Search result: GB/T 15764-2008 (GB/T 15764-1995 Older version)
| Standard ID | Contents [version] | USD | STEP2 | [PDF] delivered in | Standard Title (Description) | Status | PDF |
| GB/T 15764-2008 | English | 649 |
Add to Cart
|
5 days [Need to translate]
|
Standard terminology of flat glass
| Valid |
GB/T 15764-2008
|
| GB/T 15764-1995 | English | 959 |
Add to Cart
|
6 days [Need to translate]
|
Standard definitions of terms relating to flat glass
| Obsolete |
GB/T 15764-1995
|
| Standard ID | GB/T 15764-2008 (GB/T15764-2008) | | Description (Translated English) | Standard terminology of flat glass | | Sector / Industry | National Standard (Recommended) | | Classification of Chinese Standard | Q33 | | Classification of International Standard | 81.040 | | Word Count Estimation | 28,218 | | Date of Issue | 2008-10-15 | | Date of Implementation | 2009-06-01 | | Older Standard (superseded by this standard) | GB/T 15764-1995 | | Drafting Organization | Qinhuangdao Glass Industry Research and Design Institute | | Administrative Organization | Standardization Technical Committee of the National Building Glass | | Regulation (derived from) | National Standard Approval Announcement 2008 No.17 (Total No.130) | | Proposing organization | China Building Materials Federation | | Issuing agency(ies) | Administration of Quality Supervision, Inspection and Quarantine of People's Republic of China; Standardization Administration of China | | Summary | This standard specifies the flat glass varieties, physical and chemical properties, materials, furnace, melting, forming, cutline, relevant terms and their definitions defects and test methods and other aspects. This standard applies to the term sheet glass production and products involved in the interpretation. |
GB/T 15764-2008
Standard terminology of flat glass
ICS 81.040
Q33
National Standards of People's Republic of China
Replacing GB/T 15764-1995
Flat Glass term
Posted 2008-10-15
2009-06-01 implementation
Administration of Quality Supervision, Inspection and Quarantine of People's Republic of China
Standardization Administration of China released
Foreword
This standard replaces GB/T 15764-1995 "term sheet glass."
This standard and GB/T 15764-1995 compared to the main changes are as follows.
--- Modify the standard English name;
--- Increasing the term. ultra-white float glass, temporary stress, permanent stress, hanging wall, adjust the shutter, security shutter, chimney, large arch, hot,
Convection, the original film, Cinder machine, curtain, optical distortion, iridescent, point-like defects (Excerpts 2.5,3.6,3.7,5.28,5.29,5.30,
5.31,5.32,6.46,6.47,7.49,7.53,7.54,9.25,9.26,9.27);
--- Remove the term. heat-reflective glass, equilibrium thickness, qualified the original board, the original plate breakage rate, the original board scrap, TEUs (1995
2.5,7.37,7.50,7.54,7.55,8.6 version);
--- The term heat-absorbing glass, gate opening, furnace, pull to the side, a running side, put the edge, edge shrinkage, cracks, knots, edge defects were revised to
Tinted glass, flue damper opening, kiln age, pull machine, drag side, put the plate, plate shrink, crack, nodules, section defect (1995 edition
2.4,5.17,5.26,7.38,7.39,7.43,7.44,9.3,9.5,9.22, Excerpts 2.4,5.17 , 5.26,7.37,7.38,
7.42,7.43,9.3,9.5,9.22);
--- Add or modify the terms of toner, coloring agents, bleaching agents, clinker, melting section, clarification, homogenization, float, Lehr, cut cut, selection of films,
Striae, bubble open, lane English equivalents (1995 edition 4.9,4.14,4.15,4.23,5.2,6.37,6.39,7.7,
7.47,8.1,8.3,9.1,9.7,9.8, Excerpts 4.9,4.14,4.15,4.22,5.2,6.37 , 6.39,7.7,7.46,8.1,
8.3,9.1,9.7,9.8);
--- Modify the definition of the following terms. crystallization, stress, density, feldspar, bleaching agents, grinding, dosing, soda ash scattering rate, cooling unit, ears
A float (7.7) process to produce flat glass.
2.4
Added glass component colorant (4.14) show a certain color of the glass plate glass.
2.5
It produced using the float process, component iron oxide content of not more than 0.015%, having a high visible light transmittance of the flat glass.
2.6
Produced by calendering surface with patterns, translucent but opaque glass sheet.
2.7
Produced by calendering sandwiched inside wire mesh or plate glass.
3 physical and chemical properties of flat glass
3.1
Produce the phenomenon of crystal glass.
3.2
Corresponding to a glass viscosity temperature 106.6Pa · s time. Also known as the softening temperature.
3.3
A temperature corresponding to a glass viscosity 1013.5Pa · s ~ 1013.6Pa · s when, at this temperature, the glass begins to eliminate stress.
......
|