QB/T 4055.2-2011 (QBT4055.2-2011)

QB/T 4055.2-2011_English: PDF (QBT 4055.2-2011, QBT4055.2-2011)
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)StatusPDF
QB/T 4055.2-2011English90 Add to Cart 0--9 seconds. Auto-delivery Cermet casings of watches - Part 2: Carbide cermet casings Obsolete QB/T 4055.2-2011

BASIC DATA
Standard ID QB/T 4055.2-2011 (QB/T4055.2-2011)
Description (Translated English) Cermet casings of watches - Part 2: Carbide cermet casings
Sector / Industry Light Industry Industry Standard (Recommended)
Classification of Chinese Standard Y11
Classification of International Standard 39.040.10
Word Count Estimation 11,17
Date of Issue 2011-05-18
Date of Implementation 2011-08-01
Quoted Standard GB/T 2828.1; GB/T 2829; GB/T 3489; GB/T 4028; GB/T 6569; GB/T 7997; GB/T 10700; GB/T 19719; QB/T 1898; QB/T 1901.2-2006
Drafting Organization Shenzhen FIYTA Sophisticated Manufacturing Co., Fiyta (Group) Co., Ltd.
Administrative Organization National Standardization Center - Watches
Regulation (derived from) China MIIT
Summary This standard specifies the watch carbide ceramic sheet metal case and bracelet requirements, test methods, inspection rules and signs, packaging, transportation and storage. This standard applies to tungsten carbide (WC) or titanium carbide (TiC) watch case and bracelet.

Standards related to: QB/T 4055.2-2011

QB/T 4055.2-2011
ICS 39.040.10
Classification: Y 11
Reference No.: 32178-2011
Light Industry Standard of the People’s Republic of China
Cermet casings of watches — Part 2: Carbide cermet
casings
Issued on May 18, 2011 Implemented on August 1, 2011
Issued by: Ministry of Industry and Information Technology of the
People's Republic of China
Table of Contents
Foreword ... 3
Introduction ... 4
1 Scope ... 5
2 Normative references ... 5
3 Terms and Definitions ... 6
4 Requirements ... 6
References and Original Chinese Documents ... 15
Cermet casings of watches — Part 2: Carbide cermet casings
1 Scope
This Part specifies technical requirements, testing methods, rules for inspection, packing,
marking, transport and storage of carbide cermet watchcases and watch-bands of
watches (known as casings for short hereafter).
This Standard applies to watch-cases and watch-bands made by carbide cermet material
with tungsten (WC) and titanium (TiC) as main composition. Watch-cases and
watch-bands made by carbide cermet material with other composition can also refer to
this Part.
2 Normative references
The following documents are necessary for the application of this Document. For dated
reference, only dated edition applies to this Document. For undated references, the latest
edition (including all amendments) applies.
GB/T 2828.1 Sampling procedures for inspection by attributes-Part1: Sampling schemes
indexed by acceptance quality limit (AQL) for lot-by-lot inspection (GB/T 2828.1-2003, ISO
2859-1: 1991, IDT)
GB/T 2829 Sampling procedures and tables for periodic inspection by attributes (Apply to
inspection of process stability)
GB/T 3489 Hard metals - Metallographic determination of porosity and uncombined
carbon (GB/T 3489-1983, ISO 4505: 1978, EQV)
GB/T 4028 Timekeeping instruments - Symbolization of control positions (GB/T
4028-1994, ISO 3158: 1976, IDT)
GB/T 6569 Test method for flexural strength of monolithic ceramics (GB/T 6569-2006, ISO
14704: 2000, MOD)
GB/T 7997 Hard metals - Vickers hardness test (GB/T 7997-1987, ISO 3878: 1983, EQV)
GB/T 10700 Test methods for elastic moduli of fine ceramics - Bending method
GB/T 19719 Jewelry - Determination of the release of nickel - Method of spectrometry
(GB/T 19719—2005, EN 1811: 1998, MOD)
GB/T 1898 Shock-resistant watches (QB/T 1898 —1993, ISO 1413: 1984, IDT)
GB/T 1901.2-2006 Watch-cases and accessories - Gold alloy coverings - Part 2:
Determination of fineness thickness corrosion resistance and adhesion (QB/T
1901.2—2006, ISO 3160-2: 2003, MOD)
3 Terms and Definitions
The following terms and definitions applied to this Document.
3.1
Carbide cermet
The cermet with carbide as main composition.
3.2
Tungsten carbide cermet
The cermet with tungsten carbide as main composition, the chemical formula is WC.
3.3
Titanium carbide cermet
The cermet with titanium carbide as main composition, the chemical formula is TiC.
4 Requirements
4.1 Impact resistance
After impact test and external force resistance test, the casings shall have no
phenomenon of falling off and function-damaged; the surface of which shall have no
cracks; the watch-cases and watch bands shall not have dents of which - diameter is
bigger than 0.2mm at the frond-side, and diameter is bigger than 1mm at sides and
back-side.
4.2 Corrosion resistance
After the corrosion test by specified time of Table 1, the casings shall have no difference in
color between before-test and after-test; the front and side parts of casings shall have no
pitting, pits and mottled traces of corrosion; and the back-side shall have no pitting and
pits.
4.3 Porosity
Bending strength σ f and modulus of elasticity Eb shall comply with the provisions of Table
3. The test of bending strength and modulus of elasticity shall be carried on the test
samples; test samples shall use the same carbide cermet material of the casings; and the
size of the test samples of bending strength shall meet the provisions of GB/T 6569; the
size of the test samples of modulus of elasticity shall meet the provisions of GB/T 10700.
Table 3 Bending strength and modulus of elasticity
5 Test Methods
5.1 Test Environment
Ambient temperature of the test is between 18 °C and 25 °C; and relative humidity is
less than 70%.
5.2 Test Items
5.2.1 Impact Resistance
5.2.1.1 Sample Status
Test sample shall be a completed watch [Translation: production-watch or commercial
watch] or simulated watch [Translation: prototype watch]. When testing, test clasp
shall be closed so as to make the watch to be the close-circular shape and use a
sponge or other soft objects to support it.
5.2.1.2 Impact
Test shall be carried out according to the test method specified by QB/T 1898; the
impact position shall be at 9H-side and the side which parallels to the disk surface of
the watch. The impact rate shall be 3.7m/s.
5.2.1.3 Resistance to External Performance
FASTERN clasp; APPLY the static tension F to the watch as shown in Figure 1
according to requirements in Table 4. REMAIN 1 minute when the tension reaches a
predetermined value. CHECK the sample according to the predetermined methods in
A) When the product is discontinued more than one production cycle and is
resumed production.
B) When new product is launched for production or old product transfers
production.
C) When the product design, structure, processes, materials have significant
changes or when the product transfers production.
D) When National Quality Supervision and Inspection agency calls for the type
inspection.
6.3 Inspection of Nickel release
Nickel release shall be tested according to the predetermined methods in GB/T9719.
7 Marking, Packaging, Transportation, and Storage
7.1 Marking
7.1.1 Marking Requirements
If the exterior parts meet the requirements of Chapter 4, marking shall be conducted
on a suitable location of the product or on the product certification, or on the product’s
instructions for use.
7.1.2 Marking Methods
Marking shall be composed of the code, the type of material and exterior parts of
cermet material as follows:
X2 -- Cermet casing (Indicated by the first letter in English)
X1 -- Cermet type (Represented by the chemical formula of the major component)
C -- Cermet material code
In which:
C: Cermet material code, cermet type of exterior parts shall be represented by C.
X1: Type of Cermet material shall be represented by the chemical formula of the
major component. Commonly used chemical formula of metal carbide cermet
materials are shown in 3.2, 3.3.
X2: Type of cermet casing, in which - "front circle" is represented by a "B" (bezel),
"Watch Case (with front ring-structure containing pre-laps)" is represented by C (case),
"Bracelet" is represented by L (link), and "strap" is represented by W (wristlet).
Example 1: The case and bracelet made of tungsten carbide cermet material is
labeled as C∙WC∙CW.
Example 2: the strap section of the titanium carbide ceramic material is labeled as
C∙TiC∙L.
7.2 Packaging
7.2.1 Casing shall be put into the packaging box with soft separated compartment to
ensure that there is no collision and extrusion damage.
7.2.2 The packaging box shall have the moisture resistance and impact resistance,
and the exterior packaging box shall have the sign of “Handle with Care”.
7 .3 Transportation and Storage
7.3.1 Casing, during transport and storage process, shall avoid extrusion, impact and
vibration.
7.3.2 The storage environment shall be kept dry and ventilated to avoid objects which
can produce corrosive gases.
...