HOME   Cart   Quotation   About-Us Tax PDFs Standard-List
Powered by Google-Search & Google-Books www.ChineseStandard.net Database: 189760 (24 Sep 2022)

GB/T 3903.14-2021 (GBT 3903.14-2021)

Chinese standards (related to): 'GB/T 3903.14-2021'
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)See DetailStatusGoogle Book
GB/T 3903.14-2021English115 Add to Cart 0--3 minutes. Auto immediate delivery. Footwear -- Test methods for outsoles -- Needle tear strength GB/T 3903.14-2021 Valid GBT 3903.14-2021
GB/T 3903.1-2017English80 Add to Cart 0--3 minutes. Auto immediate delivery. Footwear -- Test methods for whole shoe -- Flexing resistance GB/T 3903.1-2017 Valid GBT 3903.1-2017
GB/T 3903.1-2008English170 Add to Cart 0--3 minutes. Auto immediate delivery. Footwear -- General test methods -- Flexing resistance GB/T 3903.1-2008 Obsolete GBT 3903.1-2008
GB/T 3903.14-2005English139 Add to Cart 3 days Footwear -- Test methods for outsoles -- Needle tear strength GB/T 3903.14-2005 Valid GBT 3903.14-2005
GB/T 3903.1-1994English199 Add to Cart 2 days General test method for footwear-Test method of flexing resistance GB/T 3903.1-1994 Obsolete GBT 3903.1-1994
GB 3903-1983English199 Add to Cart 2 days Test method for peeling strength of leather shoes GB 3903-1983 Obsolete GB 3903-1983


   
BASIC DATA
Standard ID GB/T 3903.14-2021 (GB/T3903.14-2021)
Description (Translated English) Footwear -- Test methods for outsoles -- Needle tear strength
Sector / Industry National Standard (Recommended)
Classification of Chinese Standard Y78
Classification of International Standard 61.060
Word Count Estimation 5,579
Date of Issue 2021-10-11
Date of Implementation 2022-05-01
Older Standard (superseded by this standard) GB/T 3903.14-2005
Drafting Organization Dezhou Xinhuarun Technology Co., Ltd., China Leather and Shoe Research Institute Co., Ltd., Pony Testing Group Co., Ltd., Anta (China) Co., Ltd., China Light Inspection and Certification (Wenling) Co., Ltd., Quanzhou Vocational College of Light Industry
Administrative Organization National Shoemaking Standardization Technical Committee (SAC/TC 305)
Proposing organization China National Light Industry Council
Issuing agency(ies) State Administration for Market Regulation, National Standardization Administration


GB/T 3903.14-2021: PDF in English (GBT 3903.14-2021)
GB/T 3903.14-2021
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 61.060
CCS Y 78
GB/T 3903.14-2021 / ISO 20874:2018
Replacing GB/T 3903.14-2005
Footwear - Test methods for outsoles - Needle tear strength
(ISO 20874:2018, IDT)
ISSUED ON: OCTOBER 11, 2021
IMPLEMENTED ON: MAY 01, 2022
Issued by: State Administration for Market Regulation;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword ... 3 
1 Scope ... 5 
2 Normative references ... 5 
3 Terms and definitions... 5 
4 Test equipment and materials ... 6 
5 Sampling and conditioning ... 7 
6 Test methods ... 8 
7 Test results ... 8 
8 Test report ... 8 
Footwear - Test methods for outsoles - Needle tear strength
1 Scope
This document describes methods for determining the needle tear strength of footwear
outsoles materials.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this
document and are indispensable for its application. For dated references, only the
version corresponding to that date is applicable to this document; for undated references,
the latest version (including all amendments) is applicable to this document.
ISO 7500-1 Metallic materials - Calibration and verification of static uniaxial testing
machines - Part 1: Tension/compression testing machines - Calibration and
verification of the force-measuring system
ISO 17709 Footwear - Sampling location, preparation and duration of conditioning
of samples and test pieces
ISO 18454 Footwear - Standard atmospheres for conditioning and testing of
footwear and components for footwear
3 Terms and definitions
The following terms and definitions are applicable to this document.
The addresses of terminology databases maintained by ISO and IEC for standardization
are as follows:
-- ISO online browsing platform: https://www.iso.org/obp
-- IEC electronics development platform: http://www.electropedia.org/
3.1
needle tear strength
Divide the maximum force required to tear the material by the needle, by the thickness
of the sample, to gain the needle tear strength.
2 – steel needle (ϕ1 mm);
3 – sample;
a – thickness.
Figure 1 – Example of clamps
4.4 Thickness gauge
The thickness gauge shall have a firm base, and its presser foot shall have a constant
weight load, which can be applied with a pressure of 10 kPa ± 3 kPa. The presser foot
of the thickness gauge shall be a circular plane whose diameter is 10 mm ± 0.1 mm.
The meter scale is 0.01 mm.
5 Sampling and conditioning
Take samples in accordance with ISO 17709. Before testing, all samples shall be
subjected to conditioning for at least 24 h according to ISO 18454.
The sample is a long strip with a length of 50 mm ± 1 mm and a width of 20 mm ± 1
mm. The sample thickness shall preferably be:
-- 2.0 mm ± 0.2 mm for polymer and elastic material solid core outsoles;
-- 4.0 mm ± 0.2 mm for semi-foamed and foamed outsoles;
-- original outsoles thickness for leather outsoles.
Note: Take at least 3 points of equidistant distance from the center line parallel to the
long side of the sample to measure the thickness of the sample; take the average
value.
Take at least 3 samples for testing. Use a suitable peeling machine to process the sample
to uniform thickness. If feasible, the smooth original "skin" of the sample shall remain
intact. The samples can be thus divided into the following 3 types:
-- There are 2 original "skins", S2;
-- There is 1 original "skin", S1;
-- There is no original "skin", S0;
The final results shall be based on the same type of samples, the sample type shall be
recorded in the report.
GB/T 3903.14-2021
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 61.060
CCS Y 78
GB/T 3903.14-2021 / ISO 20874.2018
Replacing GB/T 3903.14-2005
Footwear - Test methods for outsoles - Needle tear strength
(ISO 20874.2018, IDT)
ISSUED ON. OCTOBER 11, 2021
IMPLEMENTED ON. MAY 01, 2022
Issued by. State Administration for Market Regulation;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword... 3 
1 Scope... 5 
2 Normative references... 5 
3 Terms and definitions... 5 
4 Test equipment and materials... 6 
5 Sampling and conditioning... 7 
6 Test methods... 8 
7 Test results... 8 
8 Test report... 8 
Footwear - Test methods for outsoles - Needle tear strength
1 Scope
This document describes methods for determining the needle tear strength of footwear
outsoles materials.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this
document and are indispensable for its application. For dated references, only the
version corresponding to that date is applicable to this document; for undated references,
the latest version (including all amendments) is applicable to this document.
ISO 7500-1 Metallic materials - Calibration and verification of static uniaxial testing
machines - Part 1.Tension/compression testing machines - Calibration and
verification of the force-measuring system
ISO 17709 Footwear - Sampling location, preparation and duration of conditioning
of samples and test pieces
ISO 18454 Footwear - Standard atmospheres for conditioning and testing of
footwear and components for footwear
3 Terms and definitions
The following terms and definitions are applicable to this document.
The addresses of terminology databases maintained by ISO and IEC for standardization
are as follows.
3.1
needle tear strength
Divide the maximum force required to tear the material by the needle, by the thickness
of the sample, to gain the needle tear strength.
2 – steel needle (ϕ1 mm);
3 – sample;
a – thickness.
Figure 1 – Example of clamps
4.4 Thickness gauge
The thickness gauge shall have a firm base, and its presser foot shall have a constant
weight load, which can be applied with a pressure of 10 kPa ± 3 kPa. The presser foot
of the thickness gauge shall be a circular plane whose diameter is 10 mm ± 0.1 mm.
The meter scale is 0.01 mm.
5 Sampling and conditioning
Take samples in accordance with ISO 17709.Before testing, all samples shall be
subjected to conditioning for at least 24 h according to ISO 18454.
The sample is a long strip with a length of 50 mm ± 1 mm and a width of 20 mm ± 1
mm. The sample thickness shall preferably be.
-- 2.0 mm ± 0.2 mm for polymer and elastic material solid core outsoles;
-- 4.0 mm ± 0.2 mm for semi-foamed and foamed outsoles;
-- original outsoles thickness for leather outsoles.
Note. Take at least 3 points of equidistant distance from the center line parallel to the
long side of the sample to measure the thickness of the sample; take the average
value.
Take at least 3 samples for testing. Use a suitable peeling machine to process the sample
to uniform thickness. If feasible, the smooth original "skin" of the sample shall remain
intact. The samples can be thus divided into the following 3 types.
-- There are 2 original "skins", S2;
-- There is 1 original "skin", S1;
-- There is no original "skin", S0;
The final results shall be based on the same type of samples, the sample type shall be
recorded in the report.
......