Powered by Google www.ChineseStandard.net Database: 189759 (16 Jun 2024)

GB/T 37622-2019 related PDF English

GB/T 37622-2019 (GB/T37622-2019, GBT 37622-2019, GBT37622-2019) & related versions
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)See DetailStatusSimilar PDF
GB/T 37622-2019English150 Add to Cart 0-9 seconds. Auto delivery. Hot rolled steel bar of fire resistant for the reinforcement of concrete GB/T 37622-2019 Valid GBT 37622-2019
Buy with any currencies (Euro, JPY, KRW...): GB/T 37622-2019    Preview this PDF: GB/T 37622-2019



GB/T 37622-2019: PDF in English (GBT 37622-2019)
GB/T 37622-2019
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.140.60
H 44
Hot Rolled Steel Bar of Fire
Resistant for the Reinforcement of Concrete
ISSUED ON: JUNE 04, 2019
IMPLEMENTED ON: MAY 01, 2020
Issued by: State Administration for Market Regulation;
Standardization Administration of PRC.
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Normative References ... 4
3 Terms and Definitions ... 6
4 Classification and Designation ... 6
5 Ordering Content ... 7
6 Size, Shape, Weight and Allowable Deviation ... 7
7 Technical Requirements ... 7
8 Test Methods ... 10
9 Inspection Rules ... 13
10 Package, Marking and Quality Certificate ... 14
Appendix A (Normative) Characteristic-Value Inspection Rules ... 15
Bibliography ... 17
Hot Rolled Steel Bar of Fire
Resistant for the Reinforcement of Concrete
1 Scope
This Standard specifies the classification, designation, ordering content, size, shape,
weight and allowable deviation, technical requirements, test methods, inspection rules,
package, marking and quality certificate, etc. of hot rolled steel bar of fire resistant for
the reinforcement of concrete.
This Standard is applicable to the hot rolled plain bars of fire-resistant and hot rolled
ribbed bars of fire-resistant (hereinafter referred to as steel bar).
2 Normative References
The following documents are essential to the application of this document. For the
dated documents, only the versions with the dates indicated are applicable to this
document; for the undated documents, only the latest version (including all the
amendments) are applicable to this document.
GB/T 222 Permissible Tolerances for Chemical Composition of Steel Products
GB/T 223.5 Steel and Iron - Determination of Acid-Soluble Silicon and Total Silicon
Content - Reduced Molybdosilicate Spectrophotometric Method
GB/T 223.11 Iron, Steel and Alloy - Determination of Chromium Content - Visual
Titration or Potentiometric Titration Method
GB/T 223.12 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium
Carbonate Separation-Diphenyl Carbazide Photometric Method for the
Determination of Chromium Content
GB/T 223.14 Methods for Chemical Analysis of Iron, Steel and Alloy - The N-
Benzoy-N-Phenylhydroxylamine Extraction Photometric Method for the
Determination of Vanadium Content
GB/T 223.19 Methods for Chemical Analysis of Iron, Steel and Alloy - The
Neocuproine-Chloroform Extraction Photometric Method for the Determination of
Copper Content
GB/T 223.23 Iron, Steel and Alloy - Determination of Nickel Content - The
Dimethylglyoxime Spectrophotometric Method
GB/T 223.26 Iron, Steel and Alloy - Determination of Molybdenum Content - The
Thiocyanate Spectrophotometric Method
GB/T 223.37 Methods for Chemical Analysis of Iron, Steel and Alloy - the
Indophenol Blue Photometric Method for the Determination of Nitrogen Content
after Distillation Separation
GB/T 223.40 Iron, Steel and Alloy - Determination of Niobium Content by the
Sulphochlorophenol S Spectrophotometric Method
GB/T 223.59 Iron, Steel and Alloy - Determination of Phosphorus Content -
Bismuth Phosphomolybdate Blue Spectrophotometric Method and Antimony
Phosphomolybdate Blue Spectrophotometric Method
GB/T 223.63 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium
(Potassium) Periodate Photometric Method for the Determination of Manganese
Content
GB/T 223.85 Iron, Steel and Alloy - Determination of Sulfur Content - Infrared
Absorption Method after Combustion in an Induction Furnace
GB/T 223.86 Iron, Steel and Alloy - Determination of Total Carbon Content -
Infrared Absorption Method after Combustion in an Induction Furnace
GB/T 228.2 Metallic Materials - Tensile Testing - Part 2: Method of Test at Elevated
Temperature
GB/T 1499.1 Steel for the Reinforcement of Concrete - Part 1: Hot Rolled Plain
Bars
GB/T 1499.2 Steel for the Reinforcement of Concrete - Part 2: Hot Rolled Ribbed
Bars
GB/T 2101 General Requirement of Acceptance Packaging Marking and
Certification for Section Steel
GB/T 4336 Carbon and Low-Alloy Steel - Determination of Multi-Element Contents
-Spark Discharge Atomic Emission Spectrometric Method (Routine Method)
GB/T 17505 Steel and Steel Products - General Technical Delivery Requirements
GB/T 20066 Steel and Iron - Sampling and Preparation of Samples for the
Determination of Chemical Composition
5 Ordering Content
The contract that orders products as per this Standard shall contain the following
contents:
a) This Standard number;
b) Product name;
c) Designation of steel bar;
d) Nominal diameter, length and weight of steel bar (or quantity, or disc weight);
e) Special requirements.
6 Size, Shape, Weight and Allowable Deviation
The size, shape, weight and allowable deviation of plain bars shall conform to the
provisions of GB/T 1499.1; while the size, shape, weight and allowable deviation of
ribbed bars shall conform to the provisions of GB/T 1499.2.
7 Technical Requirements
7.1 Smelting method
The steel shall be smelted in a converter or an electric arc furnace; and may be refining
outside the furnace, if necessary.
7.2 Designation chemical composition
7.2.1 The designation, chemical composition and carbon equivalent (smelting analysis)
of steel bars shall conform to the provisions of Table 2.
Table 2
Designation
Chemical composition (mass fraction) / %
Carbon equivalent
Ceq / %
Welding Mechanical connection
The rounding off and judgment for values of inspection results shall conform to the
provisions of YB/T 081.
9 Inspection Rules
9.1 Inspection classification
The inspection of steel bar can be divided into characteristic-value inspection and
delivery inspection.
9.2 Characteristic-value inspection
9.2.1 The Characteristic-value inspection is applicable to the following cases:
a) Supplier’s inspection on the product quality control;
b) Inspection proposed by purchaser, and agreed between the supplier and the
purchaser;
c) Inspection for the third-party product certification and arbitration.
9.2.2 The characteristic-value inspection shall be carried out as per the provisions of
Appendix A.
9.3 Delivery inspection
9.3.1 Applicable cases
The delivery inspection is applicable to the inspection on the acceptance batch of steel
bars.
9.3.2 Batching rules
The steel bars shall be inspected and accepted in batches. Each batch consists of the
steel bars with the same designation, the same furnace-number, the same
specification. The weight per batch is usually no greater than 60t. For the portion
exceeding 60t, add a tensile test specimen and a bending test specimen for increasing
per 40t (or remainder for less than 40t).
9.3.3 Inspection items and sampling quantity
The inspection items and sampling quantity of steel bars shall conform to the
provisions of Table 6 and 9.3.2.
9.3.4 Inspection results
Appendix A
(Normative)
Characteristic-Value Inspection Rules
A.1 Test batches and sampling quantities
A.1.1 Test batches
For the benefit of test, the delivery shall be further divided into test batches. The
batching rules shall conform to the provisions of 9.3.2.
A.1.2 Sampling quantities per batch
A.1.2.1 The chemical compositions (finished-product analysis) shall take two
specimens from different pieces of steel bars.
A.1.2.2 The mechanical property test, and the like tests shall take 15 specimens from
different pieces of steel bars (if 60 specimens are applicable, see provisions of A.2.1).
A.2 Assessment of test results
A.2.1 Parameter inspection
In order to inspect the specified properties, such as characteristic parameters ReL, Rm,
Agt or A, the following parameters shall be determined:
a) All individual values of Xi (n=15) for 15 specimens;
b) Average value m15 (n=15);
c) Standard deviation S15 (n=15).
If all properties satisfy the conditions given in Formula (A.1), then such test batch meet
the requirements.
Where:
fk – the required characteristic-value;
2.33 – if n=15, 90% confidence level (1-a = 0.90), the unqualified rate 5% (P=0.95),
then it indicates the value of acceptance coefficient k.
......

BASIC DATA
Standard ID GB/T 37622-2019 (GB/T37622-2019)
Description (Translated English) Hot rolled steel bar of fire resistant for the reinforcement of concrete
Sector / Industry National Standard (Recommended)
Classification of Chinese Standard H44
Classification of International Standard 77.140.60
Word Count Estimation 14,195
Date of Issue 2019-06-04
Date of Implementation 2020-05-01
Drafting Organization Yancheng Lianxin Iron and Steel Co., Ltd., Guangxi Shenglong Metallurgical Co., Ltd., Gangyan Shenghua Technology Co., Ltd., Fujian Sangang Minguang Co., Ltd., Jiangsu Yonggang Group Co., Ltd., Shiheng Special Steel Group Co., Ltd., Jiangsu Province Binxin Iron and Steel Group Co., Ltd., Luoyang Luoyang Iron and Steel Group Iron and Steel Co., Ltd., Jiangsu Xugang Iron and Steel Group Co., Ltd., Jiangxi Taixin Iron and Steel Co., Ltd., Tangshan Delong Iron and Steel Co., Ltd., Yangchun New Iron and Steel Co., Ltd., Beijing University of Science and Technology, Metallurgical Industrial Information Standards Institute
Administrative Organization National Steel Standardization Technical Committee (SAC/TC 183)
Proposing organization China Iron and Steel Association
Issuing agency(ies) State Administration for Market Regulation, China National Standardization Administration