GB/T 5137.5-2020English170 Add to Cart 0--9 seconds. Auto-delivery Test methods of safety glazing materials used on road vehicles -- Part 5: Resistant-to-chemical and resistant-to-temperature changes test Valid GB/T 5137.5-2020

BASIC DATA
Standard ID GB/T 5137.5-2020 (GB/T5137.5-2020)
Description (Translated English) Test methods of safety glazing materials used on road vehicles -- Part 5: Resistant-to-chemical and resistant-to-temperature changes test
Sector / Industry National Standard (Recommended)
Classification of Chinese Standard T34
Classification of International Standard 43.040.60
Word Count Estimation 7,795
Date of Issue 2020-03-31
Date of Implementation 2021-02-01
Drafting Organization China Building Materials Inspection and Certification Group Co., Ltd., Fuyao Glass Industry Group Co., Ltd., Jiangsu Tiezhu Glass Co., Ltd., China Automotive Technology Research Center Co., Ltd., Xinyi Auto Parts (Tianjin) Co., Ltd., Shentong Technology Group Co., Ltd., Xinyi Auto Parts (Wuhu) Co., Ltd., Xinyi Energy Saving Glass (Sichuan) Co., Ltd., National Safety Glass and Quartz Glass Quality Supervision and Inspection Center
Administrative Organization National Automotive Standardization Technical Committee (SAC/TC 114)
Proposing organization Ministry of Industry and Information Technology of the People's Republic of China
Issuing agency(ies) State Administration for Market Regulation, National Standardization Administration

Standards related to: GB/T 5137.5-2020

GB/T 5137.5-2020
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 43.040.60
T 34
Replacing GB/T 17339-1998
Test methods of safety glazing materials used on road
vehicles - Part 5: Resistant-to-chemical and resistant-
to-temperature changes test
ISSUED ON: MARCH 31, 2020
IMPLEMENTED ON: FEBRUARY 01, 2021
Issued by: State Administration for Market Regulation;
Standardization Administration of the PRC.
Table of Contents
Foreword ... 3 
1 Scope ... 5 
2 Normative references ... 5 
3 Terms and definitions ... 5 
4 Test conditions ... 5 
5 Resistant-to-chemical test ... 6 
6 Resistant-to-temperature changes test ... 9 
Foreword
GB/T 5137 "Test methods of safety glazing materials used on road vehicles" is
divided into 5 parts:
- Part 1: Mechanical properties tests;
- Part 2: Optical properties tests;
- Part 3: Radiation, high temperature, humidity, fire and simulated weathering
resistance tests;
- Part 4: Determination of solar characteristic;
- Part 5: Resistant-to-chemical and resistant-to-temperature changes test.
This Part is Part 5 of GB/T 5137.
This Part is drafted in accordance with the rules given in GB/T 1.1-2009.
This Part replaces GB/T 17339-1998 "Road vehicles - Safety glazing materials
- Test methods for resistant-to-chemicals and resistant-to-temperature
changes". Compared with GB/T 17339-1998, in addition to editorial changes,
the main technical changes of this Part are as follows:
- ADD normative references (see Clause 2);
- ADD terms and definitions (see Clause 3);
- ADD test conditions (see Clause 4);
- ADD test apparatus for resistant-to-chemical test (see 5.3);
- ADD the resistant-to-chemical test method for rigid plastics - weight-bearing
method (see 5.5.3);
- ADD test apparatus and appliances for resistant-to-temperature changes
test (see 6.2);
- ADD the resistant-to-temperature changes test method for rigid plastics
(see 6.4.2);
- Delete the test report (see Clause 4 of GB/T 17339-1998).
This Part was proposed by Ministry of Industry and Information Technology of
the PRC.
Test methods of safety glazing materials used on road
vehicles - Part 5: Resistant-to-chemical and resistant-
to-temperature changes test
Warning - Some test procedures specified in this document may lead to
dangerous situations. Users are responsible for taking appropriate safety
precautions.
1 Scope
This Part of GB/T 5137 specifies the methods of resistant-to-chemical and
resistant-to-temperature changes test of safety glazing materials used on road
vehicles.
This Part applies to the test of plastic-glass composite materials, rigid plastics,
and flexible plastics used on road vehicles. The weight-bearing method for
resistant-to-chemical is only applicable to rigid plastics.
2 Normative references
The following documents are indispensable for the application of this document.
For the dated references, only the editions with the dates indicated are
applicable to this document. For the undated references, the latest edition
(including all the amendments) are applicable to this document.
GB/T 5137.1 Test methods of safety glazing materials used on road vehicles
- Part 1: Mechanical properties tests (GB/T 5137.1-2020, ISO 3537:2015,
MOD)
QC/T 1119 Road vehicles - Glazing materials - Terminology (QC/T 1119-2019,
ISO 3536:2016, MOD)
3 Terms and definitions
The terms and definitions defined in QC/T 1119 apply to this document.
4 Test conditions
Unless otherwise specified, the test shall be carried out under the following
environmental conditions:
a) Ambient temperature: 20 °C±5 °C;
b) Atmospheric pressure: 8.60×104 Pa~1.06×105 Pa;
c) Relative humidity: 40%~80%.
5 Resistant-to-chemical test
5.1 Test purpose
Determine the resistant-to-chemical properties of plastic-glass composite
materials, rigid plastics, and flexible plastics during vehicle use.
5.2 Chemical reagents for the test
5.2.1 Abrasive-free liquid soap
Deionized water contains 1% (mass fraction) potassium oleate solution.
5.2.2 Window cleaning fluid
The aqueous solution OF isopropanol and dipropylene glycol monomethyl ether
with concentration of 5%~10% (mass fraction) respectively AND ammonia
hydroxide with mass concentration of 1%~5% (mass fraction).
5.2.3 Denatured alcohol
A mixture of 10 volumes of ethanol and 1 volume of methanol.
5.2.4 Gasoline
A mixture of 50% (volume fraction) toluene, 30% (volume fraction) 2,2,4-
trimethylpentane, 15% (volume fraction) 2,4,4-trimethyl-1-pentene, and 5%
(volume fraction) ethanol.
5.2.5 Kerosene
A mixture of 50% (volume fraction) n-octane and 50% (volume fraction) n-
decane.
5.3 Test apparatus
Soaking method should use metal or glassware with suitable capacity.
The test apparatus for weight-bearing method is shown in Figures 1 and 2. USE
a metal plate with a length of not less than 25 mm and a thickness of not more
2 - Fixed end.
Figure 2 -- Schematic diagram of the method of applying chemical
substances
5.4 Sample
The sample is a flat test piece of 180 mm×25 mm, or a test piece cut from a flat
part of the product. Before testing, the sample shall be placed in an environment
with a temperature of 23 °C±2 °C and a relative humidity of 50%±5% for at least
48 h.
5.5 Test procedure
5.5.1 Test preparation
The test shall be conducted under ventilated conditions. The operator shall
wear safety protective equipment. Before the test, the sample shall be cleaned
nondestructively.
5.5.2 Soaking method
POUR each chemical reagent specified in 5.2 into 5 utensils, respectively. The
amount of solution should be such that the sample is completely immersed.
After immersing the sample in the chemical reagent for 1 min, take it out;
immediately use a clean absorbent cotton cloth to wipe it dry. CHECK the
sample for softening, sticking, cracking, or obvious devitrification. For rigid
plastics applied to the driving vision area, after the test, take 1 of them and
perform the cross-cut test according to the test method of GB/T 5137.1;
determine the adhesion level.
A new sample shall be used for each chemical reagent.
5.5.3 Weight-bearing method
5.5.3.1 Sample installation
The sample is placed horizontally on the test stand to become a horizontal lever.
One end of the sample is the fixed end. The support is placed 51 mm from the
fixed end. A load is applied at the free end 102 mm from the support, as shown
in Figure 1. The load mass G is obtained from formula (1):
Where:
G - Load mass, in grams (g);
...