Determination of free cementite, pearlite and Widmanstatten structure in steel
| Valid |
GB/T 13299-2022
|
GB/T 13299-1991 | English | 70 |
Add to Cart
|
0--9 seconds. Auto-delivery
|
Steel. Determination of microstructure
| Obsolete |
GB/T 13299-1991
|
Standard ID | GB/T 13299-2022 (GB/T13299-2022) | Description (Translated English) | Determination of free cementite, pearlite and Widmanstaten structure in steel | Sector / Industry | National Standard (Recommended) | Classification of Chinese Standard | H24 | Classification of International Standard | 77.040.99 | Date of Issue | 2022-07-11 | Date of Implementation | 2023-02-01 | Older Standard (superseded by this standard) | GB/T 13299-1991 | Standard ID | GB/T 13299-1991 (GB/T13299-1991) | Description (Translated English) | Steel. Determination of microstructure | Sector / Industry | National Standard (Recommended) | Classification of Chinese Standard | H24 | Classification of International Standard | 77.040.30 | Word Count Estimation | 19,145 | Date of Issue | 1991/12/13 | Date of Implementation | 1992/10/1 | Quoted Standard | GB/T 13298 | Drafting Organization | Taiyuan Iron and Steel Company | Proposing organization | Ministry of Metallurgical Industry of the People Republic of China | Issuing agency(ies) | State Bureau of Technical Supervision | Summary | This standard specifies the metallurgical evaluation method free cementite steel, low carbon steel deformed pearlite banded structure and widmanstatten, evaluation principles and organizational characteristics. This standard applies to low-carbon, medium carbon steel, steel and profiles of microstructure evaluation; other steel grades according to the relevant standards or protocols, may refer to the standard assessment. |
GB/T 13299-2022
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.040.99
CCS H 24
Replacing GB/T 13299-1991
Determination of Free Cementite, Pearlite and
Widmanstaten Structure in Steel
ISSUED ON: JULY 11, 2022
IMPLEMENTED ON: FEBRUARY 1, 2023
Issued by: State Administration for Market Regulation;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative References ... 5
3 Terms and Definitions ... 5
4 Cutting and Preparation of Specimens ... 6
4.1 Cutting of Specimens ... 6
4.2 Preparation of Specimens ... 10
5 Determination Method of Free Cementite ... 10
5.1 General Principle ... 10
5.2 Comparison Method with Standard Rating Pictures ... 11
5.3 Quantitative Analysis Method with an Image Instrument ... 12
6 Determination Method of Pearlite ... 13
6.1 General Principle ... 13
6.2 Determination Method ... 13
7 Determination Method of Widmanstaten Structure ... 14
7.1 General Principle ... 14
7.2 Determination Method ... 14
8 Test Report ... 15
Appendix A (normative) Standard Rating Pictures of Free Cementite ... 17
Appendix B (informative) An Example of Quantitative Analysis of Cementite in SPCC
Steel ... 26
Appendix C (normative) Standard Rating Pictures of Pearlite ... 31
Appendix D (normative) Standard Rating Pictures of Widmanstaten Structure ... 40
Bibliography ... 46
Foreword
This document was drafted in accordance with the rules provided in GB/T 1.1-2020 Directives
for Standardization - Part 1: Rules for the Structure and Drafting of Standardizing Documents.
This document serves as a replacement for GB/T 13299-1991 Steel - Determination of
Microstructure. In comparison with GB/T 13299-1991, apart from structural adjustments and
editorial modifications, the main technical changes are as follows:
---Terms and definitions are added (see Chapter 3);
---The cutting and preparation of specimens are added (see Chapter 4);
---The magnification “400 times (360 ~ 450 times allowed)” for the determination of free
cementite and pearlite is modified into “500 times”; the magnification “100 times (95
~ 110 times allowed)” for the determination of Widmanstaten structure is modified into
“100 times” (see 5.2, 6.2 and 7.2; 4.1 of Version 1991);
---The principle of dividing different series of free cementite is modified (see 5.2.3; 5.1 of
Version 1991);
---The dimensional requirements of free cementite and pearlite rating series are modified
(see Table 1 and Table 2; Table 1 and Table 2 of Version 1991);
---The relevant content of the determination method of banded structure is deleted (see 5.3
and A3 in Appendix A of Version 1991);
---The relevant content of the quantitative analysis method of the image instrument for the
determination of free cementite is added (see 5.3);
---The requirements for the recording of the contents “serial No. of this document,
specimen status, test date and tester’s name” are added (see Chapter 8);
---The standard rating pictures of free cementite and pearlite are modified: the pictures
with a magnification of 400 times are modified into pictures with a magnification of
500 times (see Appendix A and Appendix C; A1 and A2 in Appendix A of Version 1991).
Please be noted that certain content of this document may involve patents. The institution
issuing this document does not undertake the responsibility of identifying these patents.
This document was proposed by China Iron and Steel Association.
This document shall be under the jurisdiction of National Technical Committee 183 on Steel of
Standardization Administration of China (SAC/TC 183).
The drafting organizations of this document: Shanxi TAIGANG Stainless Steel Co., Ltd.;
SHOUGANG Group Co., Ltd.; China Metallurgical Information and Standardization Institute;
Determination of Free Cementite, Pearlite and
Widmanstaten Structure in Steel
1 Scope
This document specifies the methods of the cutting, preparation and determination of free
cementite, pearlite and Widmanstaten structure specimens in steel.
This document is applicable to the determination of free cementite, pearlite and Widmanstaten
structure in low-carbon and medium-carbon steel plates, steel strips and steel rods (billets). For
other steel types, this document may be taken as a reference.
2 Normative References
The contents of the following documents constitute indispensable clauses of this document
through the normative references in this text. In terms of references with a specified date, only
versions with a specified date are applicable to this document. In terms of references without a
specified date, the latest version (including all the modifications) is applicable to this document.
GB/T 13298 Inspection Methods of Microstructure for Metals
3 Terms and Definitions
The following terms and definitions are applicable to this document.
3.1 Ferrite
Ferrite refers to -Fe solid solution containing alloying elements.
[source: GB/T 30067-2013, 2.2.247]
3.2 Pearlite
When the carbon content in iron-carbon alloy is greater than 0.025% and less than 6.67%, a
metastable microstructure formed when local regions in austenite tend to be eutectoid. This
structure is formed by slow cooling in the process of eutectoid transformation, which is an
alternating lamellar structure formed by ferrite and cementite.
[source: GB/T 30067-2013, 2.2.348]
3.3 Free Cementite
Free cementite refers to granular cementite that exists independently on the ferrite matrix or
grain boundaries.
NOTE: the free cementite in low-carbon annealed steel with a carbon content of no more than 0.15%
is mainly a product of pearlite transformation, and a small amount of tertiary cementite
may also exist; the free cementite in ultra-low carbon steel (with a carbon content of less
than 0.02%) is tertiary cementite.
3.4 Pearlite Colony
Pearlite colony refers to a bounded aggregate of sheets of the same phase with the same
orientation.
[source: GB/T 30067-2013, 2.2.349]
3.5 Widmanstaten Structure
Widmanstaten structure refers to a structure, in which, pearlite exists, in hypoeutectoid steel,
when proeutectoid ferrite grows from the austenite grain boundary or within the grain along a
certain grain plane of the austenite, and precipitates in the form of needles.
[source: GB/T 30067-2013, 2.2.268, modified]
4 Cutting and Preparation of Specimens
4.1 Cutting of Specimens
4.1.1 Cutting positions
Under general circumstances, the specimens shall be cut from the steel (or intermediate billet)
in the delivery state; the sampling method and sampling size shall comply with the stipulations
of the product standards or technical conditions. If there is no special stipulation, the inspection
surface of free cementite and pearlite specimens shall be parallel to the longitudinal axis of steel
strips, steel plates and steel rods (billets); the inspection surface of Widmanstaten structure
specimen shall be perpendicular to the longitudinal axis of steel strips, steel plates and steel
rods (billets). See the suggested specific sampling positions and methods in Figure 1 ~ Figure
6 (in which, Position A is applicable to the sampling of Widmanstaten structure specimen;
Position B is applicable to the sampling of free cementite and pearlite specimens).
4.1.2 Sampling method of steel plate or steel strip
The sampling of steel plate or steel strip is as follows:
a) Steel plate or steel strip with a thickness less than or equal to 25 mm: the specimen is
cut from the middle part from the center of the steel plate (strip) to the outer surface;
the inspection surface shall be a full-thickness section (see Figure 1); the length of the
specimen is recommended not to be less than 20 mm;
5.2 Comparison Method with Standard Rating Pictures
5.2.1 Place the specimen under the bright field of a metallographic microscope for observation;
the magnification is 500 times. The diameter of the field of view of the magnified image is 80
mm. Observe the entire inspection surface; select the most serious field of view on the
inspection surface. During the determination, compare the most serious field of view of free
cementite on the inspection surface with the standard rating pictures in Appendix A for rating,
so as to determine the level of the free cementite.
5.2.2 In accordance with the characteristics of the cementite, such as: shape, distribution and
size, determine the rating of the free cementite.
5.2.3 In accordance with the structural characteristics, the rating pictures of free cementite are
divided into three series:
a) Series A: the cementite is distributed along the grain boundaries in the form of a
network; it is determined in accordance with the ratio of the portion surrounded by
the cementite network on the periphery of individual ferrite grains and the
completeness of the cementite network;
b) Series B: the cementite is distributed in single-layer, double-layer or multi-layer chain;
it is determined in accordance with the particle size of free cementite, the distribution
degree of chain layer and the length of chain;
c) Series C: the cementite is point-shaped; it is determined in accordance with the
particle size of the point-shaped cementite and the degree of banded distribution of
cementite.
5.2.4 The pictures of each series are from Level 0 to Level 5. Table 1 provides a detailed
description of the structural characteristics of each level.
5.2.5 The determination results are expressed in levels, and the characteristics of the levels are
between two adjacent levels, and half levels can be added. If necessary, a series of letters shall
be marked, such as: 1.0A and 2.5B, etc.
5.3 Quantitative Analysis Method with an Image Instrument
5.3.1 The metallographic manual measurement method (grid cut point method and microscope
scale method) or metallographic image analysis software can be adopted to determine the area
content of free cementite. The magnification shall adopt 500 times. Conduct random
measurement of not less than 5 fields of view. The positions of the 5 fields of view can be at
the edge, quarter or center of the specimen; the specific positions can be agreed upon by the
supply-side and the demand-side. If there is no clear stipulation, randomly measure 5 fields of
view at a quarter of the thickness of the specimen; take the average value of the 5 fields of view
as the final measurement result of the percentage composition of free cementite; 2 decimal
places shall be retained. The specific determination method can refer to GB/T 15749 or GB/T
18876.1.
5.3.2 Calculate the standard deviation s of the results, the expanded uncertainty U95 and the
relative expanded uncertainty U95rel of the probability 95%. The relative expanded uncertainty
is an estimate of the relative precision of the measurement mean; the change of the number of
fields of view will affect the relative precision. Generally, when U95rel is not greater than 30%,
the measurement result is valid. If U95rel is greater than 30%, the number of fields of view shall
be increased, until U95rel is not greater than 30%. Appendix B provides an example of
quantitative analysis of cementite in SPCC steel.
6 Determination Method of Pearlite
6.1 General Principle
This method is applicable to the determination of pearlite in steel plates, steel strips and steel
rods (billets) with a carbon content of 0.1% ~ 0.30%.
6.2 Determination Method
6.2.1 Place the specimen under the bright field of a metallographic microscope for observation;
the magnification is 500 times. The diameter of the field of view of the magnified image is 80
mm. Observe the entire inspection surface; select the most serious field of view on the
inspection surface for determination. During the determination, compare the most serious field
of view on the inspection surface with the standard rating pictures in Appendix C for rating, so
as to determine the level of the pearlite.
6.2.2 In accordance with the characteristics of the pearlite, such as: structure (granular, fine-
grained pearlite colony or flaky), quantity and distribution, determine the rating of the pearlite.
6.2.3 In accordance with the structural characteristics, the rating pictures of pearlite are divided
into three series:
a) Series A: applicable to the rating of granular pearlite in cold-rolled steel with a carbon
content of 0.10% ~ 0.20%. The larger the level, then, the cementite particles aggregate
and tend to form bands;
b) Series B: applicable to the rating of fine-grained pearlite colony in hot-rolled steel
with a carbon content of 0.10% ~ 0.20%. The larger the level, then, the granular
pearlite transitions to lamellar pearlite forming deformation bands (and forms split
bands);
c) Series C: applicable to the rating of pearlite in hot-rolled steel with a carbon content
of 0.21% ~ 0.30%. The larger the level, then, the fine flaky pearlite transitions from
a colony structure with less uniform size and uniform distribution to an uneven band
structure. At this moment, it shall be determined in accordance with the width of the
continuous band constituted by pearlite aggregation.
6.2.4 The pictures of each series are from Level 0 to Level 5. Table 2 provides a detailed
description of the structural characteristics of each level.
6.2.5 The determination results are expressed in levels, and the characteristics of the levels are
between two adjacent levels, and half levels can be added. If necessary, a series of letters shall
be marked, such as: 1.0A and 2.5B, etc.
7 Determination Method of Widmanstaten Structure
7.1 General Principle
This method is applicable to the determination of Widmanstaten structure in steel plates, steel
strips and steel rods (billets) with a carbon content between 0.15% ~ 0.50%.
7.2 Determination Method
7.2.1 Place the specimen under the bright field of a metallographic microscope for observation;
the magnification is 100 times. The diameter of the standard field of view is 80 mm. Observe
the entire inspection surface; select the most serious field of view on the inspection surface.
During the determination, compare the most serious field of view on the inspection surface with
the standard rating pictures in Appendix D for rating, so as to determine the level of the
Widmanstaten structure.
7.2.2 In accordance with the quantity and size of the precipitated acicular ferrite and the size of
ferrite network, determine the level of the Widmanstaten structure.
7.2.3 In accordance with the structural characteristics, the rating pictures of Widmanstaten
structure are divided into two series:
a) Series A: applicable to the Widmanstaten structure rating of steel with a carbon
content of 0.15% ~ 0.30%.
b) Series B: applicable to the Widmanstaten structure rating of steel with a carbon
content of 0.31% ~ 0.50%.
7.2.4 The pictures of each series are from Level 0 to Level 5. Table 3 provides a detailed
description of the structural characteristics of each level.
7.2.5 The determination results are expressed in levels, and the characteristics of the levels are
between two adjacent levels, and half levels can be added. If necessary, a series of letters shall
be marked, such as: 1.0A and 2.5B, etc.
8 Test Report
The test report should include the following contents:
a) Designation, batch No. and specification of steel;
b) Serial No. of specimen;
c) Serial No. of this document;
......
GB/T 13299-1991
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
UDC 669.14: 620.186
H 24
GB/T 13299-91
Steel - Determination of microstructure
ISSUED ON: DECEMBER 13, 1991
IMPLEMENTED ON: OCTOBER 01, 1992
Issued by: Administration of Technical Supervision of the People’s
Republic of China
Table of Contents
1 Subject content and scope of application ... 3
2 Reference ... 3
3 Cutting and preparation of specimens ... 3
4 Determination method of microstructure ... 3
5 Determination principles of microstructure ... 4
6 Test record ... 8
Annex A Standard rating diagrams (supplement) ... 9
Additional information: ... 14
Steel - Determination of microstructure
1 Subject content and scope of application
This Standard specifies the metallographic determination method,
determination principles and structural characteristics of free cementite, pearlite
of low-carbon deformed steels, banded structure and Widmannstatten structure
of steels.
This Standard applies to the determination of microstructure of steel plates,
steel strips and sections of low-carbon and medium-carbon steels. Other steel
types can be determined with reference to this Standard according to relevant
standards or agreements.
2 Reference
GB/T 13298 Inspection methods of microstructure for metals
3 Cutting and preparation of specimens
The cutting and preparation of specimens shall be carried out in accordance
with the relevant provisions of GB/T 13298.
4 Determination method of microstructure
4.1 The magnification for determination of free cementite and pearlite is 400×
(360 ~ 450× is allowed). The magnification for determination of banded
structure and Widmannstatten structure is 100× (95 ~ 110× is allowed).
4.2 The standard field of view diameter is 80 mm.
4.3 The determination is carried out by comparison with the corresponding
standard rating diagrams.
4.4 The two surface layers with a depth of approximately 10 % of the thickness
of the steel plate are not inspected.
4.5 When rating, it shall select the highest level in each field of view on the
grinding surface for determination.
4.6 The determination results are expressed by levels. If the level
characteristics are between the adjacent 2 levels, a half level can be attached.
If necessary, the series letter shall be marked, such as 1A, 3B.
5 Determination principles of microstructure
5.1 Free cementite (rating diagrams are shown in Annex A1)
For the determination of free cementite of low-carbon annealed steels with a
carbon content of less than or equal to 0.15 %, it is determined based on the
shape, distribution and size characteristics of cementite.
Table 1 is the description of the structural characteristics of which the rating
diagrams are shown in Annex A1. It consists of each 6 levels in 3 series.
A series: It is determined according to the principle of forming cementite
networks at grain boundaries. The ratio of the part surrounded by cementite
networks at the periphery of individual ferrite grains is used as the determination
principle.
B series: It is determined according to the principle of free cementite granules
constituting single-layer, double-layer and multi-layer chains of different lengths
and increase in granule size.
C series: It is determined according to the principle of transition from evenly
distributed dotted cementite to uneven banded structure.
5.2 Pearlite of low-carbon deformed steels (rating diagrams are shown in
Annex A2)
For the determination of pearlite of low-carbon deformed steels with a carbon
content of 0.10 % to 0.30 %, it is determined according to the structure (granular,
fine granular pearlite colony or lamellar), quantity and distribution
characteristics of pearlite.
Table 2 is the description of the structural characteristics of which the rating
diagrams are shown in Annex A2. It consists of each 6 levels in 3 series.
A series: It is designated for the rating of granular pearlite of cold-rolled steels
with a carbon content of 0.10 % to 0.20 %. As the level increases, cementite
granules aggregate and tend to form bands.
B series: It is designated for the rating of fine granular pearlite colonies of hot-
rolled steels with a carbon content of 0.1 % to 0.20 %. As the level increases,
granular pearlite transitions to lamellar pearlite that forms deformation bands
(and forms split bands).
C series: It is designated for the rating of pearlite of hot-rolled steels with a
carbon content of 0.21 % to 0.30 %. As the level increases, fine lamellar pearlite
transitions from uneven-size and evenly distributed colony structure to uneven
banded structure. At this time, it must be determined based on the width of the
continuous band composed of aggregated pearlite.
5.3 Banded structure (rating diagrams are shown in Annex A3)
For the determination of banded structure of pearlitic steels, it is determined
according to the increase in the quantity of banded ferrites, considering the
degree and continuity of banded structure that passes through the field of view,
and the quantity of deformed ferrite grains.
Table 3 is the description of the structural characteristics of which the rating
diagrams are shown in A3. It consists of each 6 levels in 3 series.
A series: It is designated for the rating of banded structure of steels with a
carbon content of 0.15 % or less.
B series: It is designated for the rating of banded structure of steels with a
carbon content of 0.16 % to 0.30 %.
C series: It is designated for the rating of banded structure of steels with a
carbon content of 0.31 % to 0.50 %.
5.4 Widmannstatten structure (rating diagrams are shown in Annex A4)
For the determination of Widmannstatten structure of pearlitic steels after
overheating, it is determined according to the quantity and size of acicular ferrite
precipitated and the size of austenite grains determined by ferrite networks.
Table 4 is the description of the structural characteristics of which the rating
diagrams are shown in Annex A4. It consists of each 6 levels in 2 series.
A series: It is designated for the rating of Widmannstatten structure of steels
with a carbon content of 0.15 % to 0.30 %.
B series: It is designated for the rating of Widmannstatten structure of steels
with a carbon content of 0.31 % to 0.50 %.
Table 1 -- Free cementite
Level Structural characteristics A series B series C series
Free cementite is granular
with a size of ≤ 2 mm,
evenly distributed
Free cementite is dotted or
small granular, tending to
constitute single-layer
chains
Free cementite is dotted or
small granules, evenly
distributed, slightly oriented
in the deformation direction
......
|