GB/T 3880.2-2012 GB/T 3880.2-2012: PDF in English (GBT 3880.2-2012)
GB/T 3880.2-2012
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.150.10
H 61
Replacing GB/T 3880.2-2006
Wrought Aluminium and Aluminium Alloy Plates,
Sheets and Strips for General Engineering –
Part 2. Mechanical Properties
ISSUED ON. DECEMBER 31, 2012
IMPLEMENTED ON. OCTOBER 1, 2013
Issued by. General Administration of Quality Supervision, Inspection
and Quarantine;
Standardization Administration of the People's Republic of
China.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Mechanical Properties ... 5
Foreword
GB/T 3880 is divided into three parts under the general title of "Wrought Aluminium
and Aluminium Alloy Plates, Sheets and Strips For General Engineering".
— Part 1. Technical Conditions of Delivery;
— Part 2. Mechanical Properties;
— Part 3. Tolerances on Forms and Dimensions.
This Part is part 2 of GB/T 3880.
This Part was drafted according to the rules specified in GB/T 1.1-2009.
This Part replaces GB/T 3880.2-2006 "Wrought Aluminium and Aluminium Alloy Plates
Sheets and Strips for General Engineering - Part 2. Mechanical Properties".
Compared with GB/T 3880.2-2006, the main technical changes in this Part are as
follows.
— Alloys 1070A, 1080A, 2017A, 2A12, 2A14, 2014A, 2E12, 2219, 3103, 3A21,
4006, 4007, 4015, 5A02, 5005A, 5040, 5049, 5449, 5050, 5251, 5154A, 5754,
5454, 5383, 6016, 7020, 7021, 7022, 7A04, 7A09, 7475, 8011 and 8079 were
added;
— Partial properties of original alloys 1050A, 1100, 1200, 3003 (except tempers
H14 and H24), 3004, 5005, 5052, 5083, 5086, 6061, 6082, 8011A and 7075 were
modified.
This Part uses redrafting method and references to EN 485-2.2008 "Aluminium and
Aluminium Alloys - Sheet, Strip and Plate - Part 2. Mechanical Properties", ASTM
B209M-07 "Aluminum and Aluminum Alloy Sheet and Plate" and JIS H4000.2006
"Aluminium and Aluminium Alloys - Sheets, Strips and Plates". This Part is not
equivalent to EN 485-2.2008, ASTM B209M-07 and JIS H4000.2006.
This Part shall be under the jurisdiction of National Technical Committee 243 on
Nonferrous Metals of Standardization Administration of China (SAC/TC 243).
Chief drafting organizations of this Part. Southwest Aluminum (Group) Co., Ltd., China
Institute of Weights and Measures Quality of Nonferrous Metal Industry, Northeast
Light Alloy Co., Ltd., Chinalco Ruimin Co., Ltd., Xiashun Aluminium Foil Co., Ltd.,
Northwest Branch of Aluminum Corporation of China, Aleris Dingsheng Aluminum
(Zhenjiang) Co., Ltd. AND Fujian Nanping Aluminium Sheet & Strip Co., Ltd.
Chief drafting staffs of this Part. Lin Lin, Zhang Yu, Ge Lixin, Li Ruishan, Zhang Siping,
Tang Dengyi, Wang Guojun, Qiu Longtao, Wang Xiguang, Huang Rong, Xie Tingcui,
Dong Zefang, Peng Wenwei, Zhao Yongjun and Huang Ruiyin.
Wrought Aluminium and Aluminium Alloy Plates,
Sheets and Strips for General Engineering –
Part 2. Mechanical Properties
1 Scope
This Part of GB/T 3880 specifies mechanical properties of wrought aluminium and
aluminium alloy plates, sheets and strips for general engineering applications.
This Part is applicable to wrought aluminium and aluminium alloy plates, sheets and
strips (hereafter referred to as “plates, sheets and strips”) for general engineering
applications.
2 Mechanical Properties
Tensile testing of plates, sheets and strips under room temperature shall be in
accordance with those specified in Table 1. During bending properties testing, the bend
radius shall be in accordance with those specified in Table 1. Plates, sheets and strips
after bending test shall be free from crack on the surface. For the mechanical
properties of plates, sheets and strips with a thickness exceeding those specified in
Table 1, the actual measured results shall be accompanied.
Table 1 (continued)
Designation Al-clad type Supply temper
Sample
temper
Thickness
mm
Test results of tensile testing under room
temperature Bend
radius b
Tensile
strength
Rm/MPa
Specified non-
proportional
elongation
strength
Rp0.2/MPa
Elongation
a/%
A50 mm A 90° 180°
Not less than
1080A —
H22 H22 >1.50 ~ 3.00 80 ~ 120 50 11 — 0.5t 0.5t>3.00 ~ 6.00 13 — 1.0t —
H14 H14
>0.20 ~ 0.50
100 ~ 140 70
4 — 0t 0.5t
>0.50 ~ 1.50 4 — 0.5t 0.5t
>1.50 ~ 3.00 5 — 1.0t 1.0t
>3.00 ~ 6.00 6 — 1.5t —
H24 H24
>0.20 ~ 0.50
100 ~ 140 60
5 — 0t 0.5t
>0.50 ~ 1.50 6 — 0.5t 0.5t
>1.50 ~ 3.00 7 — 1.0t 1.0t
>3.00 ~ 6.00 9 — 1.5t —
H16 H16
>0.20 ~ 0.50
110 ~ 150 90
2 — 0.5t 1.0t
>0.50 ~ 1.50 2 — 1.0t 1.0t
>1.50 ~ 4.00 3 — 1.0t 1.0t
H26 H26
>0.20 ~ 0.50
110 ~ 150 80
3 — 0.5t —
>0.50 ~ 1.50 3 — 1.0t —
>1.50 ~ 4.00 4 — 1.0t —
H18 H18
>0.20 ~ 0.50
2 — 1.0t —
>0.50 ~ 1.50 2 — 2.0t —
>1.50 ~ 3.00 2 — 2.5t —
H112 H112 >6.00 ~ 12.50 70 — 20 — — — >12.50 ~ 25.00 70 — — 20 — —
F — 2.50 ~ 25.00 — — — — — —
1070 — O O
>0.20 ~ 0.30
55 ~ 95
15 — 0t —
>0.30 ~ 0.50 20 — 0t —
>0.50 ~ 0.80 25 — 0t —
>0.80 ~ 1.50
30 — 0t —
>1.50 ~ 6.00 35 — 0t —
>6.00 ~ 12.50 35 — — —
>12.50 ~ 50.00 — 30 — —
Table 1 (continued)
Designation Al-clad type Supply temper
Sample
temper
Thickness
mm
Test results of tensile testing under room
temperature Bend
radius b
Tensile
strength
Rm/MPa
Specified non-
proportional
elongation
strength
Rp0.2/MPa
Elongation
a/%
A50 mm A 90° 180°
Not less than
1050 —
H26 H26 >0.80 ~ 1.50 120 85 3 — 2.0t — >1.50 ~ 4.00 4 — 2.0t —
>0.20 ~ 0.50
130 —
1 — — —
H18 H18 >0.50 ~ 0.80 2 — — —
>0.80 ~ 1.50 3 — — — >1.50 ~ 3.00 4 — — —
>4.50 ~ 6.00 85 45 10 — — —
>6.00 ~ 12.50 80 45 10 — — —
H112 H112 >12.50 ~ 25.00 70 35 — 16 — —
>25.00 ~ 50.00 65 30 — 22 — — >50.00 ~ 75.00 65 30 — 22 — —
F — >2.50 ~ 150.00 — — —
1050A —
H111
H111
>0.20 ~ 0.50 20 — 0t 0t
>0.50 ~ 1.50 22 — 0t 0t
>1.50 ~ 3.00 >65 ~ 95 20 26 — 0t 0t
>3.00 ~ 6.00
29 — 0.5t 0.5t
>6.00 ~ 12.50 35 — 1.0t 1.0t
>12.50 ~
180.00 — 32 — —
>0.20 ~ 0.50 2 — 0t 0.5t
H12 H12 >0.50 ~ 1.50 >85 ~ 125 65 4 — 0t 0.5t
>1.50 ~ 3.00 5 — 0.5t 0.5t>3.00 ~ 6.00 7 — 1.0t 1.0t
>0.20 ~ 0.50 4 — 0t 0.5t
H22 H22 >0.50 ~ 1.50 >85 ~ 125 55 5 — 0t 0.5t
>1.50 ~ 3.00 6 — 0.5t 0.5t>3.00 ~ 6.00 11 — 1.0t 1.0t
>0.20 ~ 0.50 2 — 0t 1.0t
H14 H14 >0.50 ~ 1.50 >105 ~ 145 85 2 — 0.5t 1.0t
>1.50 ~ 3.00 4 — 1.0t 1.0t>3.00 ~ 6.00 5 — 1.5t —
Table 1 (continued)
Designation Al-clad type
Supply
temper
Sample
temper
Thickness
mm
Test results of tensile testing under room
temperature Bend
radius b
Tensile
strength
Rm/MPa
Specified non-
proportional
elongation
strength
Rp0.2/MPa
Elongation
a/%
A50 mm A 90° 180°
Not less than
>0.50 ~ 0.80
2 — — —
H18 H18 >0.80 ~ 1.50 125 3 — — — >1.50 ~ 4.50 4 — — —
1145 >4.50 ~ 6.50 85 45 10 — — —
H112 H112 >6.50 ~ 12.50 80 45 10 — — —
>12.50 ~ 25.00 70 35 — 16 — — F — >2.50 ~ 150.00 — — —
1235 —
O O >0.20 ~ 1.00 65 ~ 105 — 15 — — —
>0.20 ~ 0.30
95 ~ 130 —
2 — — —
>0.30 ~ 0.50 3 — — —
H12 H12 >0.50 ~ 1.50 6 — — —
>1.50 ~ 3.00 8 — — — >3.00 ~ 4.50 9 — — —
>0.20 ~ 0.30
2 — — —
>0.30 ~ 0.50 3 — — —
H22 H22 >0.50 ~ 1.50 95 6 — — —
>1.50 ~ 3.00 8 — — — >3.00 ~ 4.50 9 — — —
>0.20 ~ 0.30
1 — — —
H14 H14 >0.30 ~ 0.50 115 ~ 150 2 — — —
>0.50 ~ 1.50 3 — — — >1.50 ~ 3.00 4 — — —
>0.20 ~ 0.30
1 — — —
H24 H24 >0.30 ~ 0.50 115 2 — — —
>0.50 ~ 1.50 3 — — — >1.50 ~ 3.00 4 — — —
>0.20 ~ 0.50
1 — — —
H16 H16 >0.50 ~ 1.50 130 ~ 165 2 — — —
>1.50 ~ 4.00 3 — — —
H26 H26 >0.20 ~ 0.50 130 — 1 — — —
Table 1 (continued)
Designation Al-clad type
Supply
temper
Sample
temper
Thickness
mm
Test results of tensile testing under room
temperature Bend
radius b
Tensile
strength
Rm/MPa
Specified non-
proportional
elongation
strength
Rp0.2/MPa
Elongation
a/%
A50 mm A 90° 180°
Not less than
1200 —
>0.20 ~ 0.50 2 — 0.5t —
H26 H26 >0.50 ~ 1.50 130 ~ 170 105 3 — 1.0t —
>1.50 ~ 4.00 4 — 1.5t —
>0.20 ~ 0.50 1 — 1.0t —
H18 H18 >0.50 ~ 1.50 150 130 2 — 2.0t —
>1.50 ~ 3.00 2 — 3.0t —
>0.20 ~ 0.50 1 — — —
H19 H19 >0.50 ~ 1.50 160 140 1 — — —
>1.50 ~ 3.00 1 — — —
H112 H112 >6.00 ~ 12.50 85 35 16 — — — >12.50 ~ 80.00 80 30 — 16 — —
F — >2.50 ~ 150.00 — — —
O >0.50 ~ 3.00 ≤225 — 12 — — —
>3.00 ~ 10.00 ≤235 — 12 — — —
T42C >0.50 ~ 3.00 350 185 15 — — — >3.00 ~ 10.00 355 195 15 — — —
T1 T42
>4.50 ~ 10.00 355 195 15 — — —
>10.00 ~ 12.50 370 215 11 — — — >12.50 ~ 25.00 370 215 — 11 — —
Al-clad
2A11
2A11
Normal al-
clad or
processed
al-clad
>25.00 ~ 40.00 330 195 — 8 — —
>40.00 ~ 70.00 310 195 — 6 — —
>70.00 ~ 80.00 285 195 — 4 — —
>0.50 ~ 1.50 15 — — —
T3 T3 >1.50 ~ 3.00 375 215 17 — — —
>3.00 ~ 10.00 15 — — —
T4 T4 >0.50 ~ 3.00 360 185 15 — — —
>3.00 ~ 10.00 370 195 15 — — — F — >4.50 ~ 150.00 — — —
Table 1 (continued)
Designation Al-clad type
Supply
temper
Sample
temper
Thickness
mm
Test results of tensile testing under room
temperature Bend
radius b
Tensile
strength
Rm/MPa
Specified non-
proportional
elongation
strength
Rp0.2/MPa
Elongation
a/%
A50 mm A 90° 180°
Not less than
Al-clad
2A12
2A12
Normal al-
clad or
processed
al-clad
O >0.50 ~ 4.50 ≤215 — 14 — — — >4.50 ~ 10.00 ≤235 — 12 — — —
T42c >0.50 ~ 3.00 390 245 15 — — — >3.00 ~ 10.00 410 265 12 — — —
>4.50 ~ 10.00 410 265 12 — — —
>10.90 ~ 12.50 420 275 7 — — —
T1 T42 >12.50 ~ 25.00 420 275 — 7 — —
>25.00 ~ 40.00 390 255 — 5 — —
>40.00 ~ 70.00 370 245 — 4 — — ...
......
(Above excerpt was released on 2015-12-13, modified on 2021-06-07, translated/reviewed by: Wayne Zheng et al.)
Source: https://www.chinesestandard.net/PDF.aspx/GBT3880.2-2012