YS/T 1075.3-2015 (YS/T1075.3-2015, YST 1075.3-2015, YST1075.3-2015)
| Standard ID | Contents [version] | USD | STEP2 | [PDF] delivered in | Standard Title (Description) | Status | PDF |
| YS/T 1075.3-2015 | English | 139 |
Add to Cart
|
3 days [Need to translate]
|
Methods for chemical analysis of vanadium-aluminium and molybdenum-aluminium master alloys - Part 3: Determination of silicon content - Molydenum blue spectrophotometry
| Valid |
YS/T 1075.3-2015
|
Standards related to: YS/T 1075.3-2015
| Standard ID | YS/T 1075.3-2015 (YS/T1075.3-2015) | | Description (Translated English) | Methods for chemical analysis of vanadium-aluminium and molybdenum-aluminium master alloys. Part 3: Determination of silicon content. Molydenuin blue spectrophotometry | | Sector / Industry | Nonferrous Metallurgy Industry Standard (Recommended) | | Classification of Chinese Standard | H14 | | Classification of International Standard | 77.120.99 | | Word Count Estimation | 6,645 | | Date of Issue | 2015-04-30 | | Date of Implementation | 2015-10-01 | | Drafting Organization | Northwest Nonferrous Metal Research Institute; Baoji Titanium Group Limited; Guangzhou Institute of Nonferrous Metals; Chengde Vanadium big industry limited liability company; Shangluo Amano Advanced Materials Co., Ltd.; Powder Metallurgy Research Institute, Central South University; Donggang East hi-Metal Materials Co., | | Administrative Organization | National Non-Ferrous Metals Standardization Technical Committee (SAC/TC 243) | | Regulation (derived from) | Ministry of Industry and Information Technology Announcement (2015 No. 28) | | Proposing organization | National Non-Ferrous Metals Standardization Technical Committee (SAC/TC 243) | | Issuing agency(ies) | Ministry of Industry and Information Technology of the People's Republic of China | | Summary | This Standard specifies the aluminum vanadium, molybdenum determination of aluminum alloy with silicon content. This Standard applies to aluminum vanadium, molybdenum determination of silicon content aluminum alloy with. Measurement range: 0.010 to 0.50%. | YS/T 1075.3-2015
(Vanadium aluminum, molybdenum intermediate aluminum alloys - Part 3. Determination of silicon content - Molybdenum blue spectrophotometric method)
ICS 77.120.99
H14
People's Republic of China Nonferrous Metals Industry Standard
Aluminum vanadium, molybdenum intermediate aluminum alloys -
Part 3. Determination of the amount of silicon
Molybdenum blue spectrophotometric method
Part 3. Determinationofsiliconcontent-
Issued on. 2015-04-30
2015-10-01 implementation
Ministry of Industry and Information Technology of the People's Republic of China released
Foreword
YS/T 1075 "aluminum vanadium, molybdenum intermediate aluminum alloy chemical analysis method" including a total of 8 sections.
--- Part 1. Determination of iron content - 1,10-phenanthroline spectrophotometry;
--- Part 2. Determination of molybdenum content of lead molybdate gravimetric method;
--- Part 3. Determination of silicon content - Molybdenum blue spectrophotometric method;
--- Part 4. vanadium content - Inductively coupled plasma atomic emission spectrometry and ferrous ammonium sulfate titration;
--- Part 5. Determination of aluminum content EDTA titration;
--- Part 6. Determination of carbon content in the high-frequency combustion - infrared absorption method;
--- Part 7. Determination of the amount of oxygen in the inert gas fusion - infrared method;
--- Part 8. molybdenum, aluminum X- determining the amount of fluorescence spectroscopy.
This section YS/T 1075 Part 3.
This section drafted in accordance with GB/T 1.1-2009 given rules.
The non-ferrous metal part by the National Standardization Technical Committee (SAC/TC243) and focal points.
This section is drafted. Northwest Nonferrous Metal Research Institute, Baoji Titanium Group Limited, the Guangzhou Research Institute of Nonferrous Metals, Chengde Vanadium has big
Limited liability company Shangluo Amano Advanced Materials Co., Ltd., Central South University Institute of powder metallurgy, high-tech metal materials East Limited Donggang
the company.
The main drafters of this section. Sunbao Lian, Wang Jinlei Rowling, Li Bo, Liu Ting, HUANG Yong, Zhang Jin, Li Jianxin, Chen Aili, Mai Libi,
Zheng Lina, Wang Yonghong, Lizhi De, single Lihua, Wang Wan, Zheng Lingzhi, Tan Zhaohui.
Aluminum vanadium, molybdenum intermediate aluminum alloys -
Part 3. Determination of the amount of silicon
Molybdenum blue spectrophotometric method
1 Scope
YS/T 1075 This section provides the aluminum vanadium, molybdenum determination of aluminum alloy with silicon content.
This section applies to aluminum vanadium, molybdenum determination of silicon content aluminum alloy with. Measurement range. 0.010% to 0.50%.
2 Method summary
Sample of nitric acid, hydrofluoric acid dissolution. Masked with boric acid fluoride, under certain acidity, ammonium molybdate added to silicon to form a silicon molybdenum yellow, join
Grass sulfuric acid mixture to improve the acidity and eliminate phosphorus, arsenic interference with ascorbic acid will be reduced to silicon silicon molybdenum yellow and molybdenum blue at 800nm wavelength spectrophotometer
Measured absorbance.
3 Reagents
3.1 nitric acid (12).
3.2 Hydrofluoric acid (ρ = 1.15g/mL).
3.3 saturated boric acid solution.
3.4 ammonium molybdate solution (50g/L).
3.5 oxalic acid - sulfuric acid mixture. Weigh 25g oxalic acid was added 300mL of water, stirring slowly added 100mL sulfuric acid (ρ = 1.84g/mL),
After dissolution, add water to 1000mL volume, mix, cool to room temperature.
3.6 ascorbic acid solution (20g/L), the time is now equipped with.
3.7 silicon standard stock solution. Weigh 2.1393g silica (wSiO2≥99.95%) (after 1000 ℃ high temperature burn 20min, and dry
Desiccator cooled to ambient temperature) was placed in a platinum crucible, 10g of a mixed flux of sodium and potassium carbonate (21), and mix. Placed 950 ℃ high
Temperature melting furnace to clear and transparent. Remove the cooling, hot water and slowly heated to the leaching solution clear. Remove cooled and transferred to 1000mL capacity
Dilution bottle with water to volume, and mix. Now moved to a polyethylene bottle. This solution 1mL containing 1.0mg silicon.
3.8 Silicon standard solution. Pipette 10.00mL silicon standard stock solution (3.7) in 1000mL volumetric flask, dilute with water to volume, and mix.
Now moved to a polyethylene bottle. This solution 1mL containing 10μg silicon.
4 Instrument
Spectrophotometer.
5 Sample
The specimen shall crush a particle size less than 500μm.
...
|