JB/T 7946.1-2017 PDF English
Search result: JB/T 7946.1-2017 English: PDF (JB/T7946.1-2017)
| Standard ID | Contents [version] | USD | STEP2 | [PDF] delivered in | Name of Chinese Standard | Status |
| JB/T 7946.1-2017 | English | 150 |
Add to Cart
|
0-9 seconds. Auto-delivery.
|
Metallograph of cast aluminium alloys - Part 1: Cast aluminium-silicon alloys modification
| Valid |
| JB/T 7946.1-1999 | English | 199 |
Add to Cart
|
2 days
|
Metallograph of cast aluminium alloys. Cast aluminium-silicon alloys. Modification
| Obsolete |
| JB/T 7946.1-1995 | English | RFQ |
ASK
|
3 days
|
(Chinese Industry Standard)
| Obsolete |
BUY with any currencies (Euro, JPY, GBP, KRW etc.): JB/T 7946.1-2017 Related standards: JB/T 7946.1-2017
PDF Preview: JB/T 7946.1-2017
JB/T 7946.1-2017: PDF in English (JBT 7946.1-2017) JB/T 7946.1-2017
JB
MECHANICAL INDUSTRY STANDARD
OF THE PEOPLE’S REPUBLIC OF CHINA
ICS 77.120.10
J 31
Registration number: 57827-2017
Replacing JB/T 7946.1-1999
Metallograph of cast aluminum alloys -
Part 1: Cast aluminum-silicon alloys modification
ISSUED ON: JANUARY 09, 2017
IMPLEMENTED ON: JULY 01, 2017
Issued by: Ministry of Industry and Information Technology of PRC
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Normative references ... 4
3 Cutting and preparation of specimen ... 4
4 Metallographic observation of specimen ... 5
5 Grading of cast aluminum-silicon alloy modification ... 5
Foreword
JB/T 7946 "Molded Aluminum Alloy Metallurgy" is divided into four parts:
- Part 1: Cast aluminum-silicon alloys modification;
- Part 2: Cast aluminum-silicon alloys burning;
- Part 3: Cast aluminum alloys pinhole;
- Part 4: Cast aluminum-copper alloys grain size.
This part is the part 1 JB/T 7946.
This part replaces JB/T 7946.1-1999 "Metallograph of cast aluminum alloys -
Cast aluminum-silicon alloys - Modification". As compared with JB/T 7946.1-
1999, the main technical changes are as follows:
- MODIFY part of technical content on cutting and preparation of specimen;
- MODIFY the grading instructions for phosphorus modification; REPLACE
the corresponding microscopic reference picture;
- ADD the grading instructions for strontium and antimony modification; ADD
corresponding microscopic reference pictures.
This part was drafted in accordance with the rules given in GB/T 1.1-2009.
This part was proposed by the China Machinery Industry Federation.
This part shall be under the jurisdiction of the National Foundry Standardization
Technical Committee (SAC/TC 54).
The responsible drafting organization of this part: Tianjin Lizhong Alloy Group
Co., Ltd.
Participated drafting organization of this part: Shenyang Foundry Research
Institute, Anhui Hualing West Kitchen Equipment Co., Ltd., Anhui Hengtai
Power Technology Co., Ltd., CITIC Daika Co., Ltd., Zhangzhou Jinnuo
Industrial Co., Ltd.
The main drafters of this part: Ge Sujing, Zong Fuchun, Liu Chuang, Xu
Zhenghua, Zhang Gaowei, Huo Huijuan, Bai Bangwei, Ma Zhengsong, Guo
Dong.
This standard replaces the standard previously issued as follows:
- JB/T 7946.1-1995, JB/T 7946.1-1999.
Metallograph of cast aluminum alloys -
Part 1: Cast aluminum-silicon alloys modification
1 Scope
This part of JB/T 7946 specifies the cutting and preparation of metallographic
specimens of cast aluminum-silicon alloys, the observation of metallographic
structure, the grading of cast aluminum-silicon alloys.
This part applies to the evaluation of the grade of modification of cast aluminum-
silicon alloys.
2 Normative references
The following documents are essential to the application of this document. For
the dated documents, only the versions with the dates indicated are applicable
to this document; for the undated documents, only the latest version (including
all the amendments) are applicable to this standard.
GB/T 3246.1 Inspection method for structure of wrought aluminum and
aluminum alloy products - Part 1: Inspection method for microstructure
3 Cutting and preparation of specimen
3.1 Cutting of specimen
The metallographic specimens are usually cut from a single-cast tensile test bar
of the same furnace. The metallographic specimens of the important castings
shall be cut from the additional cast test bars of the castings or from the
representative parts of the castings according to the technical agreement.
3.2 Preparation of specimens
3.2.1 The metallographic specimen is coarsely ground, finely ground by
sandpaper, then coarsely polished and finely polished to obtain a flat, scratch-
free, distortion-free mirror surface, until a clear microstructure is observed.
Metallographic specimens can be finely polished or electrolytically polished if
required.
3.2.2 Polished metallographic specimens are directly observed by an optical
microscope. If there is a special need, use the 0.5% (mass fraction) of
hydrofluoric acid aqueous solution to etch it according to the provisions of GB/T
3246.1.
3.2.3 During the process of cutting and preparing metallographic specimens, it
shall be ensured that the metallographic structure does not change.
4 Metallographic observation of specimen
4.1 Use an optical microscopy to observe the microstructure of the cast
aluminum-silicon alloy. The magnification of metallographic structure after
sodium modification, strontium modification, antimony modification is 200 times;
the magnification of metallographic structure after phosphorus modification is
100 times.
4.2 First, observe the metallographic structure of the entire metallographic
specimen; then evaluate it according to the level figure corresponding to the
field of view of most metallographic structures.
5 Grading of cast aluminum-silicon alloy modification
5.1 The cast aluminum-silicon alloy modification is divided into no modification,
insufficient modification, normal modification, deterioration of modification, mild
over-modification, severe over-modification. The grading description is as
shown in Table 1. The reference metallographic structure is as shown in Figure
1.
Table 1 -- Description of grading of cast aluminum-silicon alloy after
sodium modification
Grade Features of metallographic texture Figure number
No modification Eutectic silicon is long needle-like, irregularly distributed, may have α dendritic or a small amount of bulk crystalline silicon Figure 1a)
Insufficient
modification
α dendrite and eutectic are uniformly distributed, some eutectic
silicon is short rod-shaped, some is needle-like Figure 1b)
Normal
modification
α dendrite and eutectic are uniformly distributed, eutectic silicon is
punctate or wormlike Figure 1c)
Deterioration of
modification
α dendrite and eutectic are not uniformly distributed, eutectic
silicon is thickened, some is short-rod shaped, some needle-like Figure 1d)
Mild over-
modification
α dendrite and eutectic are basically uniformly distributed, but
linear α-belt appears in some eutectics Figure 1e)
Severe over-
modification
α dendrite and eutectic are irregularly distributed, a coarse
modification zone appears (a wavy α-belt appears in the fine
eutectic with many eutectic silicon in it)
Figure 1f)
......
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.
|