds, includes all tax/VAT and complies with 100+ countries' tax regulations (tax exempted in 100+ countries) -- See Avoidance of Double Taxation Agreements (DTAs): List of DTAs signed between Singapore and 100+ countriesQuestion 4: Do you accept my currency other than USD?Answer: Yes. If you need your currency to be printed on the invoice, please write an email to Sales@ChineseStandard.net. In 2 working-hours, we will create a special link for you to pay in any currencies. Otherwise, follow the normal steps: Add to Cart -- Checkout -- Select your currency to pay. |