GB/T 37682-2019 (GBT 37682-2019)

GB/T 37682-2019_English: PDF (GBT37682-2019)
Standard IDContents [version]USDSTEP2[PDF] delivered inStandard Title (Description)Related StandardStatusGoogle Book
GB/T 37682-2019English145 Add to Cart 0--10 minutes. Auto-delivered. Large exposed gear steel castings -- Technical specification GB/T 37682-2019 Valid GB/T 37682-2019
 

BASIC DATA
Standard ID GB/T 37682-2019 (GB/T37682-2019)
Description (Translated English) Large exposed gear steel castings--Technical specification
Sector / Industry National Standard (Recommended)
Classification of Chinese Standard J31
Classification of International Standard 77.140.80
Word Count Estimation 10,175
Date of Issue 2019-06-04
Date of Implementation 2019-06-04
Drafting Organization CITIC Heavy Industry Machinery Co., Ltd., Erzhong (Deyang) Heavy Equipment Co., Ltd., Henan University of Science and Technology
Administrative Organization National Large-scale Casting and Forging Standardization Technical Committee (SAC/TC 506)
Regulation (derived from) National Standard Announcement No.7 of 2019
Proposing organization China Machinery Industry Federation
Issuing agency(ies) State Administration of Markets and China National Standardization Administration

GB/T 37682-2019
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.140.80
J 31
Large exposed gear steel castings -
Technical specification
ISSUED ON: JUNE 04, 2019
IMPLEMENTED ON: JUNE 04, 2019
Issued by: State Administration for Market Regulation;
Standardization Administration of the PRC.
Table of Contents
Foreword ... 3 
1 Scope ... 4 
2 Normative references ... 4 
3 Ordering requirements ... 5 
4 Manufacturing process ... 5 
5 Technical requirements ... 6 
6 Inspection rules and test methods ... 8 
7 Quality certification ... 11 
8 Identification, surface protection, packaging, storage and transportation ... 12 
Appendix A (Informative) Defect treatment method for large exposed gear steel
castings after finishing ... 13 
Large exposed gear steel castings -
Technical specification
1 Scope
This Standard specifies the ordering requirements, manufacturing process,
technical requirements, inspection rules and test methods, acceptance and
quality certification, identification and packaging of large exposed gear steel
castings.
This Standard applies to the ordering, manufacture, and inspection of large
gear steel castings in the form of exposed drive, which are cast using the sand
mold.
2 Normative references
The following documents are indispensable for the application of this document.
For the dated references, only the editions with the dates indicated are
applicable to this document. For the undated references, the latest edition
(including all the amendments) are applicable to this document.
GB/T 222 Permissible Tolerances for Chemical Composition of Steel
Products
GB/T 223 (all parts) Methods for chemical analysis of iron, steel and alloy
GB/T 228.1 Metallic materials - Tensile testing - Part 1: Method of test at
room temperature
GB/T 229 Metallic Materials - Charpy Pendulum Impact Test Method
GB/T 231.1 Metallic materials - Brinell hardness test - Part 1: Test method
GB/T 4336 Carbon and low-alloy steel - Determination of multi-element
contents - Spark discharge atomic emission spectrometric method (routine
method)
GB/T 5678 Sampling methods of spectrochemical analysis for cast alloys
GB/T 6414 Castings - Dimensional Tolerances and Geometrical Tolerances
and Machining Allowances
the supplier.
4.4 Defect removal and repair welding
4.4.1 Casting defects are allowed to be repaired by repair welding. Before repair
welding, the defects shall be cleaned, and confirmed by magnetic particle
testing or penetrant testing whether to meet the requirements of repair welding.
4.4.2 The repair welding of casting defects shall be carried out by qualified
operators in accordance with the process requirements. Before repair welding,
generally, it shall carry out the welding procedure qualification.
4.4.3 After the defect is removed, if the depth exceeds 25 mm or exceeds 40%
of the section thickness, it shall be regarded as a major defect. It shall record
the repair welding of the major defect.
4.4.4 After the repair welding of the defect, it shall carry out the stress relief heat
treatment. The repair welding zone shall be tested according to the non-
destructive testing standard of the casting, to confirm the quality of the repair
welding.
4.4.5 Upon agreement between the supplier and the purchaser, the defect
treatment after casting finishing may be carried out with reference to Appendix
A.
5 Technical requirements
5.1 Chemical composition
5.1.1 The chemical composition of each cast steel designation shall comply with
the requirements of Table 1.
5.1.2 Unless otherwise specified, the residual element content is not used as
the basis for acceptance.
5.1.3 When required by the purchaser, the chemical composition analysis of the
product may be carried out. The permissible tolerances for chemical
composition of products shall meet the requirements of GB/T 222.
According to the ordering requirements of the purchaser, the castings may be
subjected to magnetic powder, penetrant, and ultrasonic testing. The required
testing methods, testing positions, and acceptance quality levels are mutually
agreed by the supplier and the purchaser.
5.4 Surface quality
5.4.1 It shall clean the casting surface. There shall be no defects such as burnt-
on sand, cracks, cold shut. It shall correct the burr of the casting and remove
the scale.
5.4.2 The surface roughness Ra shall be less than or equal to 50 μm. The
surface to be non-destructively tested shall meet the requirements of non-
destructive testing.
5.5 Shape, dimensional tolerances, mass tolerances
5.5.1 The casting shape shall meet the requirements of the ordering drawings.
The dimensional tolerances of the casting shall meet the requirements of GB/T
6414. The tolerance grade is generally Grade DCTG14. The special grade is
agreed by the supplier and the purchaser.
5.5.2 The rim wall thickness and joint plate wall thickness of the casting shall
be uniform. The thinnest shall not be less than 5% of the wall thickness required
by the drawing. The thickest shall not be greater than 10% of the wall thickness
required by the drawing.
5.5.3 If a process supplement is finally retained, the mass tolerances of the
casting are not used as the basis for acceptance. In special cases, the mass
tolerances of the casting are agreed by the supplier and the purchaser.
6 Inspection rules and test methods
6.1 Chemical composition
6.1.1 The melting chemical composition shall be sampled and inspected
according to the melting heat. Samples for chemical composition analysis of
products may be taken from the test lug or the position at least 6 mm below the
casting surface. When a casting is cast in multiple ladle, it shall analyze each
ladle. The analysis results of each ladle shall meet the composition
requirements of the selected designation.
6.1.2 Chemical analysis sampling shall be in accordance with the provisions of
GB/T 20066; the analysis shall be in accordance with the provisions of GB/T
223. Spectrochemical analysis sampling shall be in accordance with the
6.6.2 When the tensile test fails, 2 standby tensile samples are taken from the
same heat to be tested. If the 3 test results are in accordance with Table 2, the
tensile properties of the castings of this heat are still qualified. If 1 of the
samples still fails the retest, the supplier may handle as specified in 6.7.
6.6.3 When the impact test fails, 3 standby impact samples are taken from the
same heat to be tested. The result is added to the previous result to recalculate
the average, which shall meet the requirements of Table 2. No more than 2 of
the 6 impact values is lower the specified average. No more than 1 is lower 70%
of the specified average. Otherwise, it will be judged as unqualified; the supplier
may handle as specified in 6.7.
6.6.4 In the hardness inspection, if there is a value below the specified minimum
hardness value on any prime line or the hardness difference between the points
exceeds 40 HBW, on both sides of the prime line, the test shall be doubled. If
the test results meet the requirements of Table 2, the casting hardness is
qualified. Otherwise, the supplier shall submit the actual distribution of the
hardness value to the purchaser for evaluation. If the purchaser evaluation is
not passed, it shall be handled according to 6.7.
6.7 Reheat treatment
When the retest result of mechanical properties still does not meet the
requirements of Table 2, the casting and the test bar may be heat treated again
and then retested in accordance with 6.2 and 6.3. Without the consent of the
purchaser, the number of reheat treatment shall not exceed 2 times (except
tempering).
7 Quality certification
7.1 The supplier shall provide the purchaser with a quality certification. The
quality certification shall include the following:
a) Supplier name;
b) Casting number or lot number;
c) Casting drawing number or ordering contract number;
d) Product executed standard number and material designation;
e) Melting furnace number and heat treatment state, heat;
f) Date or number of manufacture;
g) The inspection results specified in the standard;