HOME   Cart(0)   Quotation   About-Us Tax PDFs Standard-List Powered by Google www.ChineseStandard.net Database: 189759 (1 Dec 2024)

GB/T 15970.6-2007 PDF in English


GB/T 15970.6-2007 (GB/T15970.6-2007, GBT 15970.6-2007, GBT15970.6-2007)
Standard IDContents [version]USDSTEP2[PDF] delivered inName of Chinese StandardStatus
GB/T 15970.6-2007English180 Add to Cart 0-9 seconds. Auto-delivery. Corrosion of metals and alloys -- Stress corrosion testing -- Part 6: Preparation and use of pre-cracked specimens for tests under constant load or constant displacement Valid
GB/T 15970.6-1998EnglishRFQ ASK 4 days Corrosion of metals and alloys--Stress corrosion testing--Part 6: Preparation and use of pre-cracked specimens Obsolete
Standards related to (historical): GB/T 15970.6-2007

Preview PDF (Powered by Google. Reload if blank, scroll for next page)

GB/T 15970.6-2007: PDF in English (GBT 15970.6-2007)

GB/T 15970.6-2007 GB NATIONAL STANDARD OF THE PEOPLE’S REPUBLIC OF CHINA ICS 77.060 H 25 GB/T 15970.6-2007 / ISO 7539-6.2003 Replacing GB/T 15970.6-1998 Corrosion of metals and alloys - Stress corrosion testing - Part 6. Preparation and use of pre-cracked specimens for tests under constant load or constant displacement (ISO 7539-6.2003, IDT) ISSUED ON. MAY 14, 2007 IMPLEMENTED ON. DECEMBER 01, 2007 Issued by. General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China; Standardization Administration of the People's Republic of China. Table of Contents Foreword ... 3 1 Scope ... 5 2 Normative reference ... 5 3 Terms and definitions ... 6 4 Principle ... 10 5 Specimens ... 11 6 Initiation and propagation of fatigue cracks ... 31 7 Procedure ... 34 8 Test report ... 44 Annex A (normative) Use of notched specimens for stress corrosion tests ... 46 Annex B (normative) Determination of crack growth velocity ... 50 Foreword GB/T 15970 consists of the following parts under the general title of “Corrosion of metals and alloys - Stress corrosion testing”. Part 1. General guidance on testing procedures (GB/T 15970.1-1995); Part 2. Preparation and use of bent-beam specimens (GB/T 15970.2-2000); Part 3. Preparation and use of U-bend specimens (GB/T 15970.3-1995); Part 4. Preparation and use of uniaxially loaded tension specimens (GB/T 15970.4-2000); Part 5. Preparation and use of C-ring specimens (GB/T 15970.5-1998); Part 6. Preparation and use of pre-cracked specimens for tests under constant load or constant displacement (GB/T 15970.6-2007); Part 7. Slow strain rate testing (GB/T 15970.7-2017); Part 8. Preparation and use of specimens to evaluate weldments (GB/T 15970.8-2005); Part 9. Preparation and use of pre-cracked specimens for tests under rising load or rising displacement (GB/T 15970.9-2007). This Part is identical to the International Standard ISO 7539-6.2003 “Corrosion of metals and alloys - Stress corrosion testing - Part 6. Preparation and use of pre-cracked specimens for tests under constant load or constant displacement”. This Part has made the following editorial modification. - DELETE the foreword of the International Standard; This Part replaces GB/T 15970.6-1998 “Corrosion of metals and alloys - Stress corrosion testing - Part 6. Preparation and use of pre-cracked specimens” Compared with GB/T 15970.6-1998, the main changes are as follows. - DELETE the content related to incremental load or incremental displacement; - ADD the influence of residual stress and electrode potential change on the test results; - ADD a description of the possible influence of residual stress during Corrosion of metals and alloys - Stress corrosion testing - Part 6. Preparation and use of pre-cracked specimens for tests under constant load or constant displacement 1 Scope 1.1 This Part of GB/T 15970 covers procedures for designing, preparing and using pre-cracked specimens for investigating susceptibility to stress corrosion. It gives recommendations for the design, preparation and use of pre-cracked specimens for investigating susceptibility to stress corrosion. Recommendations concerning notched specimens are given in Annex A. The term “metal” as used in this Part includes alloys. 1.2 Because of the need to confine plasticity at the crack tip, pre-cracked specimens are not suitable for the evaluation of thin products such as sheet or wire and are generally used for thicker products including plate bar and forgings. They can also be used for parts joined by welding. 1.3 Pre-cracked specimens may be loaded with equipment for application of a constant load or can incorporate a device to produce a constant displacement at the loading points. Tests conducted under increasing displacement or increasing load are dealt with in GB/T 15970.9. 1.4 A particular advantage of pre-cracked specimens is that they allow data to be acquired from which critical defect sizes, above which stress corrosion cracking may occur, can be estimated for components of known geometry subjected to known stresses. They also enable rates of stress corrosion crack propagation to be determined. The latter data may be taken into account when monitoring parts containing defects during service. 2 Normative reference The following documents contain the provisions which, through reference in this Part of GB/T 15970, become the provisions of this Part. For dated references, their subsequent amendments (excluding corrigendum) or revisions do not apply to this Part. However, the parties who enter into agreement based on this Part are encouraged to investigate whether the latest versions of these documents are applicable. For undated reference documents, the latest versions apply to this Part. ......
 
Source: Above contents are excerpted from the PDF -- translated/reviewed by: www.chinesestandard.net / Wayne Zheng et al.