GB/T 38809-2020 (GBT38809-2020)

GB/T 38809-2020_English: PDF (GBT 38809-2020, GBT38809-2020)
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)StatusPDF
GB/T 38809-2020English225 Add to Cart 0--9 seconds. Auto-delivery General specification for low alloy ultra-high strength steels Valid GB/T 38809-2020

BASIC DATA
Standard ID GB/T 38809-2020 (GB/T38809-2020)
Description (Translated English) General specification for low alloy ultra-high strength steels
Sector / Industry National Standard (Recommended)
Classification of Chinese Standard H40
Classification of International Standard 77.140.20
Word Count Estimation 18,143
Date of Issue 2020-06-02
Date of Implementation 2020-12-01
Drafting Organization General Iron and Steel Research Institute, Fushun Special Steel Co., Ltd., Jiangyin Xingcheng Special Steel Co., Ltd., China Aviation Industry Corporation Shenyang Aircraft Design Institute, Jiangsu Yonggang Group Co., Ltd., Metallurgical Industry Information Standards Research Institute, Xi'an Aerospace Power Machinery Co., Ltd. Company, Xi'an Changfeng Electromechanical Research Institute, Northwest Industry Group Co., Ltd., Commercial Aircraft Corporation of China Ltd. Shanghai Aircraft Design and Research Institute, Fangda Special Steel Technology Co., Ltd.
Administrative Organization National Steel Standardization Technical Committee (SAC/TC 183)
Proposing organization China Iron and Steel Association
Issuing agency(ies) State Administration for Market Regulation, National Standardization Administration

Standards related to: GB/T 38809-2020

GB/T 38809-2020
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.140.20
H 40
General Specification for Low Alloy Ultra-high
Strength Steels
ISSUED ON: JUNE 2, 2020
IMPLEMENTED ON: DECEMBER 1, 2020
Issued by: State Administration for Market Regulation;
Standardization Administration of the People’s Republic of
China.
Table of Contents
Foreword ... 3 
1 Scope ... 4 
2 Normative References ... 4 
3 Order Content ... 6 
4 Dimensions, Shape and Weight ... 7 
5 Technical Requirements ... 7 
6 Test Methods ... 17 
7 Inspection Rules ... 18 
8 Packaging, Marking and Quality Certificate ... 19 
Appendix A (informative) A Comparison Table of Steel Designation and Code
... 20 
Appendix B (normative) Magnetic Particle Inspection Method ... 21 
General Specification for Low Alloy Ultra-high
Strength Steels
1 Scope
This Standard specifies the order content, dimensions, shape, weight, technical
requirements, test methods, inspection rules, packaging, marking and quality
certificate of low alloy ultra-high strength steels.
This Standard is applicable to rolled or forged low alloy ultra-high strength steel bars
(hereinafter referred to as steel bars).
The designation and chemical composition specified in this Standard are also
applicable to steel ingots, billets or their products.
2 Normative References
The following documents are indispensable to the application of this document. In
terms of references with a specified date, only versions with a specified date are
applicable to this document. In terms of references without a specified date, the latest
version (including all the modifications) is applicable to this document.
GB/T 222 Permissible Tolerances for Chemical Composition of Steel Products
GB/T 223.11 Iron, Steel and Alloy - Determination of Chromium Content - Visual
Titration or Potentiometric Titration Method
GB/T 223.17 Methods for Chemical Analysis of Iron, Steel and Alloy - The
Diantipyrylmethane Photometric Method for the Determination of Titanium Content
GB/T 223.23 Iron, Steel and Alloy - Determination of Nickel Content - The
Dimethylglyoxime Spectrophotometric Method
GB/T 223.26 Iron, Steel and Alloy - Determination of Molybdenum Content - The
Thiocyanate Spectrophotometric Method
GB/T 223.43 Iron, Steel and Alloy - Determination of Tungsten Content - Gravimetric
Method and Spectrophotometric Method
GB/T 223.53 Methods for Chemical Analysis of Iron, Steel and Alloy - The Flame
Atomic Absorption Spectrophotometric Method for the Determination of Copper
Content
GB/T 223.58 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium
Arsenite-sodium Nitrite Titrimetric Method for the Determination of Manganese Content
GB/T 223.59 Iron, Steel and Alloy - Determination of Phosphorus Content - Bismuth
Phosphomolybdate Blue Spectrophotometric Method and Antimony
Phosphomolybdate Blue Spectrophotometric Method
GB/T 223.60 Methods for Chemical Analysis of Iron, Steel and Alloy - The Perchloric
Acid Dehydration Gravimetric Method for the Determination of Silicon Content
GB/T 223.69 Iron, Steel and Alloy - Determination of Carbon Contents - Gas-volumetric
Method after Combustion in the Pipe Furnace
GB/T 223.72 Iron, Steel and Alloy - Determination of Sulfur Content - Gravimetric
Method
GB/T 223.76 Methods for Chemical Analysis of Iron, Steel and Alloy - The Flame
Atomic Absorption Spectrometric Method for the Determination of Vanadium Content
GB/T 224 Determination of Depth of Decarburization of Steels
GB/T 226 Test Method for Macrostructure and Defect of Steel by Etching
GB/T 228.1 Metallic Materials - Tensile Testing - Part 1: Method of Test at Room
Temperature
GB/T 229 Metallic Materials - Charpy Notch Impact Test
GB/T 231.1 Metallic Materials - Brinell Hardness Test - Part 1: Test Method
GB/T 702 Hot-rolled Steel Bars - Dimensions, Shape, Weight and Tolerances
GB/T 908 Forged Bars - Dimensions, Shape, Weight and Tolerances
GB/T 2101 General Requirement of Acceptance, Packaging, Marking and Certification
for Section Steel
GB/T 2975 Steel and Steel Products - Location and Preparation of Samples and Test
Pieces for Mechanical Testing
GB/T 4161 Metallic Materials - Determination of Plane-strain Fracture Toughness
GB/T 4162-2008 Forged and Rolled Steel Bars - Method for Ultrasonic Testing
GB/T 4336 Standard Test Method for Spark Discharge Atomic Emission Spectrometric
Analysis of Carbon and Low-alloy Steel (routine method)
GB/T 6394 Determination of Estimating the Average Grain Size of Metal
GB/T 8170 Rules of Rounding off for Numerical Values & Expression and Judgement
of Limiting Values
GB/T 10121 Steel Products - Method for Magnetic Particle Inspection of Tower Sample
GB/T 10561-2005 Steel - Determination of Content of Nonmetallic Inclusions -
Micrographic Method Using Standards Diagrams
GB/T 13298 Inspection Methods of Microstructure for Metals
GB/T 13299 Steel - Determination of Microstructure
GB/T 15711 Inspection of Non-metallic Inclusions of Steel - Etching Test Method of
Tower Samples
GB/T 17505 Steel and Steel Products - General Technical Delivery Requirements
GB/T 20066 Steel and Iron - Sampling and Preparation of Samples for the
Determination of Chemical Composition
GB/T 20123 Steel and Iron - Determination of Total Carbon and Sulfur Content -
Infrared Absorption Method after Combustion in an Induction Furnace (routine method)
GB/T 36026-2018 High-strength Corrosion-resistant Alloy Bars for Oil and Gas
Engineering
GB/T 37566 Method of Ultrasonic Testing for Round Steel
YB/T 5293 Metallic Materials - Forging Test
3 Order Content
The contract or order form that orders in accordance with this Standard shall at least
include the following content:
a) Serial No. of this Standard;
b) Product name;
c) Designation;
d) Specifications and precisions (see Chapter 4);
e) Weight;
f) Smelting method (see 5.2);
g) Delivery state (see 5.3);
Appendix B
(normative)
Magnetic Particle Inspection Method
B.1 Overview
The method specified in this Appendix is merely limited to non-metallic inclusion
magnetic particle inspection. During the inspection process, if real fractures are found,
such as: cracks, fissures, delamination and folds, then, the steel shall be scrapped,
unless these defects are caused by sample preparation.
B.2 Sample Preparation for Magnetic Particle Inspection
B.2.1 In terms of steel bars whose nominal diameter is not less than 300 mm, samples
may be prepared in accordance with one of the following methods:
a) From each sample billet, cut a 1/4 section (sufficient margin should be
retained) to forge into sample blank with a diameter of 75 mm ~ 150 mm.
Make the center of the sample billet roughly on the surface of the sample
blank; maintain the axis of the sample blank approximately parallel to the axis
of the original bar;
b) Forge the entire section of the steel bar into a round bar with a diameter of
150 mm, then, in accordance with B.2.2, prepare the samples.
B.2.2 In terms of steel bars whose nominal diameter is greater than 150 mm and less
than 300 mm, from each sample billet, cut a 1/4 section (sufficient margin should be
retained). Through machining or forging, make a sample blank with a diameter of 75
mm ~ 150 mm. In addition, make the center of the sample billet roughly on the surface
of the sample blank. Then, process the sample blank into a cylindrical sample with a
length of 125 mm. The minimum cutting amount of the sample blank shall comply with
the stipulations of B.2.4.
B.2.3 In terms of steel bars whose nominal diameter is not greater than 150 mm,
samples may be prepared in accordance with one of the following methods:
a) From each sample billet, cut a 1/4 section (sufficient margin should be
retained). Through machining, make a cylindrical sample with a length of 125
mm. In addition, make the center of the sample billet roughly on the surface
of the sample. The minimum cutting amount of the sample blank shall comply
with the stipulations of B.2.4;
b) Forge the entire section of the steel bar into tower-shaped samples with an
equal length. The dimensions of the tower-shaped samples are shown in
...