YS/T 1050.7-2015 (YST1050.7-2015)

Standard ID	Contents [version]	USD	STEP2	[PDF] delivered in	Standard Title (Description)	Related Standard	Status	PDF
YS/T 1050.7-2015	English	139	Add to Cart	3 days [Need to translate]	Methods for chemical analysis of lead antimony concentrates - Part 7: Determination of bismuth and copper contents - Flame atomic absorption spectrometric method	YS/T 1050.7-2015	Valid	YS/T 1050.7-2015

YS/T 1050.7-2015
(Lead-antimony concentrates - Part 7. Determination of the amount of bismuth and copper - Flame atomic absorption spectrometric method)
ICS 73.060
D42
People's Republic of China Nonferrous Metals Industry Standard
Methods for chemical analysis of lead-antimony concentrate
Part 7. the amount of bismuth and copper contents -
Flame Atomic Absorption Spectrometry
Part 7. Determinationofbismuthandcoppercontents-
Issued on. 2015-04-30
2015-10-01 implementation
Ministry of Industry and Information Technology of the People's Republic of China released
Foreword
YS/T 1050-2015 "Methods for chemical analysis of lead-antimony concentrate" is divided into the following nine sections.
--- Part 1. Determination of lead content Na2EDTA titration;
--- Part 2. Determination of antimony content cerium sulfate titration;
--- Part 3. Determination of arsenic content potassium bromate titration;
--- Part 4. Determination of zinc contents Na2EDTA titration;
--- Part 5. Determination of sulfur content - Gravimetric method;
--- Part 6. Determination of iron content cerium sulfate titration;
--- Part 7. Determination of the amount of bismuth and copper - Flame atomic absorption spectrometry amount;
--- Part 8. gold and silver content determination fire assay;
--- Part 9. Determination of the amount of silver by flame atomic absorption spectrometry.
This is Part 7.
This section drafted in accordance with GB/T 1.1-2009 given rules.
The non-ferrous metal part by the National Standardization Technical Committee (SAC/TC243) centralized.
This section is responsible for drafting unit. Guangxi Metallurgical Product Quality Supervision and Inspection Station.
This section is drafted. Guilin University of Technology.
Participated in the drafting of this section. Beijing Mining Research Institute, Guangxi Zhuang Autonomous Region Analysis and Testing Center, Liuzhou one hundred Ren special advanced material
Material Limited.
The main drafters of this section. Zhou Sulian, Huangzhao Min, Huang He, Zhang Chen, Zhang, Lin Dongdong, Huang Xusheng, Zhang Hongyun, Zhang Lin, Wei Lili,
Juan, Gan Day Star.
Methods for chemical analysis of lead-antimony concentrate
Part 7. the amount of bismuth and copper contents -
Flame Atomic Absorption Spectrometry
1 Scope
This section YS/T 1050 specifies the method for measuring the amount of bismuth in lead-antimony concentrate and copper content.
This section applies to the determination of the amount of bismuth in the lead-antimony concentrate and copper content of the measurement range (mass fraction) of 0.015% to 1.00% bismuth, copper
From 0.15% to 1.00%.
2 Method summary
Sample with nitric acid, potassium chlorate and sulfuric acid decomposition in hydrochloric acid medium, with air - acetylene flame atomic absorption spectrometer wavelength 223.1nm
And 324.8nm at bismuth and copper were measured absorbance to the standard curve method to calculate the amount of bismuth and copper content.
3 Reagents
Unless otherwise indicated, this part of the reagents were analytical reagent, the water for the two water.
3.1 potassium chlorate.
3.2 hydrochloric acid (ρ = 1.19g/mL).
3.3 nitric acid (ρ = 1.42g/mL).
3.4 sulfate (ρ = 1.84g/mL).
Hydrochloride 3.5 (6100).
3.6 nitric acid (11).
3.7 tartaric acid solution (100g/L).
3.8 copper standard stock solution. Weigh 0.2500g copper (mass fraction ≥99.99%) placed in 250mL beaker, add 20mL nitrate
Acid (3.6), cover the surface of the pan, over low heat until completely dissolved, remove, cool. The solution is transferred to 250mL volumetric flask, constant volume of water, mixed
uniform. This copper-containing solution 1mL 1mg.
3.9 bismuth standard stock solution. Weigh 0.2500g bismuth (mass fraction ≥99.99%) placed in 250mL beaker, add 20mL nitrate
Acid (3.6), cover the surface of the pan, over low heat until completely dissolved, remove, cool. The solution is transferred to 250mL volumetric flask, add 25mL nitrate
Acid (3.3) with water to volume, and mix. This solution 1mL bismuth-containing 1mg.
3.10 copper and bismuth mixed standard solution. Pipette 5.00mL copper standard s