GB/T 9755-2024_English: PDF (GB/T9755-2024)
| Standard ID | Contents [version] | USD | STEP2 | [PDF] delivered in | Standard Title (Description) | Status | PDF |
| GB/T 9755-2024 | English | 439 |
Add to Cart
|
4 days [Need to translate]
|
Synthetic resin emulsion based wall coatings
| Valid |
GB/T 9755-2024
|
| GB/T 9755-2014 | English | 305 |
Add to Cart
|
0--9 seconds. Auto-delivery
|
Synthetic resin emulsion coatings for exterior wall
| Valid |
GB/T 9755-2014
|
| GB/T 9755-2001 | English | 399 |
Add to Cart
|
3 days [Need to translate]
|
Synthetic resin emulsion coatings for exterior wall
| Obsolete |
GB/T 9755-2001
|
| GB/T 9755-1995 | English | 239 |
Add to Cart
|
2 days [Need to translate]
|
Synthetic resin emulsion coatings for exterior wall
| Obsolete |
GB/T 9755-1995
|
| GB 9755-1988 | English | 199 |
Add to Cart
|
2 days [Need to translate]
|
Synthetic resin emulsion coatings for exterior wall
| Obsolete |
GB 9755-1988
|
| Standard ID | GB/T 9755-2024 (GB/T9755-2024) | | Description (Translated English) | Synthetic resin emulsion based wall coatings | | Sector / Industry | National Standard (Recommended) | | Classification of Chinese Standard | G51 | | Classification of International Standard | 87.040 | | Word Count Estimation | 22,282 | | Date of Issue | 2024-11-28 | | Date of Implementation | 2025-06-01 | | Older Standard (superseded by this standard) | GB/T 9755-2014,GB/T 9756-2018 | | Drafting Organization | CNOOC Changzhou Paint Chemical Research Institute Co., Ltd., Carpoly Chemical Group Co., Ltd., Nippon Paint (China) Co., Ltd., Deawei (China) Co., Ltd., Sankeshu Paint Co., Ltd., Zhejiang Zhiqiang Paint Co., Ltd., Akzo Nobel Paint (Shanghai) Co., Ltd., Zhuhai Caizhu E-commerce Co., Ltd., China Coatings Industry Association, Jotun Paint (Zhangjiagang) Co., Ltd., Jiangsu Lanling Polymer Materials Co., Ltd., Shenzhen Guangtian Environmental Protection Paint Co., Ltd., Beixin Paint Co., Ltd. Company, Dow Chemical (China) Investment Co., Ltd., Ningbo Xin'an Coatings Co., Ltd., Guohengxin (Changzhou) Testing and Certification Technology Co., Ltd., Guangdong Bades New Materials Co., Ltd., Guke Energy Saving Technology Co., Ltd., Xiamen Dongshun Coatings Co., Ltd., Shanghai Tianchenxian | | Administrative Organization | National Technical Committee for Standardization of Paints and Pigments (SAC/TC 5) | | Proposing organization | China Petroleum and Chemical Industry Council | | Issuing agency(ies) | State Administration for Market Regulation, National Standardization Administration | | Standard ID | GB/T 9755-2014 (GB/T9755-2014) | | Description (Translated English) | Synthetic resin emulsion coatings for exterior wall | | Sector / Industry | National Standard (Recommended) | | Classification of Chinese Standard | G51 | | Classification of International Standard | 87.040 | | Word Count Estimation | 19,177 | | Date of Issue | 2014/7/8 | | Date of Implementation | 2014/12/1 | | Older Standard (superseded by this standard) | GB/T 9755-2001 | | Quoted Standard | GB/T 1728-1979; GB/T 1733-1993; GB/T 1766; GB/T 1865-2009; GB/T 1910; GB/T 3186; GB/T 6682-2008; GB/T 6750; GB/T 8170-2008; GB/T 9265; GB/T 9268-2008; GB/T 9271-2008; GB/T 9278; GB/T 9286; GB/T 9750; GB/T 9780-2013; GB/T 13491-1992; GB/T 15608; GB/T 16422 | | Adopted Standard | JIS K5663-2003, NEQ | | Drafting Organization | CNOOC Changzhou Paint Chemical Research Institute | | Administrative Organization | National Paint and color Standardization Technical Committee | | Regulation (derived from) | 2014 National Standards Bulletin No. 18 | | Proposing organization | China Petroleum and Chemical Industry Federation | | Issuing agency(ies) | General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China, Standardization Administration of the People's Republic of China | | Summary | This standard specifies the synthetic resin latex exterior paint product classification, classification, requirements, test methods, inspection rules and signs, packaging and storage and other content. This standard applies to the synthetic resin emulsion | | Standard ID | GB/T 9755-2001 (GB/T9755-2001) | | Description (Translated English) | Synthetic resin emulsion coatings for exterior wall | | Sector / Industry | National Standard (Recommended) | | Classification of Chinese Standard | G51 | | Classification of International Standard | 87.040 | | Word Count Estimation | 10,188 | | Date of Issue | 2001-09-06 | | Date of Implementation | 2002-04-01 | | Older Standard (superseded by this standard) | GB/T 9755-1995 | | Quoted Standard | GB/T 1250-1989; GB/T 1728-1979 (1989); GB/T 1733-1993; GB/T 1766-1995; GB/T 1865-1997; GB 3186-1982 (1989); GB/T 6682 -1992; GB/T 9265-1988; GB/T 9266-1988; GB/T 9270-1988; GB/T 9271-1988; GB 9278-1988; GB/T 9750-1998; GB/T 13491-1992; GB/T 15608-1995; HG/T 2458-1993; JC/T 412-1991; JG/T 25-1999 | | Adopted Standard | JIS K5663-1995; NEQ | | Drafting Organization | China National Chemical Construction Corporation Changzhou Chemical Research Institute | | Administrative Organization | National Standardization Technical Committee pigment coatings | | Proposing organization | National Petroleum and Chemical Industry Bureau of the People Republic of China | | Issuing agency(ies) | General Administration of Quality Supervision, Inspection and Quarantine of the People Republic of China | | Summary | This standard specifies: Synthetic resin emulsion exterior paint product classification, requirements, test methods, inspection rules and signs, packaging, storage and other requirements. This standard applies to: synthetic resin emulsion as the base material, and pigments, extender pigments and various additives formulated -, later applied to form a smooth surface a thin coat layer outer blocking paint. The coating applied to the surface of substandard buildings and structures decorative and protective. |
GB/T 9755-2024. Synthetic resin emulsion wall coatings
ICS 87.040
CCSG51
National Standard of the People's Republic of China
Replaces GB/T 9755-2014, GB/T 9756-2018
Synthetic resin emulsion wall paint
Released on 2024-11-28
2025-06-01 Implementation
State Administration for Market Regulation
The National Standardization Administration issued
Preface
This document is in accordance with the provisions of GB/T 1.1-2020 "Guidelines for standardization work Part 1.Structure and drafting rules for standardization documents"
Drafting.
This document replaces GB/T 9755-2014 "Synthetic resin emulsion exterior wall paint" and GB/T 9756-2018 "Synthetic resin emulsion interior wall paint"
This document is based on GB/T 9755-2014 and integrates some contents of GB/T 9756-2018.
Compared with.2014, in addition to structural adjustments and editorial changes, the main technical changes are as follows.
a) The “Scope” has been changed (see Chapter 1, Chapter 1 of the.2014 edition);
b) Added “Terms and Definitions” (see Chapter 3);
c) The “Product Classification” has been changed (see Chapter 4, Chapter 3 of the.2014 edition);
d) Added the "reinforcement performance" item and index of exterior wall primer, the "low temperature film forming property" item and index of exterior wall primer and exterior wall topcoat,
Items and indicators of interior wall primer and interior wall finish (see Chapter 5);
e) Deleted the items and indicators of "Compatibility with the next coating" for exterior wall primer, "Water permeability" for exterior wall topcoat, and "Water permeability" for medium
Painting items and indicators (see Chapter 4 of the.2014 edition);
f) Changed the indicators of "salinity and alkali resistance" and "water permeability" of exterior wall primer and "artificial weathering resistance" of exterior wall finish.
Purpose indicators (see Chapter 5, Chapter 4 of the.2014 edition);
g) Added requirements for polyester film, black and white card stock and mortar blocks (see 6.3.1.2.1, 6.3.1.2.2, 6.3.1.2.6);
h) Changed the requirements for "Asbestos-free fiber cement medium density slab" and "Asbestos-free fiber cement slab" (see 6.3.1.2.4, 6.3.1.2.5,.2014
5.3.2, A.1.3 of the.2015 edition);
i) Changed the “board making requirements” (see 6.3.2, 5.3 of the.2014 edition);
j) Changed the following terms. "State in container", "Applicability", "Appearance of coating", "Drying time", "Alkali resistance", "Water resistance", "Anti-salt and alkali", "Transparency"
Test methods for "water resistance", "scrub resistance" and "fouling resistance" (see 6.4, Chapter 5 of the.2014 edition);
k) Added test methods for the items of “low temperature film formation” and “reinforcement performance” (see 6.4.5 and 6.4.13).
Please note that some of the contents of this document may involve patents. The issuing organization of this document does not assume the responsibility for identifying patents.
This document was proposed by the China Petroleum and Chemical Industry Federation.
This document is under the jurisdiction of the National Technical Committee on Standardization of Paints and Pigments (SAC/TC5).
This document was drafted by. CNOOC Changzhou Coatings Chemical Research Institute Co., Ltd., Carpoly Chemical Group Co., Ltd., Nippon Paint
(China) Co., Ltd., DeAiWei (China) Co., Ltd., Sankeshu Paint Co., Ltd., Zhejiang Zhiqiang Paint Co., Ltd., AkzoNobel
Bell Paints (Shanghai) Co., Ltd., Zhuhai Caizhu E-commerce Co., Ltd., China Coatings Industry Association, Jotun Paints (Zhangjiagang) Co., Ltd.
Jiangsu Lanling Polymer Materials Co., Ltd., Shenzhen Guangtian Environmental Protection Coatings Co., Ltd., Beixin Coatings Co., Ltd., Dow Chemical (China)
Investment Co., Ltd., Ningbo Xin'an Coatings Co., Ltd., Guohengxin (Changzhou) Testing and Certification Technology Co., Ltd., Guangdong Bades New Materials Co., Ltd.
The previous versions of the documents replaced by this document are as follows.
---GB/T 9755, first issued in 1988, first revised in.1995, second revised in.2001, third revised in.2014;
---GB/T 9756, first issued in 1988, first revised in.1995, second revised in.2001, third revised in.2009
Revised for the fourth time in.2018.
Synthetic resin emulsion wall paint
1 Scope
This document specifies the product classification and grading, requirements, test methods, inspection rules, and marking, packaging, and other requirements of synthetic resin emulsion wall coatings.
and storage.
This document is applicable to synthetic resin emulsion prepared by emulsion polymerization as the base material, mixed with pigments, extender pigments and various additives
A wall paint that forms a thin coating with a smooth surface after application.
2 Normative references
The contents of the following documents constitute essential clauses of this document through normative references in this document.
For referenced documents without a date, only the version corresponding to that date applies to this document; for referenced documents without a date, the latest version (including all amendments) applies to
This document.
GB 175 General purpose Portland cement
GB/T 1727-2021 General preparation method for paint films
GB/T 1728-2020 Determination of drying time of paint film and putty film
GB/T 1766-2008 Rating method for aging of paint and varnish coatings
GB/T 1865-2009 Artificial weathering and artificial radiation exposure of paints and varnishes - Filtered xenon arc radiation
GB/T 1910-2015 Newsprint
GB/T 3186 Sampling of paints, varnishes and raw materials for paints and varnishes
GB/T 5206 Terms and definitions for paints and varnishes
GB/T 6682-2008 Specifications and test methods for water used in analytical laboratories
GB/T 6750-2007 Paints and varnishes - Determination of density - Pycnometer method
GB/T 8170-2008 Rules for rounding off values and expression and determination of limit values
GB/T 9265-2009 Determination of alkali resistance of architectural coatings
GB/T 9266-2009 Determination of scrub resistance of architectural coatings
GB/T 9268-2008 Determination of freeze-thaw resistance of latex paint
GB/T 9271-2008 Standard test panels for paints and varnishes
GB/T 9278 Temperature and humidity for condition adjustment and testing of coating samples
GB/T 9750 Packaging marking for coating products
GB/T 9780-2013 Test method for stain resistance of architectural coatings
GB/T 13452.2-2008 Determination of film thickness of paints and varnishes
GB/T 13491 General rules for packaging of coating products
GB/T 15608 Chinese Color System
GB/T 16422.3-2022 Plastics laboratory light source exposure test method Part 3.Fluorescent ultraviolet lamp
GB/T 20777 Inspection and preparation of paint and varnish samples
GB/T 23981.1-2019 Determination of hiding power of paints and varnishes Part 1.Determination of contrast ratio between white and light-colored paints
GB/T 30648.2-2015 Determination of resistance of paints and varnishes to liquids Part 2.Immersion method
GB/T 37356 Lighting conditions and methods for visual assessment of paint and varnish coatings
......
GB/T 9755-2014
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 87.040
G 51
Replacing GB/T 9755-2001
Synthetic resin emulsion coatings for exterior wall
合成树脂乳液外墙涂料
ISSUED ON. JULY 08, 2014
IMPLEMENTED ON. DECEMBER 01, 2014
Issued by. General Administration of Quality Supervision, Inspection and
Quarantine of PRC;
National Standardization Administration.
Table of Contents
Foreword... 3
1 Scope... 5
2 Normative references... 5
3 Product classification and grading... 6
4 Requirements... 6
5 Test method... 8
6 Inspection rules... 15
7 Marking, packaging, storage... 16
Appendix A (Normative) Test method for salt and alkaline resistance... 17
Appendix B (Normative) Water permeability test method... 20
Appendix C (Normative) Test method for scrubbing resistance... 22
Synthetic resin emulsion coatings for exterior wall
1 Scope
This standard specifies the product classification, grading, requirements, test methods,
inspection rules and marking, packaging and storage of synthetic resin emulsion
coatings for exterior wall.
This standard applies to exterior wall coatings that are made of synthetic resin emulsion
as the base material, pigments, body pigments (primers may not add pigments or body
pigments) and various additives; it can form a thin coating with a smooth surface after
application, including primers, midcoats, topcoats. This coating is suitable for
decoration and protection of the outer surfaces of buildings and structures.
2 Normative references
The following documents are essential to the application of this document. For the dated
documents, only the versions with the dates indicated are applicable to this document;
for the undated documents, only the latest version (including all the amendments) is
applicable to this standard.
GB/T 1728-1979 Methods of test for drying time of coatings of paints and putties
GB/T 1733-1993 Determination of resistance to water of films
GB/T 1766 Paints and varnishes - Rating schemes of degradation of coats
GB/T 1865-2009 Paints and varnishes - Artificial weathering and exposure to
artificial radiation - Exposure to filtered xenon-arc radiation
GB/T 1910 Newsprint
GB/T 3186 Paints, varnishes and raw materials for paints and varnishes - Sampling
GB/T 6682-2008 Water for analytical laboratory use - Specification and test
methods
GB/T 6750 Paints and varnishes - Determination of density - Pycnometer method
GB/T 8170-2008 Rules of rounding off for numerical values and expression and
judgement of limiting values
GB/T 9265 Determination for alkali resistance of film of architectural paints and
coatings
GB/T 9268-2008 Determination of freeze-thaw resistance of latex and emulsion
paints
GB/T 9271-2008 Paints and varnishes standard panels for testing
GB/T 9278 Temperatures and humidity for conditioning and testing of paint
specimens
GB/T 9286 Paints and varnishes - Cross cut test for films
GB/T 9750 Marks for package of coating products
GB/T 9780-2013 Test method for dirt pickup resistance and stain removal of film of
architectural coatings and paint
GB/T 13491-1992 General rule for packing of coatings
GB/T 15608 The Chinese color system
GB/T 16422.3-1997 Plastics - Methods of exposure to laboratory light sources - Part
3.Fluorescent UV lamps
GB/T 23981 Determination of contrast ratio of white and light colored paints
HG/T 3001-1999 Iron blue pigments
JC/T 412.1-2006 Fiber cement flat sheets - Part 1.Non-asbestos fiber cement flat
sheets
JG/T 25 Determination for freeze-thaw resistance of film of building coatings
3 Product classification and grading
This standard divides synthetic resin emulsion coatings for exterior wall into three
categories. primer, midcoat, topcoat.
Topcoat is divided into three grades according to the use requirements. superior grade,
first-grade, qualified grade. Primer is divided into Type I and Type II according to the
requirements of salt and alkali resistance and impermeability.
4 Requirements
4.1 Primer shall meet the requirements of Table 1.
mix evenly, it is evaluated as qualified.
5.5 Workability
5.5.1 Primer workability
Apply the specimen on the smooth surface of the test board with a brush. If the brush
runs smoothly, it is evaluated as "no difficulty in brushing".
5.5.2 Workability of midcoat and topcoat
Apply the specimen on the smooth surface of the test board with a brush. The coating
amount is about 100 μm wet film thickness. The long side of the test board is horizontal;
the short side is placed vertically at an angle of about 85° to the horizontal plane. After
6 hours of placement, apply the second coat of the specimen in the same way. When the
brush runs smoothly during the second coat, it can be evaluated as "no difficulty in
brushing the second coat".
5.6 Low temperature stability
Perform the test for 3 cycles according to Method A in GB/T 9268-2008.
5.7 Appearance of coating film
After the test in 5.5, place the test board for 24 hours and visually observe the coating
film. If there is no obvious shrinkage and sagging, meanwhile the coating film is
uniform, it is evaluated as “normal”.
5.8 Drying time
It is carried out according to the provisions of surface drying method B in GB/T 1728-
1979.
5.9 Alkali resistance
It is carried out according to the provisions of GB/T 9265.If 2 of the 3 test boards do
not show blistering, powdering, obvious discoloration and other coating damage
phenomena, it can be evaluated as "no abnormality". If the above damage phenomena
occur, describe it according to GB/T 1766.
5.10 Water resistance
It is carried out according to the provisions of method A in GB/T 1733-1993.In addition
to edge sealing, the back of the test board must be sealed before the test. Immerse the 3
test boards in the grade-3 water specified in GB/T 6682.If 2 of the 3 test boards do not
show blistering, powdering, obvious discoloration and other coating damage
phenomena, it can be evaluated as "no abnormality". If the above coating damage
phenomena occur, describe it according to GB/T 1766.
5.11 Salt and alkali resistance
For the test of salt and alkali resistance, see Appendix A.
5.12 Water permeability
For the test of water permeability, see Appendix B.
5.13 Adhesion
It is carried out according to the provisions of GB/T 9286.Use a single-edged knife to
cut 3 parallel lines along the long side of the sample in the parallel and vertical
directions, with a spacing of 3 mm and a grid number of 4, to conduct a tape tear test.
5.14 Contrast ratio
It is carried out according to the provisions of GB/T 23981; the arbitration test uses the
polyester film method.
5.15 Scrubbing resistance
It is carried out according to the provisions of Appendix C.
5.16 Artificial weathering resistance
The test is carried out according to the provisions of Cycle A in GB/T 1865-2009.The
evaluation of the results is carried out according to GB/T 1766.
5.17 Stain resistance
Perform two cycles of the test according to the provisions of Chapter 5 of GB/T 9780-
2013 “The test method for stain resistance of exterior walls - Brushing method B (fast
oven). For some exterior wall paint samples, when testing stain resistance, after
consultation with the relevant parties, the test boards are allowed to be tested after 7
days of curing and then irradiated with ultraviolet light for 4 hours (ultraviolet light
irradiation is carried out in accordance with GB/T 16422.3-1997, exposure method 1,
the light source is UV-A340 lamp tube).
5.18 Temperature change resistance of coating
According to the provisions of JG/T 25, 3 cycles are performed [18 hours of immersion
in (23 ± 2) °C water, 3 hours of freezing at (-20 ± 2) °C, 3 hours of hot baking at (50 ±
2) °C as one cycle]. If at least 2 of the 3 test boards shall not show any coating damage
phenomena such as powdering, cracking, blistering, peeling, obvious discoloration, etc.,
it can be evaluated as "no abnormality". If the above coating damage phenomena occur,
describe them in accordance with GB/T 1766.
5.19 Adaptability with the next coat
Appendix A
(Normative)
Test method for salt and alkaline resistance
A.1 Main materials and instruments
A.1.1 Preparation of PVA-iron blue water dispersion
A.1.1.1 Preparation of 2% PVA (powdered polyvinyl alcohol 1788) aqueous
solution
Add water to the container according to the calculated amount; slowly add powdered
polyvinyl alcohol 1788 under high-speed stirring; continue to stir at high speed after
the polyvinyl alcohol is added (stir for at least 1 hour). When there are no lumps or
blocks in the solution, the material can be discharged. After filtering through a 177 μm
filter, it shall be left to stand under the test environment specified in 5.2 for use. The
storage period shall not exceed 1 month.
A.1.1.2 Preparation of PVA-iron blue aqueous dispersion
Add 2% PVA aqueous solution (see A.1.1.1) into the container according to the
calculated amount; slowly add LA09-03 iron blue pigment that meets the requirements
of HG/T 3001-1999 while stirring; the mass ratio of 2% PVA aqueous solution (see
A.1.1.1) to iron blue pigment is 4.1; stir at high speed for about 10 min ~ 15 min, until
uniform; let it stand for 12 h under the test environment specified in 5.2 before use; the
storage period shall not exceed 1 month. Iron blue pigment should be supplied in a
unified manner to ensure its quality.
A.1.2 Preparation of test solution
Anti-salt-alkalinity test solution. NaOH, Ca(OH)2, CaCl2 mixed solution.
Prepare a mixed solution of NaOH, Ca(OH)2, CaCl2 according to the ratio of
NaOH.Ca(OH)2.CaCl2.water = 2.2.0.012.96 (mass ratio), one day before the test
[Ca(OH)2 has reached supersaturation and precipitation will occur. The mixed solution
does not need to be filtered and can be directly used for testing]. Place it in a closed
container. Place it overnight under the test environment specified in 5.2, to ensure that
the solution temperature reaches the standard conditions.
A.1.3 Test substrate
The substrate is a medium-density flat plate made of non-asbestos fiber reinforced
cement. The density of the test board is (1.2 ± 0.1) × 103 kg/m3; the thickness of the test
board is (6 ± 0.5) mm. The medium-density flat board made of non-asbestos fiber
reinforced cement should be supplied in a unified manner to ensure its quality. Remove
Appendix C
(Normative)
Test method for scrubbing resistance
C.1 Scope of application
Applicable to the determination of scrubbing resistance of architectural coatings that
can be made into flat coatings.
C.2 Test environment
The state conditioning of the test board and the temperature and humidity of the test
shall comply with the provisions of GB/T 9278.
C.3 Instruments
C.3.1 Scrubbing resistance tester
An instrument that can make a brush move back and forth on the coating surface of the
test sample and scrub the coating. The brush movement frequency is (37 ± 2)
reciprocating cycles per minute; the distance of one reciprocating stroke is 300 mm ×
2.The area in the middle of 100 mm is roughly uniform motion.
C.3.2 Auxiliary equipment
C.3.2.1 Brush
Evenly punch (60 ± 1) small holes with a diameter of about 3 mm on a 90 mm × 38 mm
× 25 mm hardwood board (or plastic board); plant black pig bristles vertically in the
holes; cut them flat at right angles to the bristles; the bristles are about 19 mm long. The
total mass of the fixture and brush is (450 ± 10) g.
Before use, immerse the bristles in (23 ± 2) °C water for 30 min; take them out and
shake off the water; then immerse 12 mm of the bristles in the washing medium that
meets the requirements of C.4 for 20 min. The brush can only be used after this
treatment.
When the bristles are worn to a length of less than 16 mm, the brush must be replaced.
C.3.2.2 Glass plate, about 6 mm thick, its length and width match the chassis size of
the washability tester.
C.3.2.3 PVC sheet, 12.7 mm wide, 0.25 mm thick, its length matches the width of the
glass plate in C.3.2.2.
C.3.2.4 Wet film preparation device, made of stainless steel, with a gap depth of 200
crusts and particles. Place a black plastic sheet (see C.3.2.6) on a glass plate or other
flat plate; use a wet film preparation device (see C.3.2.4) to scrape one line on the black
plastic sheet (see C.3.2.6). Prepare two test boards in total. The scraping speed shall be
quite slow, which takes 3 s ~ 4 s from one end to the other to avoid forming pinholes in
the paint film. Place the test board horizontally and cure it for 7 days under the test
environment specified in 5.2.
C.5.2 Measurement
C.5.2.1 Perform two parallel measurements.
C.5.2.2 Place the clean glass plate (see C.3.2.2) in the bottom plate of the scrubber.
Place a thin sheet (see C.3.2.3) on the glass plate (see C.3.2.2) perpendicular to the
running track of the brush. Make sure that the thin sheet (see C.3.2.3) is smooth and has
no burrs. Place the test board (see C.5.1) on the glass plate (see C.3.2.2) with the thin
sheet, with the coating facing up. The thin sheet shall be located in the middle of the
test board and make sure that the coating above the thin sheet has no defects and the
test area is flat. Place the fixed frame (see C.3.2.5) on the test board (see C.5.1) to fix
the test board. Clamp the fixed frame (see C.3.2.5) with the clamps at both ends of the
scrubber. The clamps on both sides of the scrubbing instrument are used to fix the frame
(see C.3.2.5); the clamps shall be sufficiently sealed to ensure that the fixation frame
(C.3.2.5) and the test board (see C.5.1) are in close contact; however, it shall be not too
tight to cause the test board (see C.5.1) to be distorted.
C.5.2.3 Before the test, use a soft paint brush to evenly apply the scrubbing medium
(see C.4) on the coating surface; let the liquid contact the coating for 60 seconds. Place
the pretreated brush on the coating surface of the test sample; keep the brush hanging
naturally. Start the instrument to scrub the coating back and forth. During scrubbing,
drip the scrubbing medium (see C.4) at a rate of about 0.04 mL per second to keep the
scrubbing surface moist.
C.5.2.4 Perform a specified number of scrubbing cycles (2000 or 1000 cycles), to
observe the removal of the paint film on the 12.7 mm wide sheet after the specified
number of scrubbing tests. If the paint film on the sheet is removed as a continuous thin
line and the length of the thin line exceeds the width of the sheet, it is judged to be
damaged.
......
Similar standards: GB/T 9755-2014 GB/T 50726-2023