HOME   Cart(0)   Quotation   About-Us Tax PDFs Standard-List Powered by Google www.ChineseStandard.net Database: 189759 (9 Feb 2025)

Q/BQB 610-2018 (Q/BQB 610-2023 Newer Version) PDF English


Search result: Q/BQB 610-2018 (Q/BQB 610-2023 Newer Version)
Standard IDContents [version]USDSTEP2[PDF] delivered inName of Chinese StandardStatus
Q/BQB 610-2023English349 Add to Cart 3 days Steel plates for structure  
Q/BQB 610-2018English215 Add to Cart 0-9 seconds. Auto-delivery. Steel plates for structure
BUY with any currencies (Euro, JPY, GBP, KRW etc.): Q/BQB 610-2018     Newer/related standards: Q/BQB 610-2023

PDF Preview: Q/BQB 610-2018


Q/BQB 610-2018: PDF in English (QBQB 610-2018)

Q/BQB 610-2018 ENTERPRISE STANDARD OF BAOSHAN IRON & STEEL CO., LTD. Replacing Q/BQB 610-2013 Steel Plates for Structure ISSUED ON: JANUARY 15, 2018 IMPLEMENTED ON: APRIL 10, 2018 Issued by: BAOSHAN IRON & STEEL CO., LTD. Table of Contents Foreword ... 3  1 Scope ... 4  2 Normative References ... 4  3 General Technical Requirements ... 5  4 Classification and Code ... 5  5 Technical Requirements ... 5  6 Inspection and Testing ... 10  7 Appendix ... 12  Appendix A (informative) A Comparison Table of this Standard, and Reference Standards and International Approximate Nameplates ... 13  Foreword This Standard was drafted in accordance with the rules in GB/T 1.1-2009 Directives for Standardization - Part 1: Structure and Drafting of Standards. The formulation of this Standard takes JIS G3101:2015/AMENDMENT 1:2017 and EN 10025-2: 2004, and the practical situation of Baoshan Iron & Steel as a reference. This Standard serves as a replacement of Q/BQB 610-2013 Steel Plates for Structure. In comparison with the previous standard, there are several main changes as follows: ---In Normative References, the reference of GB/T 20124 is added; the reference of GB/T 20126 is deleted; the year of issuance of GB/T 2975 is added; ---The stipulations of phosphorus and sulfur content in the chemical composition of various nameplates become more rigorous; ---The stipulations of re-test of impact test are improved. In this Standard, Appendix A is informative. This Standard was proposed by the Manufacturing Management Department of Baoshan Iron & Steel Co., Ltd. This Standard was drafted by the Manufacturing Management Department of Baoshan Iron & Steel Co., Ltd. The drafter of this Standard: Huang Jinhua. The issuance of the previous versions of the standard replaced by this Standard is as follows: ---Q/BQB 610-2004, Q/BQB 610-2009, Q/BQB 610-2013. Steel Plates for Structure 1 Scope This Standard specifies the dimensions, appearance, technical requirements, inspection and testing, signs and inspection documents of steel plates for structure. This Standard is applicable to steel plates for structure manufactured by Baoshan Iron & Steel Co., Ltd. 2 Normative References The following documents are indispensable to the application of this Standard. In terms of references with a specified date, only versions with a specified date are applicable to this Standard. In terms of references without a specified date, the latest version (including all the modifications) is applicable to this Standard. GB/T 223 Methods for Chemical Analysis of Iron, Steel and Alloy GB/T 228.1 Metallic Materials - Tensile Testing - Part 1: Method of Test at Room Temperature GB/T 229 Metallic Materials - Charpy Pendulum Impact Test Method GB/T 232 Metallic Materials - Bend Test GB/T 2975-1998 Steel and Steel Products - Location and Preparation of Test Pieces for Mechanical Testing GB/T 4336 Carbon and Low-alloy Steel - Determination of Multi-element Contents - Spark Discharge Atomic Emission Spectrometric Method (routine method) GB/T 20066 Steel and Iron - Sampling and Preparation of Samples for the Determination of Chemical Composition GB/T 20123 Steel and Iron - Determination of Total Carbon and Sulfur Content Infrared Absorption Method after Combustion in an Induction Furnace (routine method) GB/T 20124 Steel and Iron - Determination of Nitrogen Content - Thermal Conductimetric Method after Fusion in a Current of Inert Gas (routine method) GB/T 20125 Low-alloy Steel - Determination of Multi-element Contents - Inductively Coupled Plasma Atomic Emission Spectrometric Method 5.2.1 Steel plates’ mechanical and process performance shall comply with the stipulations in Table 6 and Table 7. 5.2.2 After bending test, the external surface of the sample shall not manifest visible cracks. If the supply-side can guarantee that products are qualified in the test, the bending test may be unnecessary. 5.2.3 Impact absorption energy is the average value of the test results of a group of three samples. One of the test results is allowed to be smaller than the stipulated value, but it shall be not less than 70% of the stipulated value. 5.2.4 Impact test is merely applicable to steel plates, whose thickness is more than, or equals to 6 mm. When impact test is conducted on steel plates, whose thickness is more than, or equals to 12 mm, standard samples shall be adopted; the test result shall satisfy the stipulated value listed in the table. During the impact test on steel plates, whose thickness is more than, or equals to 6 mm, and less than 12.0 mm, or auxiliary samples shall be adopted; the test result shall be respectively not less than 75% or 50% of the stipulated value listed in the table. 5.2.5 If the result of impact test does not comply with the stipulated requirements, another 3 samples may be taken from the same product for testing. Under this circumstance, the average value of the 6 samples in total shall be not less than the stipulated value. In addition, there can be 2 samples at the most that are lower than the stipulated value; only 1 value is allowed to be less than 70% of the stipulated value. Table 8 6.3 Sampling Frequency 6.3.1 Sampling frequency of chemical composition analysis In accordance with furnace, conduct smelting analysis of chemical composition. 6.3.2 Sampling frequency of tensile performance and bending performance Each batch shall be constituted of steel plates of the same furnace number, the same nameplate, and the same delivery state, and whose weight is not more than 50 tons, and whose maximum thickness is not more than 2 times of the minimum thickness. When the weight of a batch is more than 50 tons, take 2 samples. When a batch is constituted of a single-piece steel plate, take 1 sample. 6.3.3 Sampling frequency of impact performance Each batch shall be constituted of steel plates of the same furnace number, the same nameplate and the same delivery state. Take the thickest steel plate from the batch as the sample. 6.3.4 Through the negotiation between the supply-side and the demand-side, the rules of group batch may be otherwise determined. 6.4 Re-test of Impact Test When the result of impact test does not comply with the stipulated requirements, single-piece steel plates which already receive the test and are disqualified in the result cannot be accepted. In terms of steel plates that are at the same thickness of the sampling steel plate, submit them piece by piece for impact test and acceptance check. In terms of steel plates of other thicknesses, constitute a new batch, then, submit for impact test and acceptance check. Inspection Items No. Sampling Size, PCS Sampling Method Test Method Chemical Analysis a 1 (per furnace) Tensile Test Bending Test Impact Test a During arbitration, test method shall adopt GB/T 223. 1 group (3 PCS) or universal methods Figure A11 a) ......
 
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.