GB/T 3190-2008 (GB/T 3190-2020 Newer Version) PDF English


GB/T 3190-2008 (GB/T3190-2008, GBT 3190-2008, GBT3190-2008)
Standard IDContents [version]USDSTEP2[PDF] delivered inName of Chinese StandardStatus
GB/T 3190-2020English205 Add to Cart 0-9 seconds. Auto-delivery. Chemical composition of wrought aluminium and aluminium alloys Valid
GB/T 3190-2008English85 Add to Cart 0-9 seconds. Auto-delivery. Wrought aluminium and aluminium alloy -- Chemical composition Obsolete
GB/T 3190-1996English679 Add to Cart 5 days Wrought aluminium and aluminium alloys--Chemical composition limits Obsolete
GB 3190-1982English85 Add to Cart 0-9 seconds. Auto-delivery. Chemical composition of wrought aluminum and aluminum alloys designation Obsolete
Newer version: GB/T 3190-2020     Standards related to (historical): GB/T 3190-2020
PDF Preview

GB/T 3190-2008: PDF in English (GBT 3190-2008)

GB/T 3190-2008 GB NATIONAL STANDARD OF THE PEOPLE’S REPUBLIC OF CHINA ICS 77.150.10 H 60 Replacing GB/T 3190-1996 Wrought Aluminium and Aluminium Alloy – Chemical Composition (ISO 209.2007 Aluminium and Aluminium Alloy - Chemical Composition, MOD) ISSUED ON JUNE. 17, 2008 IMPLEMENTED ON. DECEMBER 1, 2008 Issued by. General Administration for Quality Supervision and Inspection and Quarantine (GAQSIQ); Standardization Administration of China (SAC). Table of Contents Foreword ... 3  1 Scope ... 5  2 Normative References ... 5  3 Requirements ... 5  4 Others ... 7  Annex A ... 32  Annex B ... 34  Foreword This Standard modifies and adopts ISO209.2007 "Wrought Aluminium and Aluminium Alloy - Chemical Composition" (English edition), and it is redrafted in accordance with ISO209.2007. For ease of comparison, the list of corresponding chapters and sections between the International Standard and this Standard is detailed in Annex B (Informative). Modifications are done while adopting the International Standard. the technical differences are marked with vertical single-line on the page margin of the involved articles; they are as follows. — Delete the designation and composition of aluminium and aluminium alloy that have not been produced in China ever; — Delete the table of comparison between new and old designations in the ISO standard; — Add four-letter designation and composition that are special in China; — Add the requirements for special control of toxic and harmful elements; — Add the requirements on composition analysis and sampling. This Standard replaces GB/T3190-1996 "Wrought Aluminium and Aluminium Alloy-Chemical Composition". Compared with GB/T3190-1996, the main revisions in this Standard are as follows. — Add designations and compositions of 130 aluminiums and aluminium alloys; divide the Table of chemical composition into two parts (two tables). Table 1 is applicable to international designations, covering 159 designations; Table 2 is applicable to four-letter designations, covering 114 designations; — Add the requirements for special control of toxic and harmful elements; — Add the denotation (method) of limit value; — Revise "Table of Comparison between New and Old Designations". Annex A and Annex B of this Standard are informative. This Standard was proposed by China Non-ferrous Metals Industry Federation. This Standard shall be under the jurisdiction of the National Standardization Technical Committee of Non-ferrous Metal. Main drafting organizations of this Standard. Northeast Light Alloy Co., Ltd., China Non-ferrous Metals Industry Standard Measurement Quality Institute Wrought Aluminium and Aluminium Alloy – Chemical Composition 1 Scope This Standard specifies the chemical composition of wrought aluminium and aluminium alloy. This Standard is applicable to aluminium and aluminium alloy products (plate, strip, foil, pipe, stick, section, line and forging) produced with press working, and cast ingot and blanks used for them. 2 Normative References The following standards contain the provisions which, through reference in this text, constitute the provisions of this Standard. For the dated reference, the subsequent amendments (excluding correction) or revisions of these publications do not apply. However, the parties who enter into agreement according to these specifications are encouraged to study whether the latest editions of these labels are applicable. For undated references, the latest edition of the normative document is applicable to this Standard. GB/T 7999 Optical emission spectrometric analysis method of aluminum and aluminum alloys GB/T 8170 Rules for rounding off of numerical values GB/T 16474 Wrought aluminium and aluminium alloy - Designation system GB/T 20975 Chemical analysis methods of aluminium and aluminium alloys (all parts) 3 Requirements 3.1 Chemical composition 3.1.1 The chemical compositions of wrought aluminiums and aluminium alloys shall meet the requirements of Table 1 and Table 2. The column "others" indicates the metallic element not listed in the table. For the contents in the table that are in single-numerical-value, it is the minimal limit for aluminium; and it is the maximal limit for other elements. The denotation of limit value is as. Table 2 are suspected exceeding the limits of "single" or "total" values specified in this Standard, then the manufacturer may do analysis for these elements. 3.3.4 When the content (mass fraction) of aluminium is larger than or equal to 99.00% and less than 99.90%, it shall be determined by the calculation (method) that 100.00% is deducted by the sum of the contents of all the elements of which the content is less than 0.010%. The content value of the elements shall be rounded to 0.0x% before summing. 3.3.5 When the content (mass fraction) of aluminium is larger than or equal to 99.00% and less than or equal to 99.99%, it shall be determined by the calculation (method) that 100.00% is deducted by the sum of the contents of all the elements of which the content is less than 0.0010%. The content value of the elements shall be rounded to 0.0XX% before summing. The sum shall be rounded to 0.0X%. 3.3.6 The chemical components shall be analyzed by the method specified in GB/T 7999 or GB/T 20975, or other reliable and accurate method. in the case of dispute, the method specified in GB/T 20975 or other method agreed by both parties must be adopted for arbitration analysis. 3.3.7 If the first analytical results does not meet the requirements, second analysis may be allowed; the second analytical result is deemed as the judgment basis for exit-factory of the manufacturer and acceptance. 4 Others 4.1 The digit-number of element contents in chemical composition analytical report shall be of correspondence to the one of the corresponding designation specified in Table 1 or Table 2. 4.2 The rounding of numerical values shall meet the requirements of GB/T 8170. 4.3 The relation table of comparison for new and old designations is detailed in Annex A. Table 1 No. Designation Chemical composition (mass fraction) /% Si Fe Cu Mn Mg Cr Ni Zn Ti Zr Others Al Single Total 1 1035 0.35 0.6 0.10 0.05 0.05 ― ― 0.10 0.05V 0.03 ― 0.03 ― 99.35 2 1040 0.30 0.50 0.10 0.05 0.05 ― ― 0.10 0.05V 0.03 ― 0.03 ― 99.40 3 1045 0.30 0.45 0.10 0.05 0.05 ― ― 0.05 0.05V 0.03 ― 0.03 ― 99.45 4 1050 0.25 0.40 0.05 0.05 0.05 ― 0.05 0.05V 0.03 ― 0.03 ― 99.50 5 1050A 0.25 0.40 0.05 0.05 0.05 ― ― 0.07 ― 0.05 ― 0.03 ― 99.50 6 1060 0.25 0.35 0.05 0.03 0.03 ― ― 0.05 0.05V 0.03 ― 0.03 ― 99.60 7 1065 0.25 0.30 0.05 0.03 0.03 ― ― 0.05 0.05V 0.03 ― 0.03 ― 99.65 8 1070 0.20 0.25 0.04 0.03 0.03 ― ― 0.04 0.05V 0.03 ― 0.03 ― 99.70 9 1070A 0.20 0.25 0.03 0.03 0.03 ― ― 0.07 ― 0.03 ― 0.03 ― 99.70 10 1080 0.15 0.15 0.03 0.02 0.02 ― ― 0.03 0.03Ga, 0.05V 0.03 ― 0.02 ― 99.80 11 1080A 0.15 0.15 0.03 0.02 0.02 ― ― 0.06 0.03Ga1 0.02 ― 0.02 ― 99.80 12 1085 0.10 0.12 0.03 0.02 0.02 ― 0.03 0.03Ga, 0.05V 0.02 ― 0.01 ― 99.85 13 1100 0.95Si+Fe 0·05~0·20 0, 05 ― ― ― 0.10 1 ― 0.05 0.15 99.00 H 1200 1.00Si+Fe 0.05 0.05 ― ― ― 0.10 ― 0.05 ― 0.05 0.15 99.00 15 1200A 1.00Si+Fe 0.10 0.30 0.30 0.10 ― 0.10 ― ― ― 0.05 0.15 99.00 16 1120 0.10 0.40 0.05~0.35 0.01 0.20 0.01 ― 0.05 0.03Ga, 0.05B, 0.02V+Ti ― 0.03 0.10 99.20 17 12302 0.70Si+Fe 0.10 0.05 0.05 ― 0.10 0.05V 0.03 ― 0.03 ― 99.30 18 1235 0.65Si+Fe 0.05 0.05 0.05 ― 0.10 0.05V 0.06 ― 0.03 ― 99.35 19 1435 0.15 0.30~0.50 0.02 0.05 0.05 ― ― 0.10 0.05V 0.03 0.03 ― 99.35 20 1145 0.55Si+Fe 0.05 0.05 0.05 ― ― 0.05 0.05V 0.03 ― 0.03 ― 99.45 21 1345 0.30 0.40 0.10 0.05 0.05 ― ― 0.05 0.05V 0.03 ― 0.03 ― 99.45 Table 1 (continued) No. Designation Chemical composition (mass fraction) /% Si Fe Cu Mn Mg Cr Ni Zn Ti Zr Others Al Single Total 58 3005 0.6 0.7 0.30 1.0~1.5 0.20~0.6 0.10 ― 0.25 ― 0.10 ― 0.05 0.15 Margin 59 3105 0.6 0.7 0.30 0.30~0.8 0.20~0.8 0.20 ― 0.40 ― 0.10 ― 0.05 0.15 Margin 60 3105A 0.6 0.7 0.30 0.30~0.8 0.20~0.8 0.20 ― 0.25 ― 0.10 ― 0.05 0.15 Margin 61 3006 0.50 0.7 0.10~0.30 0.50~0.8 0.30~0.6 0.20 ― 0.15~0.40 ― 0.10 ― 0.05 0.15 Margin 62 3007 0.50 0.7 0.05~0.30 0.30~0.8 0.6 0.20 ― 0.40 ― 0.10 ― 0.05 0.15 Margin 63 3107 0.6 0.7 0.05~0.15 0.40~0.9 ― ― ― 0.20 ― 0.10 ― 0.05 0.15 Margin 64 3207 0.30 0.45 0.10 0.40~0.8 0.10 ― ― 0.10 ― ― ― 0.05 0.10 Margin 65 3207A 0.35 0.6 0.25 0.30~0.8 0.40 0.20 ― 0.25 ― ― ― 0.05 0.15 Margin 66 3307 0.6 0.8 0.30 0.50~0.9 0.30 0.20 ― 0.Ί0 ― 0.10 ― 0.05 0.15 Margin 67 40042 9·0~10.5 0.8 0.25 0.10 1.0~2.0 ― ― 0.20 ― ― ― 0.05 0.15 Margin 68 4032 11.0~13.5 1.0 0.50~1.3 ― 0.8~1.3 0.10 0.50~1.3 0.25 ― ― ― 0.05 0.15 Margin Table 1 (continued) No. Designation Chemical composition (mass fraction) /% Si Fe Cu Mn Mg Cr Ni Zn Ti Zr Others Al Single Total 94 5056 0.30 0.40 0.10 0.05~0.20 4.5~5.6 0.05~0.20 ― 0..10 ― ― ― 0.05 0.15 Margin 95 5356 0.25 0.40 0.10 0.05~0.20 4.5~5.5 0.05~0.20 ― 0.10 1 0.06~0.20 ― 0.05 0.15 Margin 96 5456 0.25 0.40 0.10 0.50~1.0 4.7~5.5 0.05~0.20 ― 0.25 ― 0.20 ― 0.05 0.15 Margin 97 5059 0.45 0.50 0.25 0.6~1.2 5.0~6.0 0... ......
 